Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 6.00 GPa | 870 ksi | |
Plastcom SLOVAMID 66 T 40 FRO 3 PA66, 40% mineral filling, flame retardant FeaturesPA 66 with the content of 40% chemically modified mineral filling a with fire retardant. Used for holders of electric hand tools, for hobby tools, gears, covers of electric tools, flat produ.. |
|||
Flexural Modulus | 6.00 GPa @Temperature 23.0 °C |
870 ksi @Temperature 73.4 °F |
ISO 178 |
Polykemi AB POLYfill PPH GF15030 PD2 Polypropylene Homopolymer, Glass Fibre-Reinforced, Chemically Coupled Information provided by Polykemi AB |
|||
Flexural Modulus | 6.00 - 8.00 GPa | 870 - 1160 ksi | Injection and Compression; ISO 178 |
Raschig Group AMPLA® 7500 melamine-modified polyester Organically and inorganically filled melamine modified Polyester molding compound. Low post-shrinkage, very good electrical values, excellent heat resistance, very good sliding behavior and wear sta.. |
|||
Flexural Modulus | 6.00 - 9.00 GPa | 870 - 1310 ksi | Compression; ISO 178 |
Raschig Group DECAL® 666/8 Phenolic Glass-fiber reinforced phenolic molding compound with mineral fillers. High heat resistance, reduced mould shrinkage and post-shrinkage, good chemical resistance and mechanical properties. This prod.. |
|||
Flexural Modulus | 6.00 - 9.00 GPa | 870 - 1310 ksi | Compression; ISO 178 |
Raschig Group RALUPOL® 2100 UP Polyester Organically and inorganically filled polyester molding compound. Low post-shrinkage, very good electrical values, good mechanical strength. This product meets the allowed upper limits for heavy meta.. |
|||
Flexural Modulus | 6.00 GPa | 870 ksi | |
Lehmann & Voss LUVOCOM® 50-7289 Polycarbonate, with carbon fiber and PTFE Applications: Data processing machinery, precision engineering, film and photo industry, sporting and leisure goods, medical enineering.Strong, stiff parts.Electrically conductive, suitable for cont.. |
|||
Flexural Modulus | 6.00 GPa | 870 ksi | ASTM D790 |
IRPC Polimaxx Polene 111JX TA8 Polypropylene Compound CHARACTERISTICS: POLYPROPYLENE HOMOPOLYMER WITH 40% TALCUM REINFORCED HIGH STIFFNESSAPPLICATIONS: INJECTION MOLDING FOR AUTOPARTS, ELECTRICAL APPLIANCES |
|||
Flexural Modulus | 6.00 GPa | 870 ksi | |
Lehmann & Voss ELECTRAFIL M-2386 Polycarbonate, with carbon fiber and PTFE Applications: Data processing machinery, precision engineering, film and photo industry, sporting and leisure goods, medical enineering.Strong, stiff parts.Electrically conductive, suitable for cont.. |
|||
Flexural Modulus | 6.00 GPa | 870 ksi | |
Lehmann & Voss LUVOCOM® 1105-7876-1 PEEK, with carbon fiber Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Strong, stiff parts.Low warpage.Emergency running property.Information provided by Lehmann.. |
|||
Flexural Modulus | 6.00 GPa | 870 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics NORYL SE1GFN3 PPE+HIPS (Europe-Africa-Middle East) Noryl* SE1GFN3 is a 30% glass reinforced, injection moldable modified polyphenylene ether resin. Designed for improved dimensional stability and good flow , this resin also uses non-chlorinated, non.. |
|||
Flexural Modulus | 6.00 GPa | 870 ksi | ISO 178 |
Solvay TECHNYL® A 52 G1 MX 20 PA66, Eh 0 Description: TECHNYL A 52 G1 MX20 is a Polyamide 6.6 glow wire resistant, reinforced with mineral fillerColors: it is marketed in black color.Available in: Latin AmericaMain Properties: ?Glow wire r.. |
|||
Flexural Modulus | 6.00 GPa | 870 ksi | ASTM D790 |
Techmer ES HiFill® ABS GF15 15% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 15% Filler by WeightFeatures: Good FlowInformation provided by TP Composites, Inc. |
|||
Flexural Modulus | 6.00 GPa | 870 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP STAT-KON RX06001 PA 66 (Europe-Africa-Middle East) LNP* Stat-kon* RX06001 is a compound based on Nylon 66 resin containing Carbon Fiber. Added features of this material include: Easy Molding, High Impact, Electrically Conductive. |
|||
Flexural Modulus | 6.00 GPa | 870 ksi | ISO 178 |
