Solvay Specialty Polymers Torlon® 7130 Polyamide-imide (PAI), 30% Carbon Fiber

Category Polymer , Thermoplastic , Polyamide-imide (PAI)
Manufacturer Solvay Specialty Polymers
Trade Name Torlon®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Torlon® 7130 Polyamide-imide (PAI), 30% Carbon Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Torlon® 7130 is an 30% carbon-fiber reinforced grade of polyamide-imide (PAI) resin. It offers high strength and modulus, exceptional creep resistance, and good fatigue resistance. It has thermal expansion characteristics similar to steel, and therefore excellent dimensional stability.Features: Fatigue Resistant; Flame Retardant; Good Chemical Resistance; Good Compressive Strength; Good Creep Resistance; Good Dimensional Stability; High Heat Resistance; High Stiffness; High Temperature Strength; Semi ConductiveUses: Aerospace Applications; Aircraft Applications; Business Equipment; Connectors; Electrical/Electronic Applications; Film; Gears; Housings; Industrial Applications; Industrial Parts; Machine/Mechanical Parts; Metal Replacement; Oil/Gas Applications; Semiconductor Molding CompoundsAdditional Properties: Coefficient of Linear Thermal Expansion - ASTM D696 9.0E-6 cm/cm/°CInformation provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Density 1.48 g/cc
0.0535 lb/in³
ASTM D792
Filler Content 30 %
30 %
Carbon Fiber
Water Absorption 0.26 %

@Time 86400 sec
0.26 %

@Time 24.0 hour
ISO 62
Linear Mold Shrinkage, Flow 0.00 - 0.0015 cm/cm
0.00 - 0.0015 in/in
Mechanical Properties Metric English Comments
Tensile Strength 221 MPa
32100 psi
ASTM D638
Tensile Stress 203 MPa
29400 psi
ASTM D1708
Flexural Strength 174 MPa

@Temperature 232 °C
25200 psi

@Temperature 450 °F
ASTM D790
350 MPa

@Temperature 23.0 °C
50800 psi

@Temperature 73.4 °F
ASTM D790
Flexural Modulus 15.7 GPa

@Temperature 232 °C
2280 ksi

@Temperature 450 °F
ASTM D790
19.9 GPa

@Temperature 23.0 °C
2890 ksi

@Temperature 73.4 °F
ASTM D790
Compressive Strength 254 MPa
36800 psi
ASTM D695
Compressive Modulus 9.86 GPa
1430 ksi
ASTM D695
Izod Impact, Notched 0.480 J/cm
0.899 ft-lb/in
ASTM D256
Izod Impact, Unnotched 3.20 J/cm
5.99 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
Thermal Conductivity 0.520 W/m-K
3.61 BTU-in/hr-ft²-°F
ASTM C177
Deflection Temperature at 1.8 MPa (264 psi) 282 °C
540 °F
Unannealed; ASTM D648
Processing Properties Metric English Comments
Rear Barrel Temperature 304 °C
579 °F
Nozzle Temperature 371 °C
700 °F
Mold Temperature 199 - 216 °C
390 - 421 °F
Drying Temperature 177 °C

@Time 10800 sec
351 °F

@Time 3.00 hour
Moisture Content <= 0.050 %
<= 0.050 %
Back Pressure 6.89 MPa
999 psi
Screw Speed 50 - 100 rpm
50 - 100 rpm
Descriptive Properties Value Comments
Availability Africa & Middle East
Asia Pacific
Europe
Latin America
North America
Form Pellets
Processing Technique Injection Molding; Machining; Profile Extrusion