Polymer Property : Flexural Modulus = 2.50 GPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Modulus	2.50 GPa	363 ksi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics Cycoloy® C6840 PC+ABS (Asia Pacific) Cycoloy* C6840 resin is an injection moldable, flame retardant PC/ABS blend. It contains non-chlorinated & non-brominated flame retardant systems intended to meet governmental regulations and variou..
Flexural Modulus	2.50 GPa	363 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics Cycoloy® CU6800 PC+ABS (Europe-Africa-Middle East) Non-chlorinated and non-brominated flame retardant PC/ABS featuring excellent flow properties for a wide variety of applications including business equipment, TVs, monitors, enclosures, among others..
Flexural Modulus	2.50 GPa	363 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics Cycoloy® CX7110 PC+ABS (Europe-Africa-Middle East) Cycoloy* resin grade CX7110 is an injection moldable PC/ABS blend with non-brominated and non-chlorinated flame retardant systems. Excellent impact/flow balance together with a UL-94 V0 rating at 1...
Flexural Modulus	2.50 GPa	363 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics Cycoloy® CX7240 PC+ABS Cycoloy* CX7240 resin is an injection moldable PC/ABS blend. It contains non-brominated and non-chlorinated flame retardant systems to meet UL-94 V0 at 0.75mm, V1 at 0.6mm, V2 at 0.2mm and 5VB at 1...
Flexural Modulus	2.50 GPa	363 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics Cycoloy® CX7240 PC+ABS (Europe-Africa-Middle East) Cycoloy* CX7240 resin is an injection moldable PC/ABS blend. It contains non-brominated and non-chlorinated flame retardant systems to meet UL-94 V0 at 0.75mm, V1 at 0.6mm, V2 at 0.4mm and 5VB at 1...
Flexural Modulus	2.50 GPa	363 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics Cycoloy® CX7240U PC+ABS Cycoloy* CX7240U resin is an injection moldable PC/ABS blend with a UV stabilization package. It contains non-brominated and non-chlorinated flame retardant systems to meet thin wall flame resistanc..
Flexural Modulus	2.50 GPa	363 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics Lexan® CFR5630D PC COPOLYMER (Asia Pacific) LEXAN™ CFR5630D Polycarbonate (PC) is a non-filled resin, suitable for injection molding and extrusion. This non-chlorinated, non-brominated flame retardant PC resin meets FAR25.853 smoke density a..
Flexural Modulus	2.50 GPa	363 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics Lexan® XHT3143 PC Copolymer XHT3143 is a high flow, UV stabilized, high heat polycarbonate copolymer. It is available in a range of opaque and limited transparent colors.
Flexural Modulus	2.50 GPa	363 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP Lubricomp DBL14 PC (Europe-Africa-Middle East) Internally lubricated Polycarbonate compound, comtaining Glass Bead and PTFEThis data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Flexural Modulus	2.50 GPa	363 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics Cycoloy® CS9610 PC+ABS (Asia Pacific) Cycoloy* CS9610 is a FR PC/ABS blend using non-brominated and non-chlorinated flame retardant systems, offering optimum mechanical & impact balance and excellent flammability and low smoke behavior...
Flexural Modulus	2.50 GPa	363 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics Geloy FXTW26SK ASA (Asia Pacific) Next generation Geloy XTW ASA for high heat exterior applications. Outstanding weatherability and toughness. Metallic sparkle VisualFx.This data was supplied by SABIC-IP for the Asia Pacific region...
Flexural Modulus	2.50 GPa	363 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics Lexan® SLX2432T PC Copolymer (Europe-Africa-Middle East) Medium viscosity PC copolymer with enhanced UV stabilization and added release agent. V2 rated. Available in transparent and tinted colors.This data was supplied by SABIC-IP for the Europe-Africa-M..
Flexural Modulus	2.50 GPa	363 ksi
Lehmann & Voss LUVOCOMÂ® 19-7827 Polyamide 46, with PTFE, easy flowing Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Isotropic shrinkage characteri..
Flexural Modulus	2.50 GPa	363 ksi	ISO 178
FiberfilÂ® J-60/10/CC/30/E NATL Polypropylene Homopolymer, 10% FiberGlass and 30% Calcium Carbonate Reinforced, Chemically coupled Information provided by FIBERFIL Engineered Plastics
Flexural Modulus	2.50 GPa	363 ksi	ASTM D790
LG Chemical LUCEL EC-605B Electrically Conductive POM, 5% Carbon Black Filled LUCEL semi-crystalline acetal copolymer resins are produced by gas phase polymerization. LUCEL resins can be widely accepted as the replacement of thermosets, aluminum and zinc die-casts or other m..
