LATI Lapex A G/20 PES, 20% Glass Fiber Reinforced

Category Polymer , Thermoplastic , Polyethersulfone (PES) , Polyethersulfone (PES), 20%Glass Fiber Filled
Manufacturer LATI
Trade Name Lapex
Port Shanghai port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF LATI Lapex A G/20 PES, 20% Glass Fiber Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Polyether Sulfone (PES) based compound. Glass fibers. Low smoke density and low toxicity index. Very high dimensional stability.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.49 g/cc
0.0538 lb/in³
Linear Mold Shrinkage, Flow 0.0035 - 0.0050 cm/cm
0.0035 - 0.0050 in/in
Linear Mold Shrinkage, Transverse 0.0075 - 0.0090 cm/cm
0.0075 - 0.0090 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 80.0 MPa
<br>@Temperature 150 °C
 11600 psi
<br>@Temperature 302 °F
90.0 MPa
<br>@Temperature 120 °C
 13100 psi
<br>@Temperature 248 °F
100 MPa
<br>@Temperature 90.0 °C
 14500 psi
<br>@Temperature 194 °F
110 MPa
<br>@Temperature 60.0 °C
 16000 psi
<br>@Temperature 140 °F
115 MPa
<br>@Temperature 23.0 °C
 16700 psi
<br>@Temperature 73.4 °F
Elongation at Break 2.5 %
<br>@Temperature 23.0 °C
 2.5 %
<br>@Temperature 73.4 °F
2.6 %
<br>@Temperature 60.0 °C
 2.6 %
<br>@Temperature 140 °F
2.7 %
<br>@Temperature 90.0 °C
 2.7 %
<br>@Temperature 194 °F
2.8 %
<br>@Temperature 120 °C
 2.8 %
<br>@Temperature 248 °F
3.0 %
<br>@Temperature 150 °C
 3.0 %
<br>@Temperature 302 °F
Elongation at Yield 2.5 %
<br>@Temperature 150 °C
 2.5 %
<br>@Temperature 302 °F
Tensile Modulus 5.90 GPa
<br>@Temperature 150 °C
 856 ksi
<br>@Temperature 302 °F
6.15 GPa
<br>@Temperature 120 °C
 892 ksi
<br>@Temperature 248 °F
6.30 GPa
<br>@Temperature 90.0 °C
 914 ksi
<br>@Temperature 194 °F
6.50 GPa
<br>@Temperature 60.0 °C
 943 ksi
<br>@Temperature 140 °F
6.70 GPa
<br>@Temperature 23.0 °C
 972 ksi
<br>@Temperature 73.4 °F
Charpy Impact Unnotched 3.50 J/cm²
16.7 ft-lb/in²
Charpy Impact, Notched 0.400 J/cm²
1.90 ft-lb/in²
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 180 °C
356 °F
Deflection Temperature at 0.46 MPa (66 psi) 220 °C
428 °F
Deflection Temperature at 1.8 MPa (264 psi) 215 °C
419 °F
Vicat Softening Point 220 °C
<br>@Load 5.00 kg
 428 °F
<br>@Load 11.0 lb
Flammability, UL94 V-0
<br>@Thickness 3.00 mm
 V-0
<br>@Thickness 0.118 in
V-0
<br>@Thickness 1.50 mm
 V-0
<br>@Thickness 0.0591 in
Oxygen Index 39 %
39 %
Processing Properties Metric English Comments
Melt Temperature 350 - 370 °C
662 - 698 °F
Mold Temperature 140 - 165 °C
284 - 329 °F
Drying Temperature 150 - 180 °C
<br>@Time 10800 sec
 302 - 356 °F
<br>@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa