Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 137 MPa | 19900 psi | ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP DFL23 PC LNP* Lubricomp* DFL23 is a compound based on Polycarbonate resin containing 15% Glass Fiber and 10% PTFE. Added features include: Internally Lubricated. |
|||
Flexural Strength | 137 MPa | 19900 psi | ASTM D790 |
LG Chemical EG920 PMMA, General Purpose Grade for Extrusion General purpose grade with excellent stress cracking resistanceIntended mainly for exterior applicationsRecommended mainly for sheets, pipes, and profilesFeatures: Excellent transparency and eleganc.. |
|||
Flexural Strength | 137 MPa | 19900 psi | ASTM D790 |
LG Chemical IG840 PMMA, General Purpose Grade for Injection Molding General purpose grade with better flowability than IH 830 but slightly below in heat resistanceMechanical strength and surface hardnessFeatures: Excellent transparency and eleganceWeather resistance.. |
|||
Flexural Strength | 137 MPa | 19900 psi | ASTM D790 |
LG Chemical LUCON PO-5300H Electrically Conductive Thermoplastic LG Chemicals has formulated a diverse range of LUCON thermoplastic compounds containing conductive additives, such as carbon powder, (nickel coated) carbon fiber, or stainless steel fiber for solvin.. |
|||
Flexural Strength | 137 MPa @Thickness 3.20 mm |
19900 psi @Thickness 0.126 in |
ASTM D790 |
LG Chemical LUMILOY GP2200 Injection Molding Grade, General Purpose 20% Glass Reinforced PPE NSF Certified for KA02 and E2035. Noted for High Flow, High Impact Strength, and Hydrolytic Stability. Uses include electric/electronic parts and water pump Housing or impellers and other parts wi.. |
|||
Flexural Strength | 137 MPa | 19900 psi | ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP RA004 PA 66 LNP LUBRICOMP* RA004 is a compound based on Nylon 66 resin containing 20% Aramid. Added features of this material include: Wear Resistant. |
|||
Flexural Strength | 137 MPa | 19900 psi | ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP RA004 PA 66 (Asia Pacific) LNP LUBRICOMP* RA004 is a compound based on Nylon 66 resin containing Aramid. Added features of this material include: Internally Lubricated. |
|||
Flexural Strength | 137 MPa | 19900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Valox® 4521 PBT VALOX 4521 is a high flow, 20% glass reinforced flame retardant PBT injection moulding resin. Applications: electrical applications |
|||
Flexural Strength | 137 MPa | 19900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Valox® 815 PBT 15% GR PBT+ PET, excellent surface finish. Typical applications are hot air gun housing assemblies, industrial glue guns, appliance housings and handles. |
|||
Flexural Strength | 137 MPa | 19900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Valox® 855 PBT 15% GR PBTP, UL94 V-0 rated. Improved surface appearance. For external housings: steam irons, appliance housings and lighting parts. |
|||
Flexural Strength | 137 MPa | 19900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Valox® 855 PBT (Asia Pacific) 15% GR PBTP, UL94 V-0 rated. Improved surface appearance. For external housings: steam irons, appliance housings and lighting parts. |
|||
Flexural Strength | 137 MPa | 19900 psi | ASTM D 790 |
SABIC Innovative Plastics LNP Thermocomp 5C004 LNP* Thermocomp* 5C004 is a compound based on Polyvinylidene Fluoride resin containing Carbon Fiber. Added features of this material include: Electrically Conductive.This data was supplied by SABIC.. |
|||
Flexural Strength | 137 MPa | 19900 psi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP 5C004 FP-V (PVDF) LNP* THERMOCOMP* 5C004 is a compound based on Polyvinylidene Fluoride resin containing 20% Carbon Fiber. Added features of this material include: Electrically Conductive. |
|||
Flexural Strength | 137 MPa | 19900 psi | ISO 178 |
SABIC Innovative Plastics LNP Thermocomp DFZ42P PC LNP* Thermocomp* DFZ42P is a compound based on Polycarbonate resin containing Glass Fiber. Added features of this material include: Exceptional Processing.This data was supplied by SABIC-IP for the.. |
