SABIC Innovative Plastics LNP THERMOCOMP NF004 PC+ABS
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Glass Fiber Filled , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP NF004 PC+ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* NF004 is a compound based on PC+ABS resin containing 20% Glass Fiber.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in³ | ASTM D792 |
| 1.30 g/cc | 0.0470 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.100 % | 0.100 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm @Time 86400 sec |
0.0040 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0041 cm/cm @Time 86400 sec |
0.0041 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0058 cm/cm @Time 86400 sec |
0.0058 in/in @Time 24.0 hour |
ISO 294 |
| 0.0060 cm/cm @Time 86400 sec |
0.0060 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 95.0 MPa | 13800 psi | ISO 527 |
| 97.0 MPa | 14100 psi | ASTM D638 | |
| Elongation at Break | 2.5 % | 2.5 % | ASTM D638 |
| 2.5 % | 2.5 % | ISO 527 | |
| Tensile Modulus | 6.48 GPa | 940 ksi | 1 mm/min; ISO 527 |
| 6.89 GPa | 999 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 137 MPa | 19900 psi | ASTM D790 |
| 143 MPa | 20700 psi | ISO 178 | |
| Flexural Modulus | 6.00 GPa | 870 ksi | ISO 178 |
| 6.20 GPa | 899 ksi | ASTM D790 | |
| Izod Impact, Notched | 1.17 J/cm | 2.19 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.98 J/cm | 11.2 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 11.0 kJ/m² | 5.23 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 37.0 kJ/m² | 17.6 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 18.0 J | 13.3 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 5.00 J | 3.69 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 77.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
42.8 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 77.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
43.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 32.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
17.8 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 32.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
18.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 140 °C | 284 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 138 °C @Thickness 3.20 mm |
280 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 134 °C | 273 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 135 °C @Thickness 3.20 mm |
275 °F @Thickness 0.126 in |
unannealed; ASTM D648 |