Solvay Specialty Polymers Polidan® T/A-LV Polyethylene, Crosslinked (XLPE)

Category Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Crosslinkable
Manufacturer Solvay Specialty Polymers
Trade Name Polidan®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Polidan® T/A-LV Polyethylene, Crosslinked (XLPE).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
POLIDAN® T/A-LV is a silane crosslinkable PE compound which is used together with a catalyst masterbatch to accelerate the crosslinking reaction. It is used for flexible crosslinkable pipes.Features: Crosslinkable; High Density; High GlossUses: Piping; Plumbing PartsAdditional Properties: Extruder Screw Compression Ratio - >2.5:1; Extruder Screw L/D Ratio - 25:1 to 30:1; Gel Content - EN 579 > 65 %; Head Temperature - 200 °CInformation provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Density 0.957 g/cc
0.0346 lb/in³
ASTM D792
Melt Flow 1.2 g/10 min
1.2 g/10 min
ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength >= 20.0 MPa
>= 2900 psi
ASTM D638
Elongation at Break >= 350 %
>= 350 %
ASTM D638
Tensile Modulus 1.30 GPa
189 ksi
ISO 527-2
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 150 µm/m-°C

@Temperature 20.0 °C
83.3 µin/in-°F

@Temperature 68.0 °F
1
Specific Heat Capacity 1.90 J/g-°C
0.454 BTU/lb-°F
ASTM C351
Thermal Conductivity 0.460 - 0.480 W/m-K
3.19 - 3.33 BTU-in/hr-ft²-°F
ASTM C177
Vicat Softening Point 129 °C
264 °F
ASTM D1525
Processing Properties Metric English Comments
Zone 1 150 - 200 °C
302 - 392 °F
Zone 2 150 - 200 °C
302 - 392 °F
Zone 3 150 - 200 °C
302 - 392 °F
Zone 4 150 - 200 °C
302 - 392 °F
Zone 5 150 - 200 °C
302 - 392 °F
Die Cooling Temperature 210 °C
410 °F
Descriptive Properties Value Comments
Availability Asia Pacific
Europe
North America
Processing Technique Extrusion; Pipe Extrusion
Copyright © lookpolymers.com All Rights Reserved