SABIC Innovative Plastics LNP STAT-KON RE002 PA 66 LNP* STAT-KON* RE002 is a compound based on Nylon 66 resin containing 10% Carbon Fiber. Added features of this material include: Electrically Conductive. |
|||
Flexural Modulus | 6.00 GPa | 870 ksi | ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP NF004 PC+ABS LNP* THERMOCOMP* NF004 is a compound based on PC+ABS resin containing 20% Glass Fiber. |
|||
Flexural Modulus | 6.00 GPa | 870 ksi | ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP RX93402 PA 66 LNP THERMOCOMP* RX93402 is a compound based on Nylon 66 resin containing Glass Fiber. Added features of this material include: Flame Retardant. |
|||
Flexural Modulus | 6.00 GPa | 870 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP WF004 PBT (Europe-Africa-Middle East) LNP* Thermocomp* WF-1004 is a compound based on Polybutylene Terephalate resin containing Glass Fiber. |
|||
Flexural Modulus | 6.00 GPa | 870 ksi | ASTM D790 |
A. Schulman POLYFORT™ FXP 6630 Nylon 6.6 Polypropylene Alloy DescriptionPolyfort® FXP 6630 is a nylon 6.6 / polypropylene alloy with 30% wollastonite.Information provided by A. Schulman. |
|||
Flexural Modulus | 6.00 GPa | 870 ksi | ASTM D790 |
A. Schulman POLYFORT™ FPP 1239H Glass Filled Chemically Coupled Homopolymer Polypropylene DescriptionPolyfort® FPP 1239H is a 30% glass filled chemically coupled homopolymer polypropylene product. Information provided by A. Schulman. |
|||
Flexural Modulus | 6.00 GPa | 870 ksi | ASTM-D790 |
Polyram PlusTek PA301G3 Nylon 6.6, Heat Stabilized, 15% Glass Fiber Heat stabilized, 15% glass fiber reinforced polyamide 6.6 for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
Flexural Modulus | 6.00 GPa | 870 ksi | ISO 178 |
Polyram PlusTek PD305G6 Nylon 12 for Injection Molding, 30% Glass-fiber Reinforced 30% Glass-fiber reinforced Nylon 12 for injection molding applications.Information provided by Polyram. |
|||
Flexural Modulus | 6.00 GPa | 870 ksi | ASTM D790 |
A. Schulman POLYFORT™ FPP 1239H Glass Filled Chemically Coupled Homopolymer Polypropylene DescriptionPolyfort® FPP 1239H is a 30% glass filled chemically coupled homopolymer polypropylene product. Information provided by A. Schulman. |
|||
Flexural Modulus | 6.00 GPa | 870 ksi | dry; ISO 178 |
DSM Stanyl® TS271P4 PA46-MF20 20% Whisker Reinforced, Wear and Friction Modified |
|||
Flexural Modulus | 6.00 GPa | 870 ksi | DAM; ISO 178 |
DuPont Performance Polymers Zytel® 80G25HS BK117 Nylon 66
(Unverified Data**) 25% Glass Reinforced Toughened Heat Stabilized Polyamide 66 Zytel 80G25HS BK117 is a 25% glass fiber reinforced toughened heat stabilized black polyamide 66 resin for injection molding.Information p.. |
|||
Flexural Modulus | 6.00 GPa | 870 ksi | ISO 178 |
Eurotec® Tecodur® PB70 GR20 NL PBT 20% glass fiber reinforced Excellent stiffness and hardnessGood mechanical strengthGood creep and fatigue behaviorVery good thermal stabilityExcellent flammability characteristicsGood electrical propertiesHigh wear resistance.. |
|||
Flexural Modulus | 6.00 GPa | 870 ksi | ISO 178 |
Ascend Performance Materials Vydyne® R530H BK0201 Nylon 66, 30% Glass Reinforced, Conditioned Vydyne® R530H BK0201 is general-purpose, heat-stabilized, hydrolysis-resistant, 30% glass-fiber reinforced PA66 resin. Available in black, it is specifically designed to maximize the retention of p.. |
|||
Flexural Modulus | 6.00 GPa | 870 ksi | ASTM D790 |
A. Schulman ComAlloy Hiloy® 628 Nylon 6/6, Mineral Reinforced Data provided by the manufacturer, ComAlloy International Company.30% Mineral Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
Flexural Modulus | 6.00 GPa @Temperature 23.0 °C |
870 ksi @Temperature 73.4 °F |
DAM; ISO 178 |
DuPont Performance Polymers Zytel® 80G25HS BK117 Nylon 66
(Unverified Data**) Zytel® 80G25HS BK117 is a 25% glass fiber reinforced, toughened, heat stabilized, black polyamide 66 resin for injection molding.Information provided by DuPont Performance Polymers |