- Victrex® PEEK -HT™ 22CA30 PolyEtherKetone, 30% Carbon Fibre Reinforced
Victrex® PEEK -HT™ 22CA30 PolyEtherKetone, 30% Carbon Fibre Reinforced
| Category | Polymer , Thermoplastic , Polyketone |
| Manufacturer | Victrex |
| Trade Name | PEEK |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Victrex® PEEK -HT™ 22CA30 PolyEtherKetone, 30% Carbon Fibre Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product Description:High performance thermoplastic material, 30% carbon fibre reinforced PolyEtherKetone (PEK), semi crystalline, granules for injection moulding, standard flow, FDA food contact compliant, colour black.Typical Application Areas:Higher temperature applications for higher strength and stiffness in a static or dynamic system. Excellent wear resistance, low coefficient of friction, low coefficient of thermal expansion. Chemically resistant to aggressive environments.Information Provided by VICTREX®
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in³ | Crystalline; ISO 1183 |
| Water Absorption at Saturation | 0.50 % @Temperature 23.0 °C |
0.50 % @Temperature 73.4 °F |
Equilibrium; by immersion; ISO 62-1 |
| 0.60 % @Temperature 100 °C |
0.60 % @Temperature 212 °F |
immersion; ISO 62-1 | |
| Viscosity | 525000 cP @Temperature 400 °C |
525000 cP @Temperature 752 °F |
melt; ISO 11443 |
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm | 0.0010 in/in | 360°C nozzle, 160°C tool; ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm | 0.0070 in/in | 405°C nozzle, 200°C tool; ISO 294-4 |
| Spiral Flow | 8.00 cm @Thickness 1.00 mm |
3.15 in @Thickness 0.0394 in |
405°C nozzle, 200°C tool |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 88 | 88 | ISO 868 |
| Tensile Strength at Break | 70.0 MPa @Temperature 275 °C |
10200 psi @Temperature 527 °F |
ISO 527 |
| 80.0 MPa @Temperature 225 °C |
11600 psi @Temperature 437 °F |
ISO 527 | |
| 110 MPa @Temperature 175 °C |
16000 psi @Temperature 347 °F |
ISO 527 | |
| 170 MPa @Temperature 125 °C |
24700 psi @Temperature 257 °F |
ISO 527 | |
| 275 MPa @Temperature 23.0 °C |
39900 psi @Temperature 73.4 °F |
ISO 527 | |
| Elongation at Break | 1.7 % @Temperature 23.0 °C |
1.7 % @Temperature 73.4 °F |
ISO 527 |
| Tensile Modulus | 28.0 GPa @Temperature 23.0 °C |
4060 ksi @Temperature 73.4 °F |
ISO 527 |
| Flexural Strength | 100 MPa @Temperature 275 °C |
14500 psi @Temperature 527 °F |
ISO 178 |
| 185 MPa @Temperature 175 °C |
26800 psi @Temperature 347 °F |
ISO 178 | |
| 265 MPa @Temperature 125 °C |
38400 psi @Temperature 257 °F |
ISO 178 | |
| 400 MPa @Temperature 23.0 °C |
58000 psi @Temperature 73.4 °F |
ISO 178 | |
| Flexural Modulus | 23.5 GPa @Temperature 23.0 °C |
3410 ksi @Temperature 73.4 °F |
ISO 178 |
| Compressive Strength | 65.0 MPa @Temperature 250 °C |
9430 psi @Temperature 482 °F |
ISO 604 |
| 95.0 MPa @Temperature 200 °C |
13800 psi @Temperature 392 °F |
ISO 604 | |
| 210 MPa @Temperature 120 °C |
30500 psi @Temperature 248 °F |
ISO 604 | |
| 300 MPa @Temperature 23.0 °C |
43500 psi @Temperature 73.4 °F |
ISO 604 | |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² @Temperature 23.0 °C |
4.28 ft-lb/in² @Temperature 73.4 °F |
ISO 180/A |
| Izod Impact, Unnotched (ISO) | 50.0 kJ/m² @Temperature 23.0 °C |
23.8 ft-lb/in² @Temperature 73.4 °F |
ISO 180/U |
| Charpy Impact Unnotched | 4.50 J/cm² @Temperature 23.0 °C |
21.4 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1U |
| Charpy Impact, Notched | 0.650 J/cm² @Temperature 23.0 °C |
3.09 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 35.0 µm/m-°C @Temperature <=152 °C |
19.4 µin/in-°F @Temperature <=306 °F |
Average below Tg; ISO 11359 |
| 90.0 µm/m-°C @Temperature >=152 °C |
50.0 µin/in-°F @Temperature >=306 °F |
Average above Tg; ISO 11359 | |
| CTE, linear, Parallel to Flow | 5.00 µm/m-°C @Temperature <=152 °C |
2.78 µin/in-°F @Temperature <=306 °F |
Below Tg; ISO 11359 |
| 5.00 µm/m-°C @Temperature >=152 °C |
2.78 µin/in-°F @Temperature >=306 °F |
Above Tg; ISO 11359 | |
| Thermal Conductivity | 2.00 W/m-K | 13.9 BTU-in/hr-ft²-°F | Along flow; ISO 22007-4 |
| 0.950 W/m-K @Temperature 23.0 °C |
6.59 BTU-in/hr-ft²-°F @Temperature 73.4 °F |
Average; ISO/CD 22007-4 | |
| Melting Point | 373 °C | 703 °F | ISO 11357 |
| Deflection Temperature at 1.8 MPa (264 psi) | 368 °C | 694 °F | ISO 75-f |
| Glass Transition Temp, Tg | 152 °C | 306 °F | Onset; ISO 11357 |
| Glow Wire Test | 960 °C @Thickness 2.00 mm |
1760 °F @Thickness 0.0787 in |
IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1e+05 | 1e+05 | 1V; ASTM D4496 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | <= 100 °C | <= 212 °F | Hopper Temperature |
| Nozzle Temperature | 405 °C | 761 °F | |
| Mold Temperature | 190 - 215 °C | 374 - 419 °F | |
| Drying Temperature | 120 °C @Time 18000 sec |
248 °F @Time 5.00 hour |
|
| 150 °C @Time 10800 sec |
302 °F @Time 3.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Toxicity Index | 0.05 | NES 713; CO content |
| 0.12 | NES 713; CO<sub>2</sub> content | |
| 0.17 | NES 713; Total gases |
Users viewing this material also viewed the following:
- MV Labs NH900 (NH4)H2PO4 Ammonium dihydrogen phosphate
- Hexion Bakelite™ PF 31 Phenolic Formaldehyde Resin, UL Listed (discontinued **)
- Solvay Specialty Polymers Solef® 60512 Polyvinylidene Fluoride (PVDF)
- Samsung Cheil Industries Starex® GR-4015A ABS, Glass Filled
- Dow Corning SYL-OFF® 7671 COATING
- DSM Akulon® K222-KGMV14 Nylon 6-25% Glass and Mineral Reinforced (European Grade) (Dry)
- ExxonMobil Enable™ 20-05HH Metallocene Polyethylene Resin (European Grade)
- Asahi Kasei Tenac® LA541 Homopolymer Acetal Resin
- BASF Ultramid® 8231G HS BK-102 14% Glass Filled PA6 (Dry)
Copyright © lookpolymers.com All Rights Reserved