Schwartz Technical Plastics LAMIGAMID® 100 Polyamide 6, Extruded, Dry
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Extruded |
| Manufacturer | Schwartz Technical Plastics |
| Trade Name | LAMIGAMID® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Schwartz Technical Plastics LAMIGAMID® 100 Polyamide 6, Extruded, Dry.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Application: machine parts under 80 mm diameter, hammer-heads, cup-shaped bearing shellsInformation provided by Schwartz Technical Plastics GmbH
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ISO R 1183 |
| Moisture Absorption at Equilibrium | 2.5 - 3.0 % | 2.5 - 3.0 % | DIN 53473 |
| Water Absorption at Saturation | 8.5 - 10 % @Temperature 20.0 °C |
8.5 - 10 % @Temperature 68.0 °F |
ISO R 62 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 160 MPa | 23200 psi | Hc 30; ISO 2039; partially |
| Tensile Strength, Yield | 80.0 MPa | 11600 psi | ISO-DIS 527 |
| Creep Strength | >= 7.00 MPa | >= 1020 psi | 1% elongation, 1000 h; DIN 53444 |
| >= 10.5 MPa | >= 1520 psi | 2% elongation, 1000 h; DIN 53444 | |
| Tensile Modulus | 3.20 GPa | 464 ksi | DIN 53457 |
| Flexural Strength | 130 MPa | 18900 psi | DIN 54352 |
| Flexural Modulus | 2.50 GPa | 363 ksi | DIN 53457 |
| Izod Impact, Notched (ISO) | NB | NB | DIN 53453 |
| Izod Impact Resistance | NB | NB | swinging hammer 0,1 DIN 51222; DIN 53453 |
| Coefficient of Friction | 0.040 | 0.040 | With lubrication |
| Coefficient of Friction, Dynamic | 0.38 | 0.38 | no lube; Steel 2162, Rvst=2E-6m, p=0.05 Mpa, v=0.6 m/s, t=40°C |
| Tear Strength Test | >= 0.50 | >= 0.50 | ISO-DIS 527 |
| K Factor (Wear Factor) | 2.3e-10 | 2.3e-10 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 70.0 - 100 µm/m-°C @Temperature 20.0 - 100 °C |
38.9 - 55.6 µin/in-°F @Temperature 68.0 - 212 °F |
DIN 53752 |
| Specific Heat Capacity | 1.67 J/g-°C | 0.399 BTU/lb-°F | |
| Thermal Conductivity | 0.230 W/m-K | 1.60 BTU-in/hr-ft²-°F | DIN 52612 |
| Melting Point | 220 °C | 428 °F | ISO R 1218 |
| Maximum Service Temperature, Air | 100 °C | 212 °F | Continuous |
| 160 °C | 320 °F | Intermittent | |
| Deflection Temperature at 0.46 MPa (66 psi) | 190 °C | 374 °F | V-notch; ISO R 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 95.0 °C | 203 °F | V-notch; ISO R 75 |
| Minimum Service Temperature, Air | -40.0 °C | -40.0 °F | Continuous |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | DIN 53482 |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | DIN 53482 |
| Dielectric Constant | 3.7 | 3.7 | DIN 53483 |
| Dielectric Strength | 50.0 kV/mm | 1270 kV/in | DIN 53481 |
| Dielectric Loss Index | 0.031 | 0.031 | DIN 53483 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Creepage/leakage Resistance | KA3c | DIN 53480 |
Users viewing this material also viewed the following:
- PolyMirae Moplen 342R Injection Molding Grade Polypropylene
- PolyOne Geon™ Vinyl Flexible B85B0 Polyvinyl Chloride, Flexible (PVC, Flexible)
- M. Holland Company LD225 LDPE (discontinued **)
- Solvay Specialty Polymers Torlon® 7130 Polyamide-imide (PAI), 30% Carbon Fiber
- Zircar Zirconia Buster M-35 Alumina Board, Disc, and Cylinder Insulation
- Formosa Plastics Formolene® HP4401 Pipe HDPE
- Daikin NEOFLON NF-1500 FEP Film
- Ensinger TECASINT 4211 SD Polyimide, Black, Carbon Fiber (PI)
- Dura-Bar 60-40-18 Continuously Cast Ductile Iron Bar Stock ASTM A536, 4018
- ACC EP MAP-10 EPI Engineered Polymers Aliphatic Polymer
Copyright © lookpolymers.com All Rights Reserved