Victrex® PEEK 90CA30 Polyetheretherketone, 30% Carbon Fibre Reinforced

Category	Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) , Polyetheretherketone, PEEK, Carbon Fiber Filled
Manufacturer	Victrex
Trade Name	PEEK
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Victrex® PEEK 90CA30 Polyetheretherketone, 30% Carbon Fibre Reinforced.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Product Description:High performance thermoplastic material, 30% carbon fibre reinforced Polyetheretherketone (PEEK), semi crystalline, granules for injection moulding, very easy flow, FDA food contact compliant, colour black.Typical Application Areas:Complex geometries with thinner cross sections or longer flow length where higher strength in a static or dynamic system is required. Excellent wear resistance, low coefficient of friction, low coefficient of thermal expansion. Chemically resistant to aggressive environments.Information Provided by VICTREX®

Physical Properties	Metric	English	Comments
Density	1.40 g/cc	0.0506 lb/in³	Crystalline; ISO 1183
Water Absorption at Saturation	0.30 % @Temperature 23.0 °C	0.30 % @Temperature 73.4 °F	Equilibrium; by immersion; ISO 62-1
	0.45 % @Temperature 100 °C	0.45 % @Temperature 212 °F	immersion; ISO 62-1
Viscosity	250000 cP @Temperature 400 °C	250000 cP @Temperature 752 °F	melt; ISO 11443
Linear Mold Shrinkage, Flow	0.0010 cm/cm	0.0010 in/in	360°C nozzle, 160°C tool; ISO 294-4
Linear Mold Shrinkage, Transverse	0.0050 cm/cm	0.0050 in/in	380°C nozzle, 190°C tool; ISO 294-4
Spiral Flow	13.0 cm @Thickness 1.00 mm	5.12 in @Thickness 0.0394 in	380°C nozzle, 190°C tool

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	88 @Temperature 23.0 °C	88 @Temperature 73.4 °F	ISO 868
Tensile Strength at Break	65.0 MPa @Temperature 275 °C	9430 psi @Temperature 527 °F	ISO 527
	85.0 MPa @Temperature 225 °C	12300 psi @Temperature 437 °F	ISO 527
	110 MPa @Temperature 175 °C	16000 psi @Temperature 347 °F	ISO 527
	180 MPa @Temperature 125 °C	26100 psi @Temperature 257 °F	ISO 527
	275 MPa @Temperature 23.0 °C	39900 psi @Temperature 73.4 °F	ISO 527
Elongation at Break	1.4 % @Temperature 23.0 °C	1.4 % @Temperature 73.4 °F	ISO 527
Tensile Modulus	28.0 GPa @Temperature 23.0 °C	4060 ksi @Temperature 73.4 °F	ISO 527
Flexural Strength	65.0 MPa @Temperature 225 °C	9430 psi @Temperature 437 °F	ISO 178
	130 MPa @Temperature 175 °C	18900 psi @Temperature 347 °F	ISO 178
	275 MPa @Temperature 125 °C	39900 psi @Temperature 257 °F	ISO 178
	380 MPa @Temperature 23.0 °C	55100 psi @Temperature 73.4 °F	ISO 178
Flexural Modulus	24.0 GPa @Temperature 23.0 °C	3480 ksi @Temperature 73.4 °F	ISO 178
Compressive Strength	70.0 MPa @Temperature 200 °C	10200 psi @Temperature 392 °F	ISO 604
	200 MPa @Temperature 120 °C	29000 psi @Temperature 248 °F	ISO 604
	300 MPa @Temperature 23.0 °C	43500 psi @Temperature 73.4 °F	ISO 604
Izod Impact, Notched (ISO)	7.00 kJ/m² @Temperature 23.0 °C	3.33 ft-lb/in² @Temperature 73.4 °F	ISO 180/A
Izod Impact, Unnotched (ISO)	40.0 kJ/m² @Temperature 23.0 °C	19.0 ft-lb/in² @Temperature 73.4 °F	ISO 180/U
Charpy Impact Unnotched	4.50 J/cm²	21.4 ft-lb/in²	ISO 179/1U
Charpy Impact, Notched	0.600 J/cm²	2.86 ft-lb/in²	ISO 179/1eA

Thermal Properties	Metric	English	Comments
CTE, linear	40.0 µm/m-°C @Temperature <=143 °C	22.2 µin/in-°F @Temperature <=289 °F	Average below Tg; ISO 11359
	90.0 µm/m-°C @Temperature >=143 °C	50.0 µin/in-°F @Temperature >=289 °F	Average above Tg; ISO 11359
CTE, linear, Parallel to Flow	5.00 µm/m-°C @Temperature <=143 °C	2.78 µin/in-°F @Temperature <=289 °F	Below Tg; ISO 11359
	5.00 µm/m-°C @Temperature >=143 °C	2.78 µin/in-°F @Temperature >=289 °F	Above Tg; ISO 11359
Specific Heat Capacity	1.80 J/g-°C @Temperature 23.0 °C	0.430 BTU/lb-°F @Temperature 73.4 °F	DSC
Thermal Conductivity	2.00 W/m-K	13.9 BTU-in/hr-ft²-°F	Along flow; ISO 22007-4
	0.950 W/m-K @Temperature 23.0 °C	6.59 BTU-in/hr-ft²-°F @Temperature 73.4 °F	Average; ISO/CD 22007-4
Melting Point	343 °C	649 °F	ISO 11357
Deflection Temperature at 1.8 MPa (264 psi)	342 °C	648 °F	ISO 75A-f
Glass Transition Temp, Tg	143 °C	289 °F	Onset; ISO 11357
Glow Wire Test	960 °C @Thickness 2.00 mm	1760 °F @Thickness 0.0787 in	IEC 60695-2-12

Electrical Properties	Metric	English	Comments
Volume Resistivity	1e+05	1e+05	1V; ASTM D4496

Processing Properties	Metric	English	Comments
Processing Temperature	<= 100 °C	<= 212 °F	Hopper Temperature
Nozzle Temperature	380 °C	716 °F
Mold Temperature	170 - 200 °C	338 - 392 °F
Drying Temperature	120 °C @Time 18000 sec	248 °F @Time 5.00 hour
	150 °C @Time 10800 sec	302 °F @Time 3.00 hour

Descriptive Properties	Value	Comments
Toxicity Index	0.05	NES 713; CO content
	0.12	NES 713; CO<sub>2</sub> content
	0.17	NES 713; Total gases