Solvay Specialty Polymers Amodel® AF-4133 V0 Polyphthalamide (PPA) Resin, 33% Glass Reinforced  (discontinued

Category Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), 30% Glass Fiber Reinforced
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Amodel® AF-4133 V0 Polyphthalamide (PPA) Resin, 33% Glass Reinforced  (discontinued.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
AMODEL AF-4133 V0 is a 33% glass reinforced grade of polyphthalamide (PPA) resin that was designed specifically to process with water-cooled molds and meet the requirements of most electrical/electronic interconnect devices. These components often consist of thin-walled, intricate designs, and frequently need to withstand IR solder reflow temperatures, pin insertions or other mechanical assembly, and may be exposed to potential ignition sources. Therefore, the material has good mechanical strength, high deflection temperature, flame retardancy, and good flow. This material processes readily using conventional injection molding equipment and methods. The processing window is relatively broad, and mold temperatures as low as 150°F (65°C) can be used.This product line was acquired by Solvay Advanced Polymers from BP Amoco in November 2001.
Physical Properties Metric English Comments
Density 1.68 g/cc
0.0607 lb/in³
ASTM D792
Water Absorption 0.18 %
0.18 %
24 hrs. ASTM D570
Linear Mold Shrinkage 0.0035 cm/cm
0.0035 in/in
ASTM E831
Linear Mold Shrinkage, Transverse 0.0060 cm/cm
0.0060 in/in
ASTM E831
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 178 MPa
25800 psi
ASTM D638
Elongation at Break 1.8 %
1.8 %
ASTM D638
Tensile Modulus 13.8 GPa
2000 ksi
ASTM D638
Flexural Yield Strength 255 MPa
37000 psi
ASTM D790
Flexural Modulus 12.4 GPa
1800 ksi
ASTM D790
Izod Impact, Notched 0.650 J/cm
1.22 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
Melting Point 332 °C
630 °F
ASTM D3418
Deflection Temperature at 1.8 MPa (264 psi) 294 °C
561 °F
ASTM D648
Flammability, UL94 V-0

@Thickness 0.800 mm
V-0

@Thickness 0.0315 in
V-0

@Thickness 0.800 mm
V-0

@Thickness 0.0315 in
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
ASTM D257
Surface Resistance 5.00e+13 ohm
5.00e+13 ohm
ASTM D257
Dielectric Strength 21.0 kV/mm
533 kV/in
ASTM D149
Arc Resistance >= 300 sec
>= 300 sec
UL 746A
Comparative Tracking Index 500 V
500 V
Processing Properties Metric English Comments
Melt Temperature 330 - 352 °C