Wellman Wellamid® GFT13-66 XE-N 13% Impact Modified Glass Reinforced Nylon 66/6, Lubricated & Heat Stabilized

Category Polymer , Thermoplastic , Nylon , Nylon 6/66 , Nylon 66/Nylon 6 Blend, Glass Fiber Filled
Manufacturer Wellman Engineering Resins
Trade Name Wellamid®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Wellman Wellamid® GFT13-66 XE-N 13% Impact Modified Glass Reinforced Nylon 66/6, Lubricated & Heat Stabilized.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Typical Applications: Machinery gear trains and linkage, conveyor belt links, fasteners, auto under hood and door parts, automotive door handles, appliance parts, sporting goods, lawn and garden equipment.Data provided by the manufacturer, Wellman Inc.
Physical Properties Metric English Comments
Density 1.18 g/cc
0.0426 lb/in³
ISO 1183
Water Absorption 1.2 %
1.2 %
Approximate 24 hr.
Linear Mold Shrinkage 0.0080 - 0.012 cm/cm
0.0080 - 0.012 in/in
ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 85.0 MPa
12300 psi
ISO 527
Elongation at Break 5.0 %
5.0 %
ISO 527
Flexural Yield Strength 120 MPa
17400 psi
ISO 178
Flexural Modulus 3.80 GPa
551 ksi
ISO 178
Izod Impact, Notched 0.900 J/cm
1.69 ft-lb/in
ISO 180
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 200 °C
392 °F
ISO 75
Flammability, UL94 HB

@Thickness 0.790 mm
HB

@Thickness 0.0311 in
From Wellman QC Laboratory Testing; UL 94
Processing Properties Metric English Comments
Rear Barrel Temperature 282 - 310 °C
540 - 590 °F
Middle Barrel Temperature 277 - 304 °C
530 - 580 °F
Front Barrel Temperature 271 - 299 °C
520 - 570 °F
Nozzle Temperature 271 - 304 °C
520 - 580 °F
Melt Temperature 271 - 304 °C
520 - 580 °F
Mold Temperature 71.1 - 93.3 °C
160 - 200 °F
Drying Temperature 79.4 °C
175 °F
Opened bags and gaylord boxes
Dry Time 2 - 4 hour
2 - 4 hour
Opened bags and gaylord boxes
Moisture Content 0.050 - 0.20 %
0.050 - 0.20 %
During molding to prevent hydrolytic degradation
<= 0.20 %
<= 0.20 %
In shipping bags, ready to mold
Injection Pressure 34.5 - 138 MPa
5000 - 20000 psi
Back Pressure 0.345 MPa
50.0 psi
Screw Speed 30 - 120 rpm
30 - 120 rpm