LATI Latamid 66 H2 G/60 PA 66, 60% Glass Fiber Reinforced, Heat Stabilized

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 60% Glass Fiber Filled
Manufacturer LATI
Trade Name Latamid
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latamid 66 H2 G/60 PA 66, 60% Glass Fiber Reinforced, Heat Stabilized.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polyamide 66 (PA66) based compound. Heat stabilized. Glass fibers.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.69 g/cc
0.0611 lb/in³
Linear Mold Shrinkage, Flow 0.0025 - 0.0055 cm/cm
0.0025 - 0.0055 in/in
Linear Mold Shrinkage, Transverse 0.0060 - 0.0090 cm/cm
0.0060 - 0.0090 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 95.0 MPa

@Temperature 150 °C
 13800 psi

@Temperature 302 °F
110 MPa

@Temperature 120 °C
 16000 psi

@Temperature 248 °F
130 MPa

@Temperature 90.0 °C
 18900 psi

@Temperature 194 °F
170 MPa

@Temperature 60.0 °C
 24700 psi

@Temperature 140 °F
215 MPa

@Temperature 23.0 °C
 31200 psi

@Temperature 73.4 °F
Elongation at Break 2.0 %

@Temperature 23.0 °C
 2.0 %

@Temperature 73.4 °F
3.0 %

@Temperature 60.0 °C
 3.0 %

@Temperature 140 °F
3.5 %

@Temperature 90.0 °C
 3.5 %

@Temperature 194 °F
4.5 %

@Temperature 120 °C
 4.5 %

@Temperature 248 °F
5.0 %

@Temperature 150 °C
 5.0 %

@Temperature 302 °F
Tensile Modulus 6.30 GPa

@Temperature 150 °C
 914 ksi

@Temperature 302 °F
8.20 GPa

@Temperature 120 °C
 1190 ksi

@Temperature 248 °F
10.5 GPa

@Temperature 90.0 °C
 1520 ksi

@Temperature 194 °F
16.0 GPa

@Temperature 60.0 °C
 2320 ksi

@Temperature 140 °F
21.0 GPa

@Temperature 23.0 °C
 3050 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 7.00 J/cm²
33.3 ft-lb/in²
Charpy Impact, Notched 1.00 J/cm²
4.76 ft-lb/in²
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 135 °C
275 °F
Deflection Temperature at 0.46 MPa (66 psi) 260 °C
500 °F
Deflection Temperature at 1.8 MPa (264 psi) 245 °C
473 °F
Vicat Softening Point 255 °C

@Load 5.00 kg
 491 °F

@Load 11.0 lb
Flammability, UL94 HB

@Thickness 0.750 mm
 HB

@Thickness 0.0295 in
Processing Properties Metric English Comments
Melt Temperature 280 - 310 °C
536 - 590 °F
Mold Temperature 80.0 - 100 °C
176 - 212 °F
Drying Temperature 90.0 - 100 °C

@Time 10800 sec
 194 - 212 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa