Sax Polymers SAXAMID 226F5RY01 Nylon 6.6, 25% Glass Fiber

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 20% Glass Fiber Filled , Nylon 66, Glass Fiber Filled, Flame Retardant
Manufacturer Sax Polymers
Trade Name SAXAMID
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Sax Polymers SAXAMID 226F5RY01 Nylon 6.6, 25% Glass Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
SAXAMID 226F5RY01 is a polyamide 6.6 injection-molding-grade reinforced with 25% glass fibers. It has a halogen-free flame retardant and UL listed.Information provided by SAX Polymers
Physical Properties Metric English Comments
Density 1.34 g/cc
0.0484 lb/in³
ISO 1183
Viscosity Test 150 cm³/g
150 cm³/g
H<sub>2</sub>SO<sub>4</sub>; ISO 307
Mechanical Properties Metric English Comments
Tensile Strength 125 MPa
18100 psi
5 mm/min; ISO 527-1
Elongation at Break 2.3 %
2.3 %
5 mm/min; ISO 527-1
Tensile Modulus 9.60 GPa
1390 ksi
1 mm/min; ISO 527-1
Flexural Strength 200 MPa
29000 psi
2 mm/min; ISO 178
Flexural Modulus 7.60 GPa
1100 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 8.00 kJ/m²

@Temperature -30.0 °C
 3.81 ft-lb/in²

@Temperature -22.0 °F
 ISO 180/1A
9.00 kJ/m²

@Temperature 23.0 °C
 4.28 ft-lb/in²

@Temperature 73.4 °F
 ISO 180/1A
Izod Impact, Unnotched (ISO) 47.0 kJ/m²

@Temperature -30.0 °C
 22.4 ft-lb/in²

@Temperature -22.0 °F
 ISO 180/1U
48.0 kJ/m²

@Temperature 23.0 °C
 22.8 ft-lb/in²

@Temperature 73.4 °F
 ISO 180/1U
Charpy Impact Unnotched 4.80 J/cm²

@Temperature -30.0 °C
 22.8 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eU
5.60 J/cm²

@Temperature 23.0 °C
 26.6 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eU
Charpy Impact, Notched 0.700 J/cm²

@Temperature -30.0 °C
 3.33 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eA
0.800 J/cm²

@Temperature 23.0 °C
 3.81 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eA
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 242 °C
468 °F
80*10*4 s=60mm; ISO 75-1 a
Vicat Softening Point 248 °C
478 °F
B/120; ISO 306
Flammability, UL94 V-0

@Thickness 0.750 mm
 V-0

@Thickness 0.0295 in
 IEC 60695-11-10
V-0

@Thickness 3.00 mm
 V-0

@Thickness 0.118 in
 IEC 60695-11-10
Glow Wire Test 725 °C

@Thickness 0.750 mm
 1340 °F

@Thickness 0.0295 in
 GWIT; IEC 60695-2-13
750 °C

@Thickness 3.00 mm
 1380 °F

@Thickness 0.118 in
 GWIT; IEC 60695-2-13
960 °C

@Thickness 0.750 mm
 1760 °F

@Thickness 0.0295 in
 GWFI; IEC 60695-2-12
960 °C

@Thickness 3.00 mm
 1760 °F

@Thickness 0.118 in
 GWFI; IEC 60695-2-12
Electrical Properties Metric English Comments
Comparative Tracking Index >= 600 V
>= 600 V
IEC 60112
Processing Properties Metric English Comments
Melt Temperature 280 - 295 °C
536 - 563 °F
Mold Temperature 70.0 - 90.0 °C
158 - 194 °F
Drying Temperature 80.0 °C

@Time 7200 - 21600 sec
 176 °F

@Time 2.00 - 6.00 hour
Moisture Content <= 0.20 %
<= 0.20 %