Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 63.0 MPa | 9140 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® HFD1262 PC Copolymer (Asia Pacific) 19 MFR LEXAN High Flow Ductile Copolymerwith 400 nm cut off, available in transparent colors only |
|||
Tensile Strength at Break | 63.0 MPa | 9140 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® LUX2114G PC (Europe-Africa-Middle East) Lexan LUX2114G (EXRL0943) is a diffusive, mid viscosity, uv stabilized, flame retardant polycarbonate with improved light transmission and providing good colorstability under heat exposure. Develope.. |
|||
Tensile Strength at Break | 63.0 MPa | 9140 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® ML6412 PC Copolymer ML6412 is an impact modified PC resin with non-brominated, non-chlorinated flame retardant system. |
|||
Tensile Strength at Break | 63.0 MPa | 9140 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® ML6412 PC Copolymer (Asia Pacific) ML6412 is an impact modified PC resin with non-brominated, non-chlorinated flame retardant system. |
|||
Tensile Strength at Break | 63.0 MPa | 9140 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® ML3041 PC (Europe-Africa-Middle East) LEXAN ML3041 has been developed for the injection moulding of thin-wall, complex parts that require high mechanical properties and impact resistance.This data was supplied by SABIC-IP for the Europe.. |
|||
Tensile Strength at Break | 63.0 MPa | 9140 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® SLX2531T PC Copolymer Transparent weatherable PC copolymer for blowmolding/extrusion. |
|||
Tensile Strength at Break | 63.0 MPa | 9140 psi | ASTM D638 |
Kotec Carbotex K-20T30 Polycarbonate, General Purpose Features: Super high flow, TransparentApplications: OA equipment, Communications, Precision parts, Machineries, Safety products, E & E parts, Household applications, Leisure articlesInformation prov.. |
|||
Tensile Strength at Break | 63.0 MPa | 9140 psi | ASTM D638 |
Kotec Carbotex K-20UV Polycarbonate, General Purpose, UV Stability Grade Features: UV Stability, High flow, TransparentApplications: OA equipment, Communications, Precision parts, Machineries, Lighting Covers, Safety products, E & E parts, Household applications, Leisure.. |
|||
Tensile Strength at Break | 63.0 MPa | 9140 psi | ASTM D638 |
Kotec Carbotex K-20UVR30 Polycarbonate, General Purpose, UV Stability + Mold Release Grade Features: UV stability, Mold release Super high flow, TransparentApplications: OA equipment, Communications, Precision parts, Machineries, Lighting covers, Safety products, E & E parts, Household ap.. |
|||
Tensile Strength at Break | 63.0 MPa | 9140 psi | ASTM D638 |
Kotec Carbotex K-30UV Polycarbonate, General Purpose, UV Stability Grade Features: UV stability, Medium viscosity, TransparentApplications: OA equipment, Communications, Precision parts, Machineries, Lighting fixtures, Safety products, E & E parts, Household applications.. |
|||
Tensile Strength at Break | 63.0 MPa | 9140 psi | ASTM D638 |
Kotec Carbotex K-40UV Polycarbonate, General Purpose, UV Stability Grade Features: UV stability, Medium viscosity, TransparentApplications: OA equipment, Communications, Precision parts, Machineries, Lighting fixtures, Safety products, E & E parts, Household applications.. |
|||
Tensile Strength at Break | 63.0 MPa | 9140 psi | ASTM D638 |
Kotec Carbotex K-50 Polycarbonate, General Purpose Features: Standard, Medium viscosity, TransparentApplications: OA equipment, Communications, Precision parts, Machineries, Lighting fixtures, Safety products, E & E parts, Household applications, Le.. |
|||
Tensile Strength at Break | 63.0 MPa | 9140 psi | ASTM D638 |
Kotec Carbotex K-50UV Polycarbonate, General Purpose, UV Stability Grade Features: UV stability, Medium viscosity, TransparentApplications: OA equipment, Communications, Precision parts, Machineries, Lighting fixtures, Safety products, E & E parts, Household applications.. |
|||
Tensile Strength at Break | 63.0 MPa | 9140 psi | ASTM D638 |
Kotec Carbotex K-50UVR Polycarbonate, General Purpose, UV Stability + Mold Release Grade Features: UV stability, Mold release, Medium viscosityApplications: OA equipment, Communications, Precision parts, Machineries, Lighting fixtures, Safety products, E & E parts, Household application.. |
|||
Tensile Strength at Break | 63.0 MPa | 9140 psi | ASTM D638 |
