Techmer ES Luriblend® PE 5903

Category Polymer , Thermoplastic , Polyethylene (PE) , HDPE
Manufacturer Techmer ES
Trade Name Luriblend®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Techmer ES Luriblend® PE 5903.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Availability: North AmericaForms: PelletsAdditive: LubricantFeatures: Lubricated, Good Wear Resistance and Low FrictionProcessing Method: Injection MoldingInformation provided by TP Composites, Inc.
Physical Properties Metric English Comments
Density 0.970 g/cc
0.0350 lb/in³
ASTM D792
Water Absorption 0.070 %

@Time 86400 sec
 0.070 %

@Time 24.0 hour
 ASTM D570
Linear Mold Shrinkage, Flow 0.030 cm/cm

@Thickness 3.17 mm
 0.030 in/in

@Thickness 0.125 in
 ASTM D955
Melt Flow 1.7 g/10 min

@Load 3.80 kg,
Temperature 190 °C
 1.7 g/10 min

@Load 8.38 lb,
Temperature 374 °F
 ASTM D1238
24 g/10 min

@Load 10.0 kg,
Temperature 190 °C
 24 g/10 min

@Load 22.0 lb,
Temperature 374 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Yield 214 MPa
31000 psi
ASTM D638
Elongation at Break 50 %
50 %
ASTM D638
Flexural Strength 41.4 MPa
6000 psi
ASTM D790
Flexural Modulus 0.483 GPa
70.0 ksi
ASTM D790
Izod Impact, Notched 0.694 J/cm

@Thickness 3.17 mm
 1.30 ft-lb/in

@Thickness 0.125 in
 ASTM D256
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 90.0 µm/m-°C
50.0 µin/in-°F
ASTM D696
Deflection Temperature at 0.46 MPa (66 psi) 93.3 °C
200 °F
Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 54.4 °C
130 °F
Unannealed; ASTM D648
Flammability, UL94 HB
HB
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+16 ohm-cm
1.00e+16 ohm-cm
ASTM D257
Dielectric Strength 19.7 kV/mm
500 kV/in
Method A (Short-Time); ASTM D149