SABIC Innovative Plastics NORYL NH7010 PPE+PS (Asia Pacific)

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Noryl
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics NORYL NH7010 PPE+PS (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
High heat, Non halogenated flame retardant Noryl product
Physical Properties Metric English Comments
Specific Gravity 1.09 g/cc
1.09 g/cc
ASTM D792
Density 1.09 g/cc
0.0394 lb/in³
ISO 1183
Moisture Absorption 0.0500 %
0.0500 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.25 %
0.25 %
ISO 62
Linear Mold Shrinkage, Flow 0.0050 - 0.0080 cm/cm

@Thickness 3.20 mm
 0.0050 - 0.0080 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 10.1 g/10 min

@Load 5.00 kg,
Temperature 300 °C
 10.1 g/10 min

@Load 11.0 lb,
Temperature 572 °F
 ASTM D1238
Melt Index of Compound 10 g/10 min

@Load 5.00 kg,
Temperature 300 °C
 10 g/10 min

@Load 11.0 lb,
Temperature 572 °F
 MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 49.0 MPa
7110 psi
Type I, 50 mm/min; ASTM D638
63.0 MPa
9140 psi
50 mm/min; ISO 527
Tensile Strength, Yield 68.0 MPa
9860 psi
Type I, 50 mm/min; ASTM D638
69.0 MPa
10000 psi
50 mm/min; ISO 527
Elongation at Break 8.4 %
8.4 %
50 mm/min; ISO 527
41 %
41 %
Type I, 50 mm/min; ASTM D638
Elongation at Yield 4.9 %
4.9 %
50 mm/min; ISO 527
5.2 %
5.2 %
Type I, 50 mm/min; ASTM D638
Tensile Modulus 2.25 GPa
326 ksi
5 mm/min; ASTM D638
2.50 GPa
363 ksi
1 mm/min; ISO 527
Flexural Yield Strength 102 MPa
14800 psi
1.3 mm/min, 50 mm span; ASTM D790
109 MPa
15800 psi
2 mm/min; ISO 178
Flexural Modulus 2.47 GPa
358 ksi
1.3 mm/min, 50 mm span; ASTM D790
2.52 GPa
365 ksi
2 mm/min; ISO 178
Izod Impact, Notched 2.23 J/cm
4.18 ft-lb/in
ASTM D256
0.890 J/cm

@Temperature -30.0 °C
 1.67 ft-lb/in

@Temperature -22.0 °F
 ASTM D256
Izod Impact, Notched (ISO) 20.0 kJ/m²
9.52 ft-lb/in²
80*10*4; ISO 180/1A
8.00 kJ/m²

@Temperature -30.0 °C
 3.81 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1A
Charpy Impact, Notched 2.10 J/cm²
9.99 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 38.0 J

@Temperature 23.0 °C
 28.0 ft-lb

@Temperature 73.4 °F
 ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 81.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
 45.3 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
81.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
 45.3 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 81.5 µm/m-°C

@Temperature -40.0 - 40.0 °C
 45.3 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
81.5 µm/m-°C

@Temperature -40.0 - 40.0 °C
 45.3 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 139 °C
282 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
139 °C

@Thickness 3.20 mm
 282 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Vicat Softening Point 160 °C
320 °F
Rate B/50; ASTM D1525
161 °C
322 °F
Rate B/50; ISO 306
162 °C
324 °F
Rate B/120; ISO 306
UL RTI, Electrical 105 °C
221 °F
UL 746B
UL RTI, Mechanical with Impact 105 °C
221 °F
UL 746B
UL RTI, Mechanical without Impact 105 °C
221 °F
UL 746B
Flammability, UL94 V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in
 UL 94 by SABIC-IP
5VA

@Thickness 2.00 mm
 5VA

@Thickness 0.0787 in
 UL 94 by SABIC-IP
Electrical Properties Metric English Comments
Arc Resistance 60 - 120 sec
60 - 120 sec
Tungsten; ASTM D495
Comparative Tracking Index 175 - 250 V
175 - 250 V
UL 746A
Hot Wire Ignition, HWI >= 120 sec
>= 120 sec
UL 746A
High Voltage Arc-Tracking Rate, HVTR >= 150 mm/min
>= 5.91 in/min
UL 746A