SABIC Innovative Plastics LNP THERMOCOMP RF004H PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP RF004H PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* RF004H is a compound based on Nylon 66 containing 20% Glass Fiber. Added feature of this grade is: Healthcare.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.30 g/cc | 1.30 g/cc | ASTM D792 |
| Density | 1.29 g/cc | 0.0466 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.890 % | 0.890 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0060 cm/cm @Time 86400 sec |
0.0040 - 0.0060 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 156 MPa | 22600 psi | Type I, 5 mm/min; ASTM D638 |
| 159 MPa | 23100 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 3.6 % | 3.6 % | Type I, 5 mm/min; ASTM D638 |
| 3.7 % | 3.7 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 7.17 GPa | 1040 ksi | 5 mm/min; ASTM D638 |
| 7.30 GPa | 1060 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 230 MPa | 33400 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 241 MPa | 35000 psi | ISO 178 | |
| Flexural Modulus | 5.86 GPa | 850 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 7.00 GPa | 1020 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 1.01 J/cm | 1.89 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 8.33 J/cm | 15.6 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 56.0 kJ/m² | 26.6 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 11.0 J | 8.11 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 37.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
21.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 38.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
21.6 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| 79.4 µm/m-°C @Temperature 23.0 - 60.0 °C |
44.1 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 79.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
44.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 260 °C @Thickness 3.20 mm |
500 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 221 °C | 430 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 247 °C @Thickness 3.20 mm |
477 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- LG Chemical Lutex 810 SBR Latex
- Lord Adhesives 406 Flexible, High Impact and Peel Resistance, Medium Working Time Acrylic Adhesive
- Kuraray SEPTON® PM2 Polypropylene Modified Plastic
- TSE Industries Millathane® E34 Millable Polyether Polyurethane Rubber with 0.25 PHR Zinc Stearate
- DuPont Teijin Films Mylar® 800C Polyester Packaging Film, 75 Gauge
- Total Lacqrene® 1160(AS) Crystal Polystyrene (discontinued **)
- A. Schulman POLYBATCH™ Green 300 Concentrate Based In Polyethylene
Copyright © lookpolymers.com All Rights Reserved