Kotec Carbotex K-75E Polycarbonate, Extrusion Grade Features: Extrusion, High viscosity, Natural transparentApplications: Sheets FilmsInformation provided by Kotec Corporation |
|||
Tensile Strength at Break | 63.0 MPa | 9140 psi | ASTM D638 |
Kotec Carbotex KV-30FD Polycarbonate, Food Grade Features: Food contact, Medium viscosity, Mold release, TransparentApplications: Household appliance, Kitchenware, Food packaging/containersInformation provided by Kotec Corporation |
|||
Tensile Strength at Break | 63.0 MPa | 9140 psi | ASTM D638 |
Kotec Carbotex KV-40FD Polycarbonate, Food Grade Features: Food contact, Medium viscosity, Mold release, TransparentApplications: Household appliance, Kitchenware, Food packaging/containersInformation provided by Kotec Corporation |
|||
Tensile Strength at Break | 63.0 MPa | 9140 psi | ASTM D 638 |
SABIC Innovative Plastics LNP Lubricomp DX99854 PC LNP LUBRICOMP* DX99854 is a compound based on Polycarbonate resin containing Proprietary Filler(s). Added features of this material include: Internally Lubricated.This data was supplied by SABIC-IP.. |
|||
Tensile Strength at Break | 63.0 MPa | 9140 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP IAL12 PA6.12 LNP* LUBRICOMP* IAL12 is a compound based on Nylon 6/12 resin containing 5% PTFE, 10% Aramid Fiber. Added features of this material include: Internally Lubricated. |
|||
Tensile Strength at Break | 63.0 MPa | 9140 psi | ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP RL004S PA 66 LNP LUBRICOMP* RL004S is a compound based on Nylon 66 resin containing 20% PTFE. Added features of this material include: Heat Stabilized, Wear Resistant. |
|||
Tensile Strength at Break | 63.0 MPa | 9140 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP STAT-KON Lexan_JK2500 PC+ABS LNP* Stat-kon* Lexan_JK2500 compound is a 20% carbon-fiber reinforced, nonhalogenated red phosporous-free, high-flow FR PC+ABS for EMI/RFI shielding. SE of 21 dB at 1.5 mm. |
|||
Tensile Strength at Break | 63.0 MPa | 9140 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics XYLEX X7509HP PC+POLYESTER PC+Polyester alloy. Houseware applications. USA/Europe Food contact. this grade will no longer be supported with biocompatibility information and should not be used for medical applications which r.. |
|||
Tensile Strength at Break | 63.0 MPa | 9140 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics XYLEX X7509HP PC+POLYESTER (Europe-Africa-Middle East) PC+Polyester alloy. Houseware applications. USA/Europe Food contact. this grade will no longer be supported with biocompatibility information and should not be used for medical applications which r.. |
|||
Tensile Strength at Break | 63.0 MPa | 9140 psi | Type I, 50 mm/min; ASTM D 638 |
SABIC Innovative Plastics Xylex FXY391DF PC+POLYESTER (Asia Pacific) PC+Polyester alloy in Diffusion Visual fx. This grade is compliant with US FDA/European food contact regulations. Color package may influence performance.This data was supplied by SABIC-IP for the A.. |
|||
Tensile Strength at Break | >= 63.0 MPa | >= 9140 psi | ASTM D638 |
UBE UBESTA® 3030UFX1 Rigid Industrial Grade Nylon 12 Description: UBE UBESTA® Industrial grade Nylon 12Comments: UV resistance, heat resistanceInformation provided by UBE. |
|||
Tensile Strength at Break | 63.0 MPa | 9140 psi | ISO 527-1/-2 |
Covestro Desmopan® DP 8715 Polyurethane + ABS injection molding grademodified with ABSgood low-temperature flexibilitygood wear resistanceApplicationSki boot shellsAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and of.. |
|||
Tensile Strength at Break | 63.0 MPa | 9140 psi | 5 mm/min; ISO 527 |
Eurostar Starflam PK0069 PA6, Mineral Fiber Filled, Flame Retardant, Injection Molded Starflam PK0069 is a Free Flame Retardant Mineral Filled Polyamide 6 Injection Molding Resin (also known as Starflam PA6 30E6 Z88)Information provided by Eurostar. |
|||
Tensile Strength at Break | 63.0 MPa | 9140 psi | ASTM D638 |
Aclo Accutech ABS ABS833G10L Glass Reinforced |
|||
Tensile Strength at Break | 63.0 MPa | 9140 psi | ASTM D638 |
Aclo Accutech Polypropylene Homopolymer HP0336G25M5CL Glass/Mineral Reinforced Coupled |
|||
Tensile Strength at Break | 63.0 MPa | 9140 psi | 50%RH; ISO 527-1/-2 |
DuPont Performance Polymers Minlon® 11C40 NC010 Nylon 66
(Unverified Data**) 40% Mineral Reinforced Polyamide 66 Minlon 11C40 NC010 is a 40% mineral reinforced heat stabilized polyamide 66 resin for injection molding.Information provided by DuPont Performance Polymers |