- Polymer Property : Flexural Strength = 19900 psi
Polymer Property : Flexural Strength = 19900 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Flexural Strength | 137 MPa | 19900 psi | ASTM D790 |
| SABIC Innovative Plastics LNP LUBRICOMP DFL36G PC LNP* Lubricomp* DFL36G is a compound based on Polycarbonate resin containing 30% Mixed Glass, 15% PTFE. Added features of this material include: Internally Lubricated. |
|||
| Flexural Strength | 137 MPa | 19900 psi | ASTM D790 |
| LG Chemical LUCON PO-5300H Electrically Conductive Thermoplastic LG Chemicals has formulated a diverse range of LUCON thermoplastic compounds containing conductive additives, such as carbon powder, (nickel coated) carbon fiber, or stainless steel fiber for solvin.. |
|||
| Flexural Strength | 137 MPa @Thickness 3.20 mm |
19900 psi @Thickness 0.126 in |
ASTM D790 |
| LG Chemical LUMILOY GP2200 Injection Molding Grade, General Purpose 20% Glass Reinforced PPE NSF Certified for KA02 and E2035. Noted for High Flow, High Impact Strength, and Hydrolytic Stability. Uses include electric/electronic parts and water pump Housing or impellers and other parts wi.. |
|||
| Flexural Strength | 137 MPa | 19900 psi | |
| Lehmann & Voss LUVOCOM® 1100-8326 Polyether sulfone, with carbon fiber, PTFE, lubricant modified Applications: Apparatus- and precision engineering, film- and photo industry, sporting- and leisure goods, medical- and electrical enineering, aircraft- and aerospace industry.Strong, stiff parts.Dy.. |
|||
| Flexural Strength | 137 MPa | 19900 psi | ASTM D790 |
| SABIC Innovative Plastics LNP LUBRICOMP DX00714H PC LNP LUBRICOMP* DX00714H is a compound based on Polycarbonate resin containing Proprietary Filler(s). Added features of this material include: Wear Resistant, Healthcare. |
|||
| Flexural Strength | 137 MPa | 19900 psi | ISO 178 |
| Solvay TECHNYL® A 50H1 PA66, DRY Description: Flame retardant polyamide 66, unreinforced, heat stabilized, for injection molding.Available in: Asia Pacific, Europe, Latin America and North AmericaProduct Applications: This phospho.. |
|||
| Flexural Strength | 137 MPa | 19900 psi | ASTM D790 |
| SABIC Innovative Plastics LNP LUBRICOMP RA004 PA 66 LNP LUBRICOMP* RA004 is a compound based on Nylon 66 resin containing 20% Aramid. Added features of this material include: Wear Resistant. |
|||
| Flexural Strength | 137 MPa | 19900 psi | ASTM D790 |
| SABIC Innovative Plastics LNP LUBRICOMP RA004 PA 66 (Asia Pacific) LNP LUBRICOMP* RA004 is a compound based on Nylon 66 resin containing Aramid. Added features of this material include: Internally Lubricated. |
|||
| Flexural Strength | 137 MPa | 19900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics Valox® 4521 PBT VALOX 4521 is a high flow, 20% glass reinforced flame retardant PBT injection moulding resin. Applications: electrical applications |
|||
| Flexural Strength | 137 MPa | 19900 psi | ISO 178 |
| SABIC Innovative Plastics LNP Stat-kon DEP32XXC PC LNP STAT-KON* DEP32XXC is a compound based on Polycarbonate resin containing Carbon Fiber, Silicone, PTFE. Added features of this material include: Electrically Conductive.This data was supplied by.. |
|||
| Flexural Strength | 137 MPa | 19900 psi | ISO 178 |
| SABIC Innovative Plastics LNP THERMOCOMP KF002 Acetal Copolymer LNP THERMOCOMP* KF002 is a compound based on Acetal Copolymer resin containing 10% Glass Fiber. |
|||
| Flexural Strength | 137 MPa | 19900 psi | 2.8 mm/min; ASTM D790 |
| Samsung Cheil Industries Infino® EM-8250G MPPE, 20% Glass Filled Information provided by Samsung Cheil Industries. |
|||
| Flexural Strength | 137 MPa | 19900 psi | 2.8 mm/min; ASTM D790 |
| Samsung Cheil Industries Infino® LS-3104G PC, 10% Glass Filled High Impact High-impact resistant PC/GF with 10% GF reinforcement for LCD BLFInformation provided by Samsung Cheil Industries. |
|||
| Flexural Strength | 137 MPa | 19900 psi | 2.8 mm/min; ASTM D790 |
| Samsung Cheil Industries Infino® LS-3104G PC, 10% Glass Filled High Impact High-impact resistant PC/GF with 10% GF reinforcement for LCD BLFInformation provided by Samsung Cheil Industries. |
