Polymer Property : Tensile Strength at Break = 159 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength at Break 159 MPa
23100 psi
5.1 mm/min; ASTM D638
PolyOne LubriOne™ SF-30CF/15T Polyphenylene Sulfide (PPS)
LubriOne™ Lubricated and Wear-Resistant Compounds have been specifically formulated to be self-lubricating materials, offering low coefficient of friction and improved wear resistance properties. L..
Tensile Strength at Break 159 MPa
23000 psi
ASTM D638
Niche Polymer PA6GF33BK Nylon 6, 33% Glass Fiber Filled
Information provided by Niche Polymer
Tensile Strength at Break 159 MPa
23100 psi
Conditioned; ISO 527-1/-2
Lanxess Durethan® DP AKV 50 HR H2.0 901510 Nylon 66, 50% Glass Fiber
PA 66, injection molding grade, 50% glass fibers, good heat-ageing resistance, and hydrolysis resistanceApplication Examples: coolant manifolds
Tensile Strength at Break 159 MPa
23100 psi
ASTM D638
SABIC Innovative Plastics LNP STAT-KON PFD06 PA 6
LNP* STAT-KON* PFD06 is a compound based on Nylon 6 resin containing 30% Glass Fiber. Added features of this material include: Electrically Conductive.
Tensile Strength at Break 159 MPa
23100 psi
ASTM D638
SABIC Innovative Plastics LNP STAT-KON PFD06 PA 6 (Asia Pacific)
LNP* Stat-kon* PFD06 is a compound based on Nylon 6 resin containing Glass Fiber, Carbon Powder. Added features of this material include: Electrically Conductive.
Tensile Strength at Break 159 MPa
23100 psi
5 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP RF004H PA 66
LNP* THERMOCOMP* RF004H is a compound based on Nylon 66 containing 20% Glass Fiber. Added feature of this grade is: Healthcare.
Tensile Strength at Break 159 MPa
23100 psi
5 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP LF006E PEEK (Europe-Africa-Middle East)
LNP* THERMOCOMP* LF006E is a compound based on Polyetheretherketone resin containing Glass Fiber. Added features include: Easy Molding.
Tensile Strength at Break 159 MPa
23000 psi
ASTM D638
Plastics Group Polifil® 930L-33GF Glass Fiber-Reinforced Nylon 6 (DAM)
Polifil® GFN/MRN 6 reinforced series of compounds provide good heat and dimensional stability and offer extended or continuous stability under high temperatures. These have been found useful in ind..
Tensile Strength at Break 159 MPa
23000 psi
ASTM D638
A. Schulman SCHULADUR® A GF50 50% Glass Fiber Reinforced PBT
Information provided by A. Schulman.
Tensile Strength at Break 159 MPa
23000 psi
ASTM D638
Techmer Lehvoss Compounds Luvotech™ J-1305/40 NAT PPS  (discontinued **)
Techmer Lehvoss Compounds, a JV between Techmer ES and Lehmann&Voss&Co. has been terminated.