- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 93.3 °C
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 93.3 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 93.3 °C | 200 °F | ASTM D648 |
| RheTech Products FT7011-01 Thermoplastic Polyolefin, Non-UV Stabilized, Black Applications: Claddings and faciasExterior componentsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 93.3 °C | 200 °F | ASTM D648 |
| RheTech Products HP513-00 High Performance Polypropylene Copolymer, Non-UV Stabilized, Natural Applications: Interior trimI/P componentsCenter consolesInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 93.3 °C | 200 °F | ASTM D648 |
| RheTech Products P250-01 Polypropylene Copolymer, Black Applications: ConsolesConsumer goodsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 93.3 °C | 200 °F | ASTM D648 |
| RheTech Products P251-01 Polypropylene Copolymer, Black Applications: Splash shieldFuse panel coversCenter consolesDoor panelsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 93.3 °C | 200 °F | ASTM D648 |
| Polymer Resources ABS-G5 ABS, 5% Glass Reinforced Acrylonitrile Butadiene Styrene, 5% Glass ReinforcedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 93.3 °C | 200 °F | ASTM D648 |
| Polymer Resources ABS-G5-[color]-3 ABS, 5% Glass Reinforced, UV-stabilized Acrylonitrile Butadiene Styrene, 5% Glass Reinforced, UV-stabilizedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test sampl.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 93.3 - 112 °C | 200 - 233 °F | Average value: 102 °C Grade Count:29 |
| Overview of materials for Acrylonitrile Butadiene Styrene (ABS), 10% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Acrylonitrile Butadiene Styrene (ABS), 10% Glass Fiber Filled". Specific grades with glass content betwe.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 93.3 °C | 200 °F | 0.250 in; ASTM D648 |
| M. Holland Company AB105 ABS Features: Medium Flow, High Impact Resistance, Good StiffnessUses: Household Goods, Packaging Processing Method: Injection MoldingInformation provided by M. Holland. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 93.3 °C | 200 °F | ASTM D648 |
| M. Holland Company CP700 Polypropylene Copolymer Features: High Flow, High Impact Resistance, Good StiffnessUses: Automotive Interior Parts, Closures, Household Goods, ToysApprovals: FDA 21 CFR 177.1520 Processing Method: Injection MoldingInform.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 93.3 °C | 200 °F | ASTM D648 |
| Ineos N02G-00 Polypropylene Impact Copolymer Grade N02G-00 is a low melt flow rate, high-impact copolymer polypropylene for sheet extrusion and thick wall injection molding applications. It offers a superior balance of stiffness and impact str.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 93.3 °C | 200 °F | ASTM D648 |
| Spartech PE4125 Reinforced High Density Polyethylene Compound Spartech Polycom's filled high molecular weight, high density polyethylenes are specifically designed for blow molding and sheet extrusion /thermoforming of structural parts. These materials offer a.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 93.3 °C | 200 °F | Unannealed; ASTM D648 |
| Techmer ES Luriblend® PE 5903 Availability: North AmericaForms: PelletsAdditive: LubricantFeatures: Lubricated, Good Wear Resistance and Low FrictionProcessing Method: Injection MoldingInformation provided by TP Composites, Inc... |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 93.3 °C | 200 °F | Unannealed; ASTM D648 |
| Techmer ES Luriblend® TPX-HDPE-99018 Availability: North AmericaForms: Pellets)Features: Good Wear Resistance and Low FrictionProcessing Method: Injection MoldingTPCI# 8869115Information provided by TP Composites, Inc. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 93.3 °C | 200 °F | Unannealed; ASTM D648 |
| Techmer ES Statiblend® 02020 MB Polypropylene, 5% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber, 5% Filler by Weight/Unspecified FillerReinforFeatures: ConductiveTPCI# 9117116Information provided by TP Composites, Inc. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 93.3 °C | 200 °F | unannealed; ASTM D648; ISO 75-2/B |
| Styron INSPIREâ„¢ TF1302 Thermoplastic Polyolefin Information provided by DowThe Inspire brand was spun off from Dow Chemical to Styron in 2010 |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 93.3 °C | 200 °F | ASTM D648 |
| A. Schulman PP 2268-01 Polypropylene High Flow, Impact Copolymer Polypropylene DescriptionPolypropylene PP 2268-01 is an automotive recognized high flow impact copolymer polypropylene.ApplicationPP 2173-01 is intended for use in interior trim applications.Information provided .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 93.3 °C @Thickness 3.17 mm |
200 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| Chase Plastics CP Pryme® A100HF ABS Molding Resin, High Flow Information provided by Chase Plastics. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 93.3 °C | 200 °F | ASTM D648 |
| Washington Penn Medium Impact Copolymer 30% Calcium Carbonate Filled Calcium carbonate-filled polypropylene compounds have been tailored specifically to meet the requirements of each of the major automobile producers. Grades are available to meet FDA food and drug pa.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 93.3 °C | 200 °F | ASTM D648 |
| A. Schulman PP 1817-01 Polypropylene Utility Grade Random Co-Polymer DescriptionPolypropylene PP 1817-01 is a utility grade random co-polymer which can be used for general purpose injection molding, extrusion, or blow molding applications. It does not have a gel spe.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 93.3 °C | 200 °F | ASTM D648 |
| A. Schulman PP 2268-01 Polypropylene High Flow, Impact Copolymer Polypropylene DescriptionPolypropylene PP 2268-01 is an automotive recognized high flow impact copolymer polypropylene.ApplicationPP 2173-01 is intended for use in interior trim applications.Information provided .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 93.3 °C | 200 °F | ASTM D648 |
| A. Schulman PP 1817-01 Polypropylene Utility Grade Random Co-Polymer DescriptionPolypropylene PP 1817-01 is a utility grade random co-polymer which can be used for general purpose injection molding, extrusion, or blow molding applications. It does not have a gel spe.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 93.3 °C | 200 °F | ASTM D648 |
| A. Schulman PP 2268-01 Polypropylene High Flow, Impact Copolymer Polypropylene DescriptionPolypropylene PP 2268-01 is an automotive recognized high flow impact copolymer polypropylene.ApplicationPP 2173-01 is intended for use in interior trim applications.Information provided .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 93.3 °C | 200 °F | ASTM D648 |
| A. Schulman PP 1817-01 Polypropylene Utility Grade Random Co-Polymer DescriptionPolypropylene PP 1817-01 is a utility grade random co-polymer which can be used for general purpose injection molding, extrusion, or blow molding applications. It does not have a gel spe.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 93.3 °C | 200 °F | ISO 75-2/Bf |
| ExxonMobil AP03B Polypropylene Impact Copolymer Product Description: A high crystallinity, medium impact copolymer resin with high melt flow rate and excellent processing attributes. It is designed for injection molded large appliance applicatio.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 93.3 °C | 200 °F | ASTM D648 |
| Spartech PP7240 Calcium Carbonate Filled High Impact Copolymer Provides the highest level of impact of all copolymers and are useful in applications where improved processing and stiffness are required versus unfilled copolymer materials.Information provided by.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 93.3 °C | 200 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill FR® PA12 IM FR Availability: North AmericaForms: PelletsAdditive: Heat Stabilizer, Impact Modifier and LubricantFeatures: Flame Retardant, Heat Stabilized, Impact Modified and LubricatedInformation provided by TP .. |
|||