- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 477 °F
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 477 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 247 °C @Thickness 3.20 mm |
477 °F @Thickness 0.126 in |
ASTM D648 |
| Ovation Polymers Opnyl OP66GF43 Nylon 66, As Conditioned Nylon 66-Glass reinforced(43%), high tensile strength, stiffness and HDT.Information provided by Ovation Polymers |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 247 °C | 477 °F | ASTM D648 |
| Polymer Resources NY66-G33 Nylon 66, 33% Glass Reinforced Nylon 66, 33% Glass Reinforced, LubricatedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon grades are test.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 247 °C | 477 °F | ASTM D648 |
| Polymer Resources NY66-G33-[color]H Nylon, 33% Glass Reinforced, Heat Stabilized (DAM) Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon grades are tested dry as molded (DAM).Information provide.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 247 °C | 477 °F | ASTM D648 |
| Plenco 50125 PET, Pellet, Injection Molded, White
(discontinued **) PLENCO 50125 is an engineering grade glass reinforced UL flame rated polyethylene terephthalate resin designed for excellent dimensional stability. It is UL listed and available in white only.Inform.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 247 °C | 477 °F | ASTM D648 |
| Polymer Resources NY66-G33-[color]-H Nylon 66, 33% Glass Reinforced, Heat Stabilized Nylon 66, 33% Glass Reinforced, Heat Stabilized, LubricatedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylo.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 247 °C | 477 °F | ASTM D648 |
| Kolon KOPA® KN333C22 CF Reinforced Nylon 66 Carbon 22%, high strengthApplications Cylinder piston partsInformation provided by API-Kolon. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 247 °C | 477 °F | ASTM D648 |
| Kolon KOPA® KN333G30BL G/F Reinforced Nylon 66 G/F 30% reinforcedApplications Engine coversInformation provided by API-Kolon. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 247 °C | 477 °F | ASTM D648 |
| Kolon KOPA® KN333G30HS G/F Reinforced Nylon 66 High thermal resistant, high strength, dimensionally stableApplications Transmission gear supportersInformation provided by API-Kolon. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 247 °C | 477 °F | DIN 53461; ASTM D648 |
| Kolon KOPA® KN333G33BL G/F Reinforced Nylon 66 KOPA® is a thermoplastic resin with excellent mechanical, thermal and electrical properties and is widely used in the automobile, electrical and industrial parts.High tensile strength, outstandin.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 247 °C | 477 °F | DIN 53461; ASTM D648 |
| Kolon KOPA® KN333G33CR G/F Reinforced Nylon 66 KOPA® is a thermoplastic resin with excellent mechanical, thermal and electrical properties and is widely used in the automobile, electrical and industrial parts.High tensile strength, outstandin.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 247 °C | 477 °F | ASTM D648 |
| Kolon KOPA® KN333G35CRBK G/F Reinforced Nylon 66 EG-resistant, high strength, dimensionally stableApplications Coolant temperature control partsInformation provided by API-Kolon. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 247 °C | 477 °F | ISO 75/Af |
| Solvay TECHNYL® A 218HP V35 PA66, 35% glass fiber, DRY Description: TECHNYL® A 218HP V35 is a polyamide 6.6, reinforced with 35% of glass fiber, heat stabilized, for injection molding. This product is available in black color.Benefits: The product of.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 247 °C | 477 °F | ISO 75/Af |
| Solvay TECHNYL® A 218W V33 Natural T PA66, 33% glass fiber, DRY Description: TECHNYL® A 218W V33 Nat T is a polyamide 66, reinforced with 33% of glass fiber, heat stabilized, for injection molding. This product is available in natural color.Benefits: The prod.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 247 °C | 477 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP LUBRICOMP RFL36L PA 66 LNP* LUBRICOMP* RFL36L is a compound based on Nylon 66 resin containing 30% Glass Fiber, 15% PTFE. Added features of this material include: Wear Resistant, Low Extractible. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 247 °C | 477 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP LUBRICOMP RFL36L PA 66 (Asia Pacific) LNP* Lubricomp* RFL36L is a compound based on Nylon 66 resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated, Low Extractible. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 247 °C | 477 °F | Unannealed; ISO 75-2/A |
