SABIC Innovative Plastics Valox® 3706 PBT+PC

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Valox®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Valox® 3706 PBT+PC.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Impact modified PBT+PC resin. Outdoor enclosure. Not available in all colors.
Physical Properties Metric English Comments
Specific Gravity 1.30 g/cc
1.30 g/cc
ASTM D792
Linear Mold Shrinkage, Flow 0.012 - 0.014 cm/cm

@Thickness 3.20 mm
 0.012 - 0.014 in/in

@Thickness 0.126 in
 SABIC Method
Linear Mold Shrinkage, Transverse 0.012 - 0.014 cm/cm

@Thickness 3.20 mm
 0.012 - 0.014 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 19 g/10 min

@Load 5.00 kg,
Temperature 266 °C
 19 g/10 min

@Load 11.0 lb,
Temperature 511 °F
 ASTM D1238
Melt Index of Compound 17 g/10 min

@Load 5.00 kg,
Temperature 265 °C
 17 g/10 min

@Load 11.0 lb,
Temperature 509 °F
 MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 39.0 MPa
5660 psi
Type I, 50 mm/min; ASTM D638
Tensile Strength, Yield 48.0 MPa
6960 psi
Type I, 50 mm/min; ASTM D638
Elongation at Break 50 %
50 %
Type I, 50 mm/min; ASTM D638
Elongation at Yield 6.0 %
6.0 %
Type I, 50 mm/min; ASTM D638
Tensile Modulus 1.96 GPa
284 ksi
50 mm/min; ASTM D638
Flexural Yield Strength 78.0 MPa
11300 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 1.99 GPa
289 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 6.67 J/cm
12.5 ft-lb/in
ASTM D256
Dart Drop, Total Energy 49.0 J

@Temperature 23.0 °C
 36.1 ft-lb

@Temperature 73.4 °F
 ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 79.2 µm/m-°C

@Temperature -40.0 - 40.0 °C
 44.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
CTE, linear, Transverse to Flow 86.4 µm/m-°C

@Temperature -40.0 - 40.0 °C
 48.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 126 °C

@Thickness 3.20 mm
 259 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 85.0 °C

@Thickness 3.20 mm
 185 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Vicat Softening Point 135 °C
275 °F
Rate B/50; ASTM D1525
UL RTI, Electrical 100 °C
212 °F
UL 746B
UL RTI, Mechanical with Impact 85.0 °C
185 °F
UL 746B
UL RTI, Mechanical without Impact 100 °C
212 °F
UL 746B
Flammability, UL94 V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in
 UL 94
5VA

@Thickness 2.49 mm
 5VA

@Thickness 0.0980 in
 UL 94
Electrical Properties Metric English Comments
Arc Resistance 60 - 120 sec
60 - 120 sec
Tungsten; ASTM D495
Comparative Tracking Index 250 - 400 V
250 - 400 V
UL 746A
Hot Wire Ignition, HWI 30 - 60 sec
30 - 60 sec
UL 746A
High Amp Arc Ignition, HAI >= 120 arcs
>= 120 arcs
UL 746A
High Voltage Arc-Tracking Rate, HVTR >= 150 mm/min
>= 5.91 in/min
UL 746A