LATI Larpeek 10 G/15 PEEK, 15% Glass Fiber Reinforced

Category Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) , Polyetheretherketone, PEEK, Glass Fiber Filled
Manufacturer LATI
Trade Name Larpeek
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Larpeek 10 G/15 PEEK, 15% Glass Fiber Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polyetheretherketone (PEEK) based compound. Glass fibers. Very good chemical resistance. Very good thermal properties. Low smoke density and low toxicity index.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.40 g/cc
0.0506 lb/in³
Linear Mold Shrinkage, Flow 0.0040 - 0.0065 cm/cm
0.0040 - 0.0065 in/in
Linear Mold Shrinkage, Transverse 0.0070 - 0.010 cm/cm
0.0070 - 0.010 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 70.0 MPa

@Temperature 150 °C
 10200 psi

@Temperature 302 °F
90.0 MPa

@Temperature 120 °C
 13100 psi

@Temperature 248 °F
110 MPa

@Temperature 90.0 °C
 16000 psi

@Temperature 194 °F
125 MPa

@Temperature 60.0 °C
 18100 psi

@Temperature 140 °F
135 MPa

@Temperature 23.0 °C
 19600 psi

@Temperature 73.4 °F
Elongation at Break 2.8 %

@Temperature 23.0 °C
 2.8 %

@Temperature 73.4 °F
3.1 %

@Temperature 60.0 °C
 3.1 %

@Temperature 140 °F
3.4 %

@Temperature 90.0 °C
 3.4 %

@Temperature 194 °F
3.8 %

@Temperature 120 °C
 3.8 %

@Temperature 248 °F
4.5 %

@Temperature 150 °C
 4.5 %

@Temperature 302 °F
Elongation at Yield 3.0 %

@Temperature 90.0 °C
 3.0 %

@Temperature 194 °F
3.0 %

@Temperature 120 °C
 3.0 %

@Temperature 248 °F
3.5 %

@Temperature 150 °C
 3.5 %

@Temperature 302 °F
Tensile Modulus 5.10 GPa

@Temperature 150 °C
 740 ksi

@Temperature 302 °F
5.50 GPa

@Temperature 120 °C
 798 ksi

@Temperature 248 °F
5.70 GPa

@Temperature 90.0 °C
 827 ksi

@Temperature 194 °F
6.10 GPa

@Temperature 60.0 °C
 885 ksi

@Temperature 140 °F
6.30 GPa

@Temperature 23.0 °C
 914 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 4.00 J/cm²

@Temperature -20.0 °C
 19.0 ft-lb/in²

@Temperature -4.00 °F
4.50 J/cm²

@Temperature 23.0 °C
 21.4 ft-lb/in²

@Temperature 73.4 °F
Charpy Impact, Notched 0.300 J/cm²

@Temperature -20.0 °C
 1.43 ft-lb/in²

@Temperature -4.00 °F
0.400 J/cm²

@Temperature 23.0 °C
 1.90 ft-lb/in²

@Temperature 73.4 °F
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 220 °C
428 °F
Deflection Temperature at 0.46 MPa (66 psi) 290 °C
554 °F
Deflection Temperature at 1.8 MPa (264 psi) 285 °C
545 °F
Vicat Softening Point >= 300 °C

@Load 5.00 kg
 >= 572 °F

@Load 11.0 lb
Flammability, UL94 V-1

@Thickness 0.750 mm
 V-1

@Thickness 0.0295 in
V-0

@Thickness 3.00 mm
 V-0

@Thickness 0.118 in
V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in
Processing Properties Metric English Comments
Melt Temperature 370 - 400 °C
698 - 752 °F
Mold Temperature 170 - 200 °C
338 - 392 °F
Drying Temperature 120 - 150 °C

@Time 10800 sec
 248 - 302 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa