Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Yield Strength | 255 MPa | 37000 psi | ASTM D790 |
Performance Polymers IPS II PPL-C4150 PEKK (Polyetherketoneketone) Linear 30 % Glass Fiber Reinforced Molding Grade Amber pelletsInformation provided by Infinite Polymer System II. |
|||
Flexural Yield Strength | 255 MPa | 37000 psi | ASTM D790 |
Solvay Specialty Polymers Amodel® AT-1125 HS Polyphthalamide (PPA)
(Unverified Data**) Amodel AT-1125 HS polyphthalamide (PPA) is a toughened, heat stabilized 25% glass reinforced resin, designed as a cost effective solution for applications requiring stiffness, good dimensional stabi.. |
|||
Flexural Yield Strength | 255 MPa | 37000 psi | ASTM D790 |
Solvay Specialty Polymers Amodel® AF-4133 V0 Polyphthalamide (PPA) Resin, 33% Glass Reinforced
(discontinued AMODEL AF-4133 V0 is a 33% glass reinforced grade of polyphthalamide (PPA) resin that was designed specifically to process with water-cooled molds and meet the requirements of most electrical/electr.. |
|||
Flexural Yield Strength | 255 MPa | 37000 psi | ASTM D790 |
PolyOne Edgetek® LCP-30CF/000 Liquid Crystal Polymer - 30% Carbon Fiber
(discontinued **) Data provided by PolyOne. |
|||
Flexural Yield Strength | 255 MPa | 37000 psi | ASTM D790 |
Chevron Phillips Ryton® BR42C Polyphenylene Sulfide Compound
(discontinued **) Black Polyphenylene Sulfide CompoundRyton® BR42C is a 40% fiberglass reinforced polyphenylene sulfide compound specially formulated to have a low coefficient of friction for use in low surface fric.. |
|||
Flexural Yield Strength | 255 MPa @Thickness 6.40 mm |
37000 psi @Thickness 0.252 in |
1.3mm/min; ASTM D790 |
LG Chemical LUMID GP2300A(W) PA6+GF30%, General Purpose Feature: Injection Molding, PA6+GF30%, General PurposeApplication: Automotive (Side Mirror Base Plate)CAS No. 25038-54-4 and 65997-17-3Information provided by LG Chemical |
|||
Flexural Yield Strength | 255 MPa @Thickness 6.40 mm |
37000 psi @Thickness 0.252 in |
2.8mm/min; ASTM D790 |
LG Chemical LUMID GP2309A(W) PA6+GF30%, General Purpose Feature: Injection Molding,PA6+GF30%, General PurposeApplication: Automotive (Cooling Fan)CAS No. 25038-54-4 and 65997-17-3Information provided by LG Chemical |
|||
Flexural Yield Strength | 255 MPa @Thickness 3.20 mm |
37000 psi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
LG Chemical LUMID GP2339B(W) PA66+GF33%, General Purpose Feature: Injection Molding, PA66+GF33%, General PurposeApplication: Automotive (Cylinder Head Cover)CAS No. 32131-17-2 and 65997-17-3Information provided by LG Chemical |
|||
Flexural Yield Strength | 255 MPa @Thickness 3.20 mm |
37000 psi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
LG Chemical LUMID SG2300B(W) PA66+GF30%, General Purpose, Good Surface Feature: Injection Molding, PA66+GF30%, General Purpose, Good SurfaceApplication: Automotive PartsCAS No. 32131-17-2, 13983-17-0 and 65997-17-3Information provided by LG Chemical |
|||
Flexural Yield Strength | 255 MPa | 37000 psi | at 3.5% strain; ISO 178-A |
Lanxess Durethan® BKV 30 H2.0 EF 901510 Nylon 6, 30% Glass Fiber PA 6, 30% glass fibers, good flowability (Easy Flow), good heat-ageing resistance |
|||
Flexural Yield Strength | 255 MPa | 37000 psi | DIN 53455; ASTM D790 |
Kolon KOPA® KN132G30VO G/F Reinforced Flame Retardant Nylon 6 KOPA® is a thermoplastic resin with excellent mechanical, thermal and electrical properties and is widely used in automobile and industrial parts.Good mechanical properties, outstanding self-lubr.. |
|||
Flexural Yield Strength | 255 MPa | 37000 psi | DIN 53455; ASTM D790 |
Kolon KOPA® KN133G30 G/F Reinforced Nylon 6 KOPA® is a thermoplastic resin with excellent mechanical, thermal and electrical properties and is widely used in automobile and industrial parts.Good mechanical properties, outstanding self-lubr.. |
|||
Flexural Yield Strength | 255 MPa | 37000 psi | ASTM D790 |
Solvay Specialty Polymers Amodel® AT-1125 HS Polyphthalamide (PPA), 25% Glass Fiber (Dry) Amodel® AT-1125 HS polyphthalamide (PPA) is a toughened, heat stabilized 25% glass reinforced resin, designed as a cost effective solution for applications requiring stiffness, good dimensional s.. |
|||
Flexural Yield Strength | 255 MPa | 37000 psi | ASTM D790 |
Techmer ES HiFill FR® TPX-HTN-01031 35% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber, 35% Filler by WeightAdditive: Heat Stabilizer Features: Flame Retardant, Heat Stabilized and High Temperature Strength UL .. |
|||
Flexural Yield Strength | 255 MPa | 37000 psi | ASTM D790 |
Techmer ES HiFill® PA4/6 GF30 HS NAT 30% Glass Filled (Dry) Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 30% Filler by WeightAdditive: Heat StabilizerFeatures: Heat StabilizedAppearance: Natural ColorInformation p.. |
|||
Flexural Yield Strength | 255 MPa | 37000 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Valox® V8090 PBT+PET (Europe-Africa-Middle East) 50% Glass Fiber Reinforced PBT-PET resin |
|||
Flexural Yield Strength | 255 MPa | 37000 psi | ASTM D790 |
Toyobo Vylopet® EMC145 Glass Reinforced Polyester, Standard Grade Key Feature: Flame retardant V-0 UL-94 classApplications: Ultra-precise componentsGeneral features of Vylopet® include heat resistance, good mechanical properties, high dielectric strength and trac.. |
|||
Flexural Yield Strength | 255 MPa | 37000 psi | ASTM D790 |
Cheng Yu Plastic N6G20 Nylon 6, 20% Glass Filled |
|||
Flexural Yield Strength | 255 MPa | 37000 psi | ASTM D790 |
Clariant Renol PA111G30IF Nylon 66, 30% Glass Fiber, Improved Flow Data provided by Clariant Masterbatches |