|||
| Flexural Strength | 137 MPa | 19900 psi | ASTM D 790 |
| SABIC Innovative Plastics LNP Thermocomp RFZ71S PA 66 LNP* Thermocomp* RFZ71S is a compound based on Nylon 66 resin containing Glass Fiber, Milled Glass. Added features of this material include: Heat Stabilized.This data was supplied by SABIC-IP for t.. |
|||
| Flexural Strength | 137 MPa | 19900 psi | ASTM D 790 |
| SABIC Innovative Plastics LNP Thermocomp RFZ71S PA 66 (Asia Pacific) LNP* Thermocomp* RFZ71S is a compound based on Nylon 66 resin containing Glass Fiber, Milled Glass. Added features of this material include: Heat Stabilized.This data was supplied by SABIC-IP for t.. |
|||
| Flexural Strength | 137 MPa | 19900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics Valox® 815 PBT (Asia Pacific) 15% GR PBTP, excellent surface finish. Typical applications are hot air gun housing assemblies, industrial glue guns, appliance housings and handles. |
|||
| Flexural Strength | 137 MPa | 19900 psi | ASTM D 790 |
| SABIC Innovative Plastics LNP Thermocomp 2C003 LNP* Thermocomp* 2C003 is a compound based on Ethylene Tetrafluoroethylene Copolymer resin containing Carbon Fiber. Added features of this material include: Electrically Conductive.This data was su.. |
|||
| Flexural Strength | 137 MPa | 19900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics LNP THERMOCOMP 2C003 ETFE LNP* THERMOCOMP* 2C003 is a compound based on ETFE resin containing 15% Carbon Fiber. Added features of this material include: Electrically Conductive. |
|||
| Flexural Strength | 137 MPa | 19900 psi | 2.8 mm/min; ASTM D790 |
| Samsung Cheil Industries Infino® NH-8310 MPPE, Glass Filled FR Information provided by Samsung Cheil Industries. |
|||
| Flexural Strength | 137 MPa | 19900 psi | ASTM D790 |
| SABIC Innovative Plastics NORYL CN1134 PPE+PS (Asia Pacific) 20% filled FR high modulus PPE/PS blend |
|||
| Flexural Strength | 137 MPa | 19900 psi | ISO 178 |
| Polyplastics Duranex® CRN7830 Polybutylene Terephthalate (PBT), Lower noise, 30% GF filled DURANEX® is a crystalline thermoplastic based on polybutylene terephthalate (PBT) that can be readily strengthened, modified, or otherwise performance enhanced through the addition of glass fibers .. |
|||
| Flexural Strength | 137 MPa | 19900 psi | ASTM D790 |
| A. Schulman SCHULAMID® 66 MF40 Mineral Filled Nylon 66 Information provided by A. Schulman. |
|||
| Flexural Strength | 137 MPa | 19900 psi | ASTM D790 |
| A. Schulman SCHULAMID® 66 MF40 Mineral Filled Nylon 66 Information provided by A. Schulman. |
|||
| Flexural Strength | 137 MPa | 19900 psi | 20 x 40 mm |
| CeramTec 192/193 Titania 192/193 is an excellent material for textile and other structural applications, where superior surface finishes are required with high chemical resistance. 193 is identical except it is metallic gra.. |
|||
| Flexural Strength | 137 MPa | 19900 psi | ASTM D790 |
| A. Schulman ComAlloy Hiloy® 130 Polypropylene, Glass/Mineral Reinforced, Chemically Coupled, UL Data provided by the manufacturer, ComAlloy International Company.40% Glass/Mineral Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
| Flexural Strength | 137 MPa | 19900 psi | ISO 178 |
| Celanese Celstran® PP-GF20-0501 Black P11 PP, 20% Glass Reinforced Material code according to ISO 1043-1: PPInformation provided by Celanese |
|||
| Flexural Strength | 137 MPa | 19900 psi | ASTM D790 |
| A. Schulman SCHULAMID® 66 MF40 Mineral Filled Nylon 66 Information provided by A. Schulman. |
|||
| Flexural Strength | 137 MPa | 19900 psi | ASTM D790 |
| SABIC Innovative Plastics LNP LUBRICOMP DCP32 PC (Asia Pacific) LNP* Lubricomp* DCP32 is a compound based on Polycarbonate resin containing PTFE, Carbon Fiber, Silicone. Added features of this material include: Electrically Conductive, Internally Lubricated. |
|||
| Flexural Strength | 137 MPa | 19900 psi | 2.8 mm/min; ASTM D790 |
| Samsung Cheil Industries Infino® NH-3208GL PC, Glass Filled FR Information provided by Samsung Cheil Industries. |
|||