Polymer Property : Flexural Modulus = 1.99 GPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Modulus	1.99 GPa	289 ksi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics Lexan® EXL6414 PC PC-Siloxane copolymer with excellent processability. Impact modified, medium flow, extreme low temp. ductility.
Flexural Modulus	1.99 GPa	289 ksi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics Lexan® EXL6414 PC (Asia Pacific) PC-Siloxane copolymer with excellent processability. Impact modified, medium flow, extreme low temp. ductility.
Flexural Modulus	1.99 GPa	289 ksi	1.3 mm/min, 50 mm span; ASTM D 790
SABIC Innovative Plastics Lexan® EXL6414 PC (Europe-Africa-Middle East) PC-Siloxane copolymer with excellent processability. Impact modified, medium flow, extreme low temp. ductility.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Flexural Modulus	1.99 GPa	289 ksi	ASTM D790
PolyOne Geon™ HTX Ultra LA426G Black 2880 Polyvinyl Chloride Alloy (PVC Alloy) Higher gloss version of Geon HTX Ultra LA426Recommend drying material for a minimum of 2 hours at 160 degrees Farenheit. Physical properties measured on LA426G Black 2880.Information provided by Pol..
Flexural Modulus	1.99 GPa	289 ksi	ASTM D790
LG Chemical TR-557I Transparent ABS, High Impact, Ice Colored Pellets LG transparent ABS has excellent transparency, impact strength, stiffness, and processability. Since its properties are well balanced, it can be applied widely to a variety of electric and electron..
Flexural Modulus	1.99 GPa	289 ksi	2.6 mm/min, 100 mm span; ASTM D790
SABIC Innovative Plastics NORYL STN15HF PPE+PS Automotive interiors. Improved flow characteristics/overall processing economy. 240F DTUL. High impact/good property retention after heat ageing.
Flexural Modulus	1.99 GPa	289 ksi	2.6 mm/min, 100 mm span; ASTM D790
SABIC Innovative Plastics NORYL STN15HF PPE+PS (Asia Pacific) Automotive interiors. Improved flow characteristics/overall processing economy. 240F DTUL. High impact/good property retention after heat ageing.
Flexural Modulus	1.99 GPa	289 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP LUBRICOMP KP002 Acetal Copoly (Asia Pacific) LNP* Lubricomp* KP002 is a compound based on Acetal Copolymer resin containing PTFE, Silicone. Added features of this material include: Internally Lubricated.
Flexural Modulus	1.99 GPa	289 ksi	2.6 mm/min, 100 mm span; ASTM D790
SABIC Innovative Plastics LNP LUBRICOMP Noryl_NWR5810 PPE+HIPS (Europe-Africa-Middle East) LNP* Lubricomp* Noryl_NWR5810 compound is a 10% PTFE filled PPE+PS. High flow and good impact. Applications requiring wear resistance/lubricity. Electronics.
Flexural Modulus	1.99 GPa	289 ksi	2.6 mm/min, 100 mm span; ASTM D790
SABIC Innovative Plastics LNP LUBRICOMP Noryl_NWR5810 PPE+PS LNP* Lubricomp* Noryl_NWR5810 compound is a 10% PTFE filled PPE+PS. High flow and good impact. Applications requiring wear resistance/lubricity. Electronics.
Flexural Modulus	1.99 GPa	289 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP LUBRICOMP QP004 PA 6/10 LNP* LUBRICOMP* QP004 is a compound based on Nylon 6/10 containing 20% PTFE/Silicone. Added feature of this grade is: Wear Resistant.
Flexural Modulus	1.99 GPa	289 ksi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics ValoxÂ® 3706 PBT+PC Impact modified PBT+PC resin. Outdoor enclosure. Not available in all colors.
Flexural Modulus	1.99 GPa	289 ksi	ASTM D790
Spartech Millennium IV Glass Filled ABS Structural Sheet Description: Structural SheetInformation provided by Spartech.
Flexural Modulus	1.99 GPa	289 ksi	Compression Molded; ASTM D790
Styron STYRONâ„¢ 6500 Ignition Resistant Polystyrene Resin Overview: STYRONâ„¢ 6500 is an ignition-resistant polystyrene resin with excellent balance of strength, heat resistance and flow properties that are tailor-made for consumer electronics applicati..
Flexural Modulus	1.99 GPa	289 ksi	2.6 mm/min, 100 mm span; ASTM D790
SABIC Innovative Plastics NORYL EZ250 PPE+PS Automotive wheel covers. Offers superior processability/flow and better chemical resistance when exposed to many automotive fluids over PX0844.
Flexural Modulus	1.99 GPa	289 ksi	1% Secant Modulus; ASTM D790
DSM Biomedical Elasthane™ 75D Thermoplastic Polyether Polyurethane (TPU) A high tensile strength, aromatic biomedical polymer with an exceptional combination of mechanical properties plus biological compatibility Elasthane™ TPU exhibits outstanding hydrolytic stabilit..
Flexural Modulus	1.99 GPa	288 ksi	ASTM D790
Entec Hyrene® PS-HI 8/2 High Impact Polystyrene Available in North America Features: High Impact ResistanceRoHS Compliant Form: Pellets Information provided by Entec