Polymer Property : Tensile Strength at Break = 23100 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength at Break 159 MPa
23100 psi
5.1 mm/min; ASTM D638
PolyOne LubriOne™ SF-30CF/15T Polyphenylene Sulfide (PPS)
LubriOne™ Lubricated and Wear-Resistant Compounds have been specifically formulated to be self-lubricating materials, offering low coefficient of friction and improved wear resistance properties. L..
Tensile Strength at Break 159 MPa
23100 psi
Conditioned; ISO 527-1/-2
Lanxess Durethan® DP AKV 50 HR H2.0 901510 Nylon 66, 50% Glass Fiber
PA 66, injection molding grade, 50% glass fibers, good heat-ageing resistance, and hydrolysis resistanceApplication Examples: coolant manifolds
Tensile Strength at Break 159 MPa
23100 psi
Conditioned; ISO 527-1/-2
Lanxess Durethan® TP 036-052 000000 Nylon 6, 60% Glass Fiber
PA 6, injection molding grade, 60% glass fibers, good flowability (Easy Flow), good heat-resistance
Tensile Strength at Break 159 MPa
23100 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP LX91475 PEEK
LNP* LUBRICOMP* LX91475 is a compound based on Polyetheretherketone resin containing proprietary fillers. Added features of this material include: Easy Molding, High Temperature Bearing Grade, Wear..
Tensile Strength at Break 159 MPa
23100 psi
ISO 527
SABIC Innovative Plastics LNP LUBRICOMP OCP34E PPS - Linear
LNP LUBRICOMP* OCP34E is a compound based on PPS - Linear resin containing 20% Carbon Fiber, 15% PTFE/Silicone. Added features of this material include: Easy Molding, Electrically Conductive, Wear ..
Tensile Strength at Break 159 MPa
23100 psi
ISO 527
SABIC Innovative Plastics LNP LUBRICOMP OCP34E PPS - Linear (Asia Pacific)
LNP LUBRICOMP* OCP34E is a compound based on PPS - Linear resin containing Silicone, Carbon Fiber, PTFE. Added features of this material include: Easy Molding.
Tensile Strength at Break 159 MPa
23100 psi
5 mm/min; ISO 527
SABIC Innovative Plastics LNP LUBRICOMP RFL36S PA 66 (Europe-Africa-Middle East)
LNP* Lubricomp* RFL36S is a compound based on Nylon 66 resin containing Glass Fiber, PTFE. Added features of this material include: Heat Stabilized.
Tensile Strength at Break 159 MPa
23100 psi
ASTM D638
SABIC Innovative Plastics LNP STAT-KON PFD06 PA 6
LNP* STAT-KON* PFD06 is a compound based on Nylon 6 resin containing 30% Glass Fiber. Added features of this material include: Electrically Conductive.
Tensile Strength at Break 159 MPa
23100 psi
ASTM D638
SABIC Innovative Plastics LNP STAT-KON PFD06 PA 6 (Asia Pacific)
LNP* Stat-kon* PFD06 is a compound based on Nylon 6 resin containing Glass Fiber, Carbon Powder. Added features of this material include: Electrically Conductive.
Tensile Strength at Break 159 MPa
23100 psi
5 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP OF008 PPS - Linear (Europe-Africa-Middle East)
LNP* Thermocomp* OF008 is a compound based on PPS - Linear resin containing Glass Fiber.
Tensile Strength at Break 159 MPa
23100 psi
ISO 527
SABIC Innovative Plastics LNP THERMOCOMP RF004 PA 66
LNP THERMOCOMP* RF004 is a compound based on Nylon 66 resin containing 20% Glass Fiber.
Tensile Strength at Break 159 MPa
23100 psi
5 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP RF004H PA 66
LNP* THERMOCOMP* RF004H is a compound based on Nylon 66 containing 20% Glass Fiber. Added feature of this grade is: Healthcare.
Tensile Strength at Break 159 MPa
23100 psi
ISO 527
SABIC Innovative Plastics LNP THERMOCOMP RF004XXD PA 66
LNP THERMOCOMP* RF004XXD is a compound based on Nylon 66 resin containing 20% Glass Fiber.
Tensile Strength at Break 159 MPa
23100 psi
5 mm/min; ISO 527
SABIC Innovative Plastics LNP Thermocomp RF006PS PA 66
LNP* Thermocomp* RF-1006 EP HS is based on Nylon 6/6 containing Glass Fiber. Characteristics of this grade include Exceptional Processing and Heat Stabilizer.This data was supplied by SABIC-IP for ..
Tensile Strength at Break 159 MPa
23100 psi
ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP RF006S PA 66
LNP* THERMOCOMP* RF006S is a compound based on Nylon 66 resin containing 30% Glass Fiber. Added features of this material include: Heat Stabilized.
Tensile Strength at Break 159 MPa
23100 psi
ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP RF006S PA 66 (Asia Pacific)
LNP* Thermocomp* RF006S is a compound based on Nylon 66 resin containing Glass Fiber. Added features of this material include: Heat Stabilized.
Tensile Strength at Break 159 MPa
23100 psi
5 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP LF006E PEEK (Europe-Africa-Middle East)
LNP* THERMOCOMP* LF006E is a compound based on Polyetheretherketone resin containing Glass Fiber. Added features include: Easy Molding.
Tensile Strength at Break 159 MPa
23100 psi
conditioned; ISO 527-1/-2
EMS-Grivory Grivory® TSG-60/4 W PA666-GF60
Product description: Grilon TSG-60/4 W is a high heat stabilized, normal viscosity PA66 + PA6 injection molding grade with 60% glass fibers, modified for parts with high thermal demands. Grilon TSG-..