Solvay Specialty Polymers Hyflon® PFA 120X Perfluoroalkoxy (PFA)  (discontinued **)

Category Polymer , Thermoplastic , Fluoropolymer , PFA
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Hyflon® PFA 120X Perfluoroalkoxy (PFA)  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Hyflon® PFA is a unique family of semi-crystalline, melt processable perfluoropolymers which combine excellent mechanical characteristics to unique properties such as chemical inertness, heat resistance, inherent flame resistance, low surface energy, and exceptional dielectric properties. Hyflon® PFA resins have been designed to retain their properties over a wide range of temperatures from cryogenic to 250-260°C (482-500°F) and are the material of choice in applications such as linings in the Chemical Process Industry, specialty cables, semiconductor industry, aerospace, and other challenging industries. Hyflon® PFA 120X is a low melt flow rate resin designed for blow molding applications, where very high viscosity and melt strength are needed. It also has significantly lower permeability to gasses than standard PFAs'.Additional Information: PROCESSING Because PFA is corrosive in the melt, machinery used to process Hyflon should be lined with corrosion resistant alloys. HEALTH SAFETY AND ENVIRONMENT Hyflon® PFA 120X is a very inert polymer and it is not harmful if used and handled according to standard processing procedures. If handled inappropriately, it may release harmful toxic chemicals. Please refer to the Material Safety Data Sheets for more information on handling and safety. PACKAGING AND STORAGE Hyflon® PFA 120X resin is available in 25 kg (55 lbs) and 600 kg (1323 lbs) packaging. Though it has an indefinite shelf life, it is recommended to store it in a clean area, protected from direct sunlight, and possible contamination.Information provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Density 2.12 - 2.17 g/cc
0.0766 - 0.0784 lb/in³
ASTM D792
Melt Flow 2.5 - 5.0 g/10 min

@Load 5.00 kg,
Temperature 372 °C
2.5 - 5.0 g/10 min

@Load 11.0 lb,
Temperature 702 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 4.60 MPa

@Temperature 280 °C
667 psi

@Temperature 536 °F
ASTM D1708
>= 26.0 MPa

@Temperature 23.0 °C
>= 3770 psi

@Temperature 73.4 °F
ASTM D1708
Elongation at Break >= 300 %

@Temperature 23.0 °C
>= 300 %

@Temperature 73.4 °F
ASTM D1708
480 %

@Temperature 280 °C
480 %

@Temperature 536 °F
ASTM D1708
Tensile Modulus 0.0490 GPa

@Temperature 280 °C
7.11 ksi

@Temperature 536 °F
1mm/min; ASTM D1708
0.500 - 0.600 GPa

@Temperature 23.0 °C
72.5 - 87.0 ksi

@Temperature 73.4 °F
1.0 mm/min; ASTM D1708
Thermal Properties Metric English Comments
Heat of Fusion 34.0 - 45.0 J/g
14.6 - 19.4 BTU/lb
DSC
35.0 - 45.0 J/g
15.1 - 19.4 BTU/lb
Crystallization Heat; DSC
CTE, linear 120 - 200 µm/m-°C
66.7 - 111 µin/in-°F
ASTM D696
Specific Heat Capacity 0.900 - 1.10 J/g-°C

@Temperature 23.0 °C
0.215 - 0.263 BTU/lb-°F

@Temperature 73.4 °F
DSC
Thermal Conductivity 0.200 W/m-K

@Temperature 40.0 °C
1.39 BTU-in/hr-ft²-°F

@Temperature 104 °F
ASTM C177
Melting Point 310 - 325 °C
590 - 617 °F
ASTM D3307
Crystallization Temperature 295 °C
563 °F
Peak, DSC
Descriptive Properties Value Comments
Agency Ratings ASTM D 3307 Type II
Availability Africa & Middle East
Asia Pacific
Europe
North America
South America
Features Flame Retardant
High Heat Resistance
Low Flow
Semi Crystalline
Forms Pellets
Generic PFA
Processing Method Extrusion
Uses Aerospace Applications
Cable Jacketing
Liners
Piping
Semiconductor Molding Compounds
Tubing