Styrolution Luran® S 778 TE UV Colored ASA

Category Polymer , Thermoplastic , ASA Polymer
Manufacturer Styrolution
Trade Name Luran®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Styrolution Luran® S 778 TE UV Colored ASA.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Extrusion grade with enhanced toughness and heat distortion resistance.Information provided by STYROLUTION, which is a joint venture between BASF and INEOS
Physical Properties Metric English Comments
Density 1.07 g/cc
0.0387 lb/in³
ISO 1183
Water Absorption 1.65 %
1.65 %
Equilibrium; ISO 62
0.45 %

@Time 86400 sec
0.45 %

@Time 24.0 hour
ISO 62
Moisture Absorption at Equilibrium 0.35 %
0.35 %
23°C/50% RH; ISO 62
Melt Flow 5.35 g/10 min

@Load 10.0 kg,
Temperature 220 °C
5.35 g/10 min

@Load 22.0 lb,
Temperature 428 °F
ISO 1133
Mechanical Properties Metric English Comments
Ball Indentation Hardness 85.0 MPa

@Load 36.5 kg,
Time 30.0 sec
12300 psi

@Load 80.5 lb,
Time 0.00833 hour
ISO 2039-1
Tensile Strength, Yield 54.0 MPa
7830 psi
50 mm/min; ISO 527-1/-2
Elongation at Break 8.0 %
8.0 %
Nominal, 50 mm/min; ISO 527-1/-2
Elongation at Yield 3.4 %
3.4 %
50 mm/min; ISO 527-1/-2
Tensile Modulus 2.50 GPa
363 ksi
ISO 527-1/-2
Flexural Strength 80.0 MPa
11600 psi
ISO 178
Charpy Impact Unnotched 9.00 J/cm²

@Temperature -30.0 °C
42.8 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eU
25.0 J/cm²

@Temperature 23.0 °C
119 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eU
Charpy Impact, Notched 0.400 J/cm²

@Temperature -30.0 °C
1.90 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
1.50 J/cm²

@Temperature 23.0 °C
7.14 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Tensile Creep Modulus, 1000 hours 1250 MPa

@Strain <=0.500 %
181000 psi

@Strain <=0.500 %
ISO 899-1
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 80.0 - 110 µm/m-°C

@Temperature 23.0 - 80.0 °C
44.4 - 61.1 µin/in-°F

@Temperature 73.4 - 176 °F
ISO 11359-1/-2
Thermal Conductivity 0.170 W/m-K
1.18 BTU-in/hr-ft²-°F
DIN 52612-1
Maximum Service Temperature, Air 90.0 °C
194 °F
Deflection Temperature at 0.46 MPa (66 psi) 106 °C
223 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 103 °C
217 °F
ISO 75-1/-2
Vicat Softening Point 104 °C
219 °F
VST/B/50; ISO 306
113 °C
235 °F
VST/A/50; ISO 306
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
IEC 60695-11-10
HB

@Diameter 4.00 mm
HB

@Diameter 0.157 in
IEC 60707
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+12 ohm-cm
1.00e+12 ohm-cm
IEC 60093
Surface Resistance 1.00e+13 ohm
1.00e+13 ohm
IEC 60093
Dielectric Constant 3.5

@Frequency 1.00e+6 Hz
3.5

@Frequency 1.00e+6 Hz
IEC 60250
3.9

@Frequency 100 Hz
3.9

@Frequency 100 Hz
IEC 60250
Dielectric Strength 35.0 kV/mm
889 kV/in
K20/P20; IEC 60243-1
Dissipation Factor 0.0090

@Frequency 100 Hz
0.0090

@Frequency 100 Hz
IEC 60250
0.033

@Frequency 1.00e+6 Hz
0.033

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 600 V
600 V
Test Liquid A; IEC 60112
Processing Properties Metric English Comments
Melt Temperature 200 - 240 °C
392 - 464 °F
Extrusion, Pipes
210 - 250 °C
410 - 482 °F
Extrusion, Plates
Drying Temperature 80.0 °C
176 °F
Pre-drying
Dry Time 2 - 4 hour
2 - 4 hour
Pre-drying
Descriptive Properties Value Comments
Color Brown 36949
Brown 36950
Brown 37002
Commercial Status Europe
Primary Processing Technique Extrusion