| Solvay Specialty Polymers Kalix® 5950 HFFR Polyamide, High Performance (HPPA), 50% Glass Fiber Kalix® 5950 HFFR is a halogen-free, flame retardant (UL-94 V0 at 0.4 mm), highly reinforced polyamide material specifically formulated for high strength and stiffness applications where good impa.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 247 °C @Thickness 3.20 mm |
477 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP STAT-KON OEL32 PPS - Linear LNP* STAT-KON* OCL32 is a compound based on PPS - Linear resin containing 10% Carbon Fiber, 15% PTFE. Added features of this grade include: Electrically Conductive, Wear Resistant. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 247 °C @Thickness 3.20 mm |
477 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP STAT-KON RFD03 PA 66 LNP* STAT-KON* RFD03 is a compound based on Nylon 66 containing 15% Glass Fiber. Added feature of this material is: Electrically Conductive. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 247 °C @Thickness 3.20 mm |
477 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOCOMP RF004H PA 66 LNP* THERMOCOMP* RF004H is a compound based on Nylon 66 containing 20% Glass Fiber. Added feature of this grade is: Healthcare. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 247 °C @Thickness 3.20 mm |
477 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOCOMP RF006S PA 66 (Asia Pacific) LNP* Thermocomp* RF006S is a compound based on Nylon 66 resin containing Glass Fiber. Added features of this material include: Heat Stabilized. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 247 °C | 477 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP Thermocomp RFB33 PA6.6 (Europe-Africa-Middle East) LNP*THERMOCOMP* RFB33 is a compound based on PA66 resin containing Glass Bead, Glass Fiber.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 247 °C | 477 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP THERMOTUF RF008IS PA 66 (Asia Pacific) LNP* Thermotuf* RF008IS is a compound based on Nylon 66 resin containing Glass Fiber. Added features of this material include: High Impact. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 247 °C @Thickness 3.20 mm |
477 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP STAT-KON RE0039 PA 66 LNP STAT-KON* RE0039 is a compound based on Nylon 66 resin containing 15% Carbon Fiber. Added features of this material include: Electrically Conductive, Flame Retardant. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 247 °C @Thickness 3.20 mm |
477 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP VERTON RV008ES PA 66 (Asia Pacific) LNP* Verton* RV008ES is a compound based on Nylon 66 resin containing Long Glass Fiber. Added features of this material include: Easy Molding, Heat Stabilized. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 247 °C @Thickness 3.20 mm |
477 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP VERTON RX06424 PA 66 (Asia Pacific) LNP VERTON* RX06424 is a compound based on Nylon 66 resin containing Long Glass. Added features of this material include: Easy Molding. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 247 °C | 477 °F | ISO 75 |
| BASF Ultramid® 66 H2 G/35-V0KB NAT 0046 35% Glass Filled PA66 (Dry) Description: Ultramid 66 H2 G/35-V0KB NAT0046 is a 35% glass reinforced, heat stabilized injection molding grade. It is a V-0 self-extinguishing grade, with phosphorous. It offers good flowability a.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 247 °C @Thickness 3.20 mm |
477 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP VERTON RV00CESS PA 66 LNP VERTON* RV00CESS is a compound based on Nylon 66 resin containing 60% Long Glass Fiber. Added features of this material include: Easy Molding, Heat Stabilized, Structural. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 247 °C @Thickness 3.20 mm |
477 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP VERTON RV00CESS PA 66 (Asia Pacific) LNP VERTON* RV00CESS is a compound based on Nylon 66 resin containing Long Glass. Added features of this material include: Easy Molding. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 247 °C | 477 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP VERTON RV00CEXS PA 66 LNP* VERTON* RV00CEXS is a compound based on Nylon 66 resin containing 60% Long Glass Fiber. Added features of this grade include: Easy Molding, Structural. |
|||