SABIC Innovative Plastics LNP LUBRILOY D2000AXH PC

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP Lubriloy
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRILOY D2000AXH PC.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP LUBRILOY* D2000AXH is a compound based on Polycarbonate resin containing Proprietary Lubricant. Added features of this material include: Wear Resistant, Healthcare.
Physical Properties Metric English Comments
Density 1.17 g/cc
0.0423 lb/in³
ASTM D792
1.17 g/cc
0.0423 lb/in³
ISO 1183
Moisture Absorption 0.130 %
0.130 %
50% RH, 24 hrs; ASTM D570
0.190 %
0.190 %
23°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.0070 - 0.0090 cm/cm

@Time 86400 sec
0.0070 - 0.0090 in/in

@Time 24.0 hour
ASTM D955
0.0070 - 0.0090 cm/cm

@Time 86400 sec
0.0070 - 0.0090 in/in

@Time 24.0 hour
ISO 294
Linear Mold Shrinkage, Transverse 0.0080 - 0.010 cm/cm

@Time 86400 sec
0.0080 - 0.010 in/in

@Time 24.0 hour
ASTM D955
0.0080 - 0.010 cm/cm

@Time 86400 sec
0.0080 - 0.010 in/in

@Time 24.0 hour
ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 53.0 MPa
7690 psi
ISO 527
60.0 MPa
8700 psi
ASTM D638
Tensile Strength, Yield 53.0 MPa
7690 psi
ASTM D638
54.0 MPa
7830 psi
ISO 527
Elongation at Break 125.6 %
125.6 %
ASTM D638
138 %
138 %
ISO 527
Elongation at Yield 6.2 %
6.2 %
ISO 527
6.5 %
6.5 %
ASTM D638
Tensile Modulus 1.86 GPa
270 ksi
50 mm/min; ASTM D638
1.98 GPa
287 ksi
1 mm/min; ISO 527
Flexural Strength 78.0 MPa
11300 psi
ISO 178
82.0 MPa
11900 psi
ASTM D790
Flexural Modulus 2.13 GPa
309 ksi
ASTM D790
2.13 GPa
309 ksi
ISO 178
Izod Impact, Notched 7.15 J/cm
13.4 ft-lb/in
ASTM D256
Izod Impact, Unnotched NB
NB
ASTM D4812
Izod Impact, Notched (ISO) 56.0 kJ/m²
26.6 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 137 kJ/m²
65.2 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 40.0 J
29.5 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 48.0 J
35.4 ft-lb
Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic 0.16
0.16
ASTM D3702 Modified
Coefficient of Friction, Static 0.090
0.090
ASTM D3702 Modified
K (wear) Factor 121 x 10-8 mm³/N-M
60.0 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 74.1 µm/m-°C

@Temperature -40.0 - 40.0 °C
41.2 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
74.2 µm/m-°C

@Temperature -40.0 - 40.0 °C
41.2 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 73.8 µm/m-°C

@Temperature -40.0 - 40.0 °C
41.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
73.8 µm/m-°C

@Temperature -40.0 - 40.0 °C
41.0 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 140 °C
284 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
140 °C

@Thickness 3.20 mm
284 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 126 °C
259 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
126 °C

@Thickness 3.20 mm
259 °F

@Thickness 0.126 in
unannealed; ASTM D648
Flammability, UL94 HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
UL 94