Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 85.0 MPa @Temperature 60.0 °C |
12300 psi @Temperature 140 °F |
ISO 527 |
LATI LARIL 13 G/20-V1 20% Glass Fiber Reinforced Polyphenylene Oxide (PPOm) (UL94V-1)
(Unverified Data**) Description: Laril thermoplastics are polyphenylene oxide (PPOm) products. They exhibit excellent toughness, even at low temperatures, good thermal resistance and dimensional stability are the most .. |
|||
Tensile Strength, Ultimate | 85.0 MPa | 12300 psi | 5 mm/min |
Polimeri Europa KOBLEND PCA PD 935 G4 PC+ABS, 20% Glass Fiber
(discontinued **) Symbol according to ISO 1043/1/2: PC+ABS (GF) Injection moulding grade, reinforced with 20% glass fibres, high stiffness, very good dimensional stability. Main application fields: structural non a.. |
|||
Tensile Strength, Ultimate | 85.0 MPa | 12300 psi | ISO 527 |
LATI LATAN 13 K/30 30% Carbon Fiber Reinforced Polyoxymethylene Copolymer (POM)
(Unverified Data**) Description: Latan series thermoplastics are polyoxymethylene copolymer (POM) products. The main applications for Latan feature good wear resistance, chemical inertness and low water absorption (gea.. |
|||
Tensile Strength, Ultimate | 85.0 MPa @Temperature 22.0 °C |
12300 psi @Temperature 71.6 °F |
25mm flat samples, compression moulded; ISO 527-4 |
Menzolit Menzolit® SMC 0430 Unsaturated Polyester UP SMC 0430 is a low emission Class-A SMC for on-line painted exterior body applications on passenger cars. These compounds mould to parts with excellent surface quality for on-line painted body panel.. |
|||
Tensile Strength, Ultimate | 84.8 MPa | 12300 psi | |
Shinil Chemical SHINSTRA PA-66 W100SRB Structural Polymer Abrasion Resistance SHINSTRA is the product line of structural polymer compound which exhibits excellent physical, mechanical, and thermal properties. Shinil uses the state-of-the-art dispersion and blending technolog.. |
|||
Tensile Strength, Ultimate | 85.0 MPa | 12300 psi | 5mm/min; ISO 527 |
Styrolution Terblend® N NG-06 30% Glass Filled ABS/PA6 (Conditioned) Terblend N NG-06 is a 30% glass fiber reinforced ABS/PA6 blend with extra high rigidity and dimensional stability.Information provided by STYROLUTION, which is a joint venture between BASF and INEOS.. |
|||
Tensile Strength, Ultimate | 85.0 MPa | 12300 psi | ISO 527 |
Wellman Wellamid® 22LN2-N Unfilled Nylon 66, Lubricated & Nucleated Typical Applications: Automotive components, gears, switches, bearings, pulleys, fasteners, electrical coil forms, chain-saw hand guards, cable ties, furniture hardware, small appliance housings, ae.. |
|||
Tensile Strength, Ultimate | 85.0 MPa | 12300 psi | ISO 527 |
Wellman Wellamid® GFT13-66 XE-N 13% Impact Modified Glass Reinforced Nylon 66/6, Lubricated & Heat Stabilized Typical Applications: Machinery gear trains and linkage, conveyor belt links, fasteners, auto under hood and door parts, automotive door handles, appliance parts, sporting goods, lawn and garden equ.. |
|||
Tensile Strength, Ultimate | 85.0 MPa | 12300 psi | ISO 527 |
Wellman Wellamid® MR409 22H-N 40% Mineral Reinforced Nylon 66, Heat Stabilized Typical Applications: Lawn and garden equipment, automotive trim, bezels, wheel covers, window frames, gas tank filler housings, brackets, metalized lighting reflectors for automotive, automotive co.. |
|||
Tensile Strength, Ultimate | 85.0 MPa | 12300 psi | ASTM D638 |
Toyobo T-422-02R Nylon, Mineral-Reinforced Key Feature: High heat distortion and good toughness, high flowInformation provided by Toyobo Co., Ltd |
|||
Tensile Strength, Ultimate | 85.0 MPa | 12300 psi | dry; ISO 527-1/-2 |
DSM Akulon® K222-KGV5 25% Glass Reinforced, Flame Retardant (Halogen free), Heat Stabilized |
|||
Tensile Strength, Ultimate | 85.0 MPa | 12300 psi | dry; ISO 527-1/-2 |
DSM Akulon® K224-PG2 PA6-I-GF8 8% Glass Reinforced, Impact Modified |
|||
Tensile Strength, Ultimate | 85.0 MPa | 12300 psi | cond; ISO 527-1/-2 |
DSM Akulon® XG-FKGS6 PA6-GF30 FR 30% Glass Reinforced, Flame Retardant, Halogen free |
|||
Tensile Strength, Ultimate | 85.0 MPa | 12300 psi | Diametral tensile strength |
3M Filtek™ Z250 Universal Restorative Dental Composite 3M™ Filtek™ Z250 universal restorative is an esthetic, light cured, radiopaque composite specifically designed for use in anterior or posterior direct or indirect restorations. Bonding to tooth s.. |