|||
Flexural Strength | 137 MPa | 19900 psi | 2.8 mm/min; ASTM D790 |
Samsung Cheil Industries Infino® CF-3200HF PC, Glass Filled High Impact Information provided by Samsung Cheil Industries. |
|||
Flexural Strength | 137 MPa | 19900 psi | 2.8 mm/min; ASTM D790 |
Samsung Cheil Industries Infino® LS-3302A PC, Glass Filled High Impact Information provided by Samsung Cheil Industries. |
|||
Flexural Strength | 137 MPa | 19900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Valox® 815 PBT (Asia Pacific) 15% GR PBTP, excellent surface finish. Typical applications are hot air gun housing assemblies, industrial glue guns, appliance housings and handles. |
|||
Flexural Strength | 137 MPa | 19900 psi | ASTM D 790 |
SABIC Innovative Plastics LNP Thermocomp 2C003 LNP* Thermocomp* 2C003 is a compound based on Ethylene Tetrafluoroethylene Copolymer resin containing Carbon Fiber. Added features of this material include: Electrically Conductive.This data was su.. |
|||
Flexural Strength | 137 MPa | 19900 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
SABIC Innovative Plastics LNP Thermocomp 2C003 LNP* Thermocomp* 2C003 is a compound based on Ethylene Tetrafluoroethylene Copolymer resin containing Carbon Fiber. Added features of this material include: Electrically Conductive.This data was su.. |
|||
Flexural Strength | 137 MPa | 19900 psi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP 2C003 ETFE LNP* THERMOCOMP* 2C003 is a compound based on ETFE resin containing 15% Carbon Fiber. Added features of this material include: Electrically Conductive. |
|||
Flexural Strength | 137 MPa | 19900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP 2C003 ETFE LNP* THERMOCOMP* 2C003 is a compound based on ETFE resin containing 15% Carbon Fiber. Added features of this material include: Electrically Conductive. |
|||
Flexural Strength | 137 MPa | 19900 psi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP NF004 PC+ABS LNP* THERMOCOMP* NF004 is a compound based on PC+ABS resin containing 20% Glass Fiber. |
|||
Flexural Strength | 137 MPa | 19900 psi | 2.8 mm/min; ASTM D790 |
Samsung Cheil Industries Infino® NH-8310 MPPE, Glass Filled FR Information provided by Samsung Cheil Industries. |
|||
Flexural Strength | 137 MPa | 19900 psi | 20 x 40 mm |
CeramTec 192/193 Titania 192/193 is an excellent material for textile and other structural applications, where superior surface finishes are required with high chemical resistance. 193 is identical except it is metallic gra.. |
|||
Flexural Strength | 137 MPa | 19900 psi | ASTM D790 |
A. Schulman SCHULAMID® 66 MF40 Mineral Filled Nylon 66 Information provided by A. Schulman. |
|||
Flexural Strength | 137 MPa | 19900 psi | ASTM D790 |
A. Schulman ComAlloy Hiloy® 130 Polypropylene, Glass/Mineral Reinforced, Chemically Coupled, UL Data provided by the manufacturer, ComAlloy International Company.40% Glass/Mineral Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
Flexural Strength | 137 MPa | 19900 psi | ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP DFL36G PC (Asia Pacific) LNP* Lubricomp* DFL36G is a compound based on Polycarbonate resin containing Glass Fiber, PTFE, Milled Glass. Added features of this material include: Internally Lubricated. |
|||
Flexural Strength | 137 MPa | 19900 psi | 2.8 mm/min; ASTM D790 |
Samsung Cheil Industries Infino® NH-3208GL PC, Glass Filled FR Information provided by Samsung Cheil Industries. |
|||
Flexural Strength | 137 MPa | 19900 psi | ASTM D790 |
LG Chemical IH830 PMMA, General Purpose Grade for Injection Molding Highest of all grades in heat resistanceMechanical strength and surface hardnessParticularly recommended for tail lamp, reflectors, and general lighting fixturesFeatures: Excellent transparency and .. |
|||
Flexural Strength | 137 MPa | 19900 psi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP GF004 PSU (Asia Pacific) LNP* Thermocomp* GF004 is a compound based on Polysulfone resin containing Glass Fiber. |