Flexural Modulus	2.50 GPa	363 ksi	ASTM D790
Kolon KOCETALÂ® LW701 Wear Modified Acetal Resin Special polymer added, improved wear property. Applications: Products for low noise and precision gear. Information provided by API-Kolon.
Flexural Modulus	2.50 GPa	363 ksi	ISO 178
Aardvark Polymers AARTELÂ® 800AM Rotational Molding Resin Aartel 800AM is a new antimicrobial grade that offers the same excellent physical and mechanical properties of standard Aartel grades plus the added benefit of protection against microbial growth, p..
Flexural Modulus	2.50 GPa	363 ksi	DIN 53457
Schwartz Technical Plastics LAMIGAMIDÂ® 100 Polyamide 6, Extruded, Dry Application: machine parts under 80 mm diameter, hammer-heads, cup-shaped bearing shellsInformation provided by Schwartz Technical Plastics GmbH
Flexural Modulus	2.50 GPa	363 ksi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics ValoxÂ® IQ3001 PBT (Asia Pacific) Valox IQ3001 is an unfilled environmentally responsible iQ-PBT resin modified with elastomer. Targeted for flexible hinge applications.
Flexural Modulus	2.50 GPa	363 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics ValoxÂ® V2000DM PBT Unreinforced, directly metallizable PBT injection molding resin with high flow better release characteristics.
Flexural Modulus	2.50 GPa	363 ksi	D790
Zhejiang Juner 302-G0 Flammable Resistant and Low Separate Out Mode Applications: Electrons and Electricity: TV Components, Plugs of Computers, Exhaust Fans of Computers, Plugs, Sockets, Shells of Electronics, Framework of Level Output Transformers, Pipe Pedestals, ..
Flexural Modulus	2.50 GPa	363 ksi	ISO 178
Unitika M1030DH PA6, Conditioned Nano composite nylonInformation provided by Unitika Ltd.
Flexural Modulus	2.50 GPa	363 ksi	ASTM D790
Eastman Eastar MN021 Copolyester Eastar copolyester MN021 is a thermoplastic condensation copolymer produced by a continuous melt-phase polymerization process followed by a solid-state polymerization process. It has been crystalliz..
Flexural Modulus	2.50 GPa	363 ksi	ASTM D 790
Cossa Polimeri ESTACARB 2060 V0 HF Flame Retardant Polycarbonate Flame retardant class V0, opaque, antimony, chlorine and bromine free, high impact resistance, high thermal resistance, good melt flow rate, good processability, good light resistanceInformation pro..
Flexural Modulus	2.50 GPa	363 ksi	2 mm/min; ISO 178
Eurostar Starflam PX06012 PA6, Flame Retardant, Injection Molded Starflam PX06012 is an Unfilled, Halogen Free and Red Phosphorous Free, Flame Retardant, Polyamide 6 Injection Molding ResinInformation provided by Eurostar.
Flexural Modulus	2.50 GPa	363 ksi	ISO 178
Celanese CELANEX 2001 PBT, Unfilled Celanex 2001 is an unreinforced polybutylene terephthalate resin with improved hydrolysis resistance developed for use in fiber optic buffer tube applications. Celanex 2001 exhibits the high melt st..
Flexural Modulus	2.50 GPa	363 ksi	ASTM D790
Ascend Performance Materials VYDYNE® 45 Nylon, Impact Modified, Weather Stable Typical property data. VYDYNE is a registered trademark of Solutia Inc.
Flexural Modulus	2.50 GPa	363 ksi	ASTM D790
Beijing Chemical Industry KAIFA® 302-G0 PBT Resin Flame retardant, low bleedingInformation provided by Beijing Chemical Industry Research Institute (Group)
Flexural Modulus	2.50 GPa	363 ksi	ISO 178
Polyplastics Duracon® M90-45 Acetal Co-polymer (POM), Weather resistance, General DURACON® is a crystalline thermoplastic acetal copolymer. The primary raw material trioxane, a trimer of formaldehyde.The thermoplastic adopts a copolymer structure in which polyoxymethylene (-C-O)..
Flexural Modulus	2.50 GPa	363 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics Lexan® LUX7632C PC COPOLYMER Lexan* LUX7632C Polycarbonate (PC) resin is a non-filled, extrudable grade. This non-chlorinated, non-brominated flame retardant PC has an UL-94 V0 rating at 1.0 mm / 5VA rating at 3.0mm and is U..