|||
Tensile Strength, Ultimate | 85.0 MPa | 12300 psi | 5mm/min; ISO 527 |
BASF Ultradur B 4300 G2 LS High Speed BK15045 10% Glass Filled PBT |
|||
Tensile Strength, Ultimate | 85.0 MPa | 12300 psi | 5mm/min; ISO 527 |
BASF Ultramid® 8260 40% Mineral Filled PA6 (Dry) Ultramid 8260 is a 40% mineral reinforced PA6 injection molding compound. It possesses high stiffness, dimensional stability and heat resistance combined with excellent processability including low.. |
|||
Tensile Strength, Ultimate | 85.0 MPa | 12300 psi | 5mm/min; ISO 527 |
BASF Ultramid® 8260 HS BK-102 40% Mineral Filled PA6 (Dry) Ultramid 8260 HS BK-102 is a heat stabilized, pigmented black, 40% mineral reinforced PA6 injection molding resin. It possesses high stiffness, dimensional stability and heat resistance combined wi.. |
|||
Tensile Strength, Ultimate | 85.0 MPa | 12300 psi | 5mm/min; ISO 527 |
BASF Ultramid® 8260 HS PA6 (Dry) |
|||
Tensile Strength, Ultimate | 85.0 - 95.0 MPa | 12300 - 13800 psi | Typical |
ATI Allegheny Ludlum AL 20™ Plate Specialty Steel The N08020 alloy has been available for many years and has found applications in many environments, such as in chlorides and in sulfuric and sulfurous acids.Although AL 20 alloy was developed for im.. |
|||
Tensile Strength, Ultimate | 85.0 MPa | 12300 psi | 5 mm/min |
Arkema Group Rilsan® AZM 23 T6LD Nylon 12, 23% Glass Fiber Filled (Dry) Designation ISO 1874-PA12,MHLR,16-050,GF23Rigid grade with glass fiber filler (23%) for injection molding. Available colors: black and natural. Reinforced light and heat stabilizing agent. Mold-rele.. |
|||
Tensile Strength, Ultimate | 85.0 MPa | 12300 psi | ATSM D638 |
Ashley Polymers Ashlene® 830SMS Nylon 6, MoS2 Filled Basic Nylon 6, medium viscosity, lubricated with Molybdenum Disulfide.Data provided by the manufacturer |
|||
Tensile Strength, Ultimate | 85.0 MPa | 12300 psi | 5mm/min; ISO 527 |
BASF Ultramid® A3EG3 15% Glass Filled PA66 (Conditioned) Ultramid A3EG3 is a 15% glass fiber reinforced injection molding PA66 grade. It conforms to FDA requirements of 21 CFR 177.1500. |
|||
Tensile Strength, Ultimate | 85.0 MPa | 12300 psi | 5mm/min; ISO 527 |
BASF Ultramid® B3M6 30% Mineral Filled PA6 (Dry) Ultramid B3M6 is a 30% mineral reinforced injection molding PA6 grade for industrial items requiring high impact strength and very high dimensional stability, excellent laser markability. |
|||
Tensile Strength, Ultimate | 85.0 MPa | 12300 psi | ASTM D638 |
A. Schulman ComAlloy Comtuf® 413 Glass Reinforced, Polycarbonate/Polyester Alloy, UL Data provided by the manufacturer, ComAlloy International Company.20% Glass Reinforced. Superior toughness and impact resistance characterize Comtuf® materialsThe ComAlloy product line has been int.. |
|||
Tensile Strength, Ultimate | 85.0 MPa | 12300 psi | ASTM D638 |
A. Schulman ComAlloy Hiloy® 637 Nylon 6/6, Glass/Mineral Reinforced, Flow Enhanced, UL Data provided by the manufacturer, ComAlloy International Company.20% Glass/Mineral Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
Tensile Strength, Ultimate | 85.0 MPa | 12300 psi | ASTM data at 5 mm/min. |
BASF Capron® 8260 40% Mineral-Filled Nylon 6 (Dry)
(discontinued **) Capron 8260 is a 40% mineral reinforced polyamide 6 injection molding compound. It possesses high stiffness, dimensional stability and heat resistance combined with excellent processability includi.. |
|||
Tensile Strength, Ultimate | 85.0 MPa | 12300 psi | ASTM D638 |
Chevron Phillips Ryton® PR09-60 Polyphenylene Sulfide Compound, Annealed 2 hours at 200°C
(discontinued **)&l Polyphenylene Sulfide CompoundRyton® PR09-60 Annealed 2 hours at 200°C is pelletized unfilled high molecular weight polyphenylene sulfide resin suitable for extrusion or injection molding.Comments.. |
|||
Tensile Strength, Ultimate | 85.0 MPa @Temperature 60.0 °C |
12300 psi @Temperature 140 °F |
ISO 527 |
LATI LARIL 13 G/30-V1 30% Glass Fiber Reinforced Polyphenylene Oxide (PPOm) (UL94V-1)
(Unverified Data**) Description: Laril thermoplastics are polyphenylene oxide (PPOm) products. They exhibit excellent toughness, even at low temperatures, good thermal resistance and dimensional stability are the most .. |