- Polymer Property : Tensile Strength at Break = 14100 psi
Polymer Property : Tensile Strength at Break = 14100 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 97.0 MPa @Thickness 4.00 mm, Temperature 23.0 °C |
14100 psi @Thickness 0.157 in, Temperature 73.4 °F |
ISO 527-2/5 |
| PolyOne Bergadur™ PB40 G15 U SO1 BK Polybutylene Terephthalate (PBT) Information provided by PolyOne |
|||
| Tensile Strength at Break | 97.0 MPa | 14100 psi | 10mm/min; ASTM D638 |
| Kingfa JH720 G20 20% Glass Fiber Reinforced PC Features:High mechanical strengthGood size stabilityLow tendency to warpGood surfaceSuitable for exact moldingApplications:Imaging equipment shellOA body frameElectrical equipmentComputer plug parts.. |
|||
| Tensile Strength at Break | 97.0 MPa | 14100 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP Lubricomp KFL34 Acetal Copolymer (Europe-Africa-Middle East) LNP* Lubricomp* KFL34 is a compound based on Acetal Copolymer resin containing Glass Fiber, PTFE.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
| Tensile Strength at Break | 97.0 MPa | 14100 psi | Type I, 50 mm/min; ASTM D638 |
| SABIC Innovative Plastics SABIC STAMAX 30YM240 PP SABIC® STAMAX 30YM240 is a 30% long glass fiber reinforced polypropylene. The glass fibers are chemically coupled to the PP matrix, resulting in high stiffness and strength. The IMDS is 16496906... |
|||
| Tensile Strength at Break | 97.0 MPa | 14100 psi | Type I, 50 mm/min; ASTM D638 |
| SABIC Innovative Plastics SABIC STAMAX 30YM243 PP SABIC® STAMAX 30YM243 is a 30% long glass fiber reinforced UV stabilized polypropylene. The glass fibers are chemically coupled to the PP matrix, resulting in high stiffness and strength. The IMD.. |
|||
| Tensile Strength at Break | 97.0 MPa | 14100 psi | ISO 527 Type 1A |
| Solvay TECHNYLSTARâ„¢ S 60G1 V30 PA6, 30% glass filled, Conditioned Description: TECHNYLSTARâ„¢ S 60G1 V30 is a reinforced 30% GF organophosphorous flame retarded grade based on a patented high flow polyamide 6 resin (TechnylStar). This product is heat stabilized.. |
|||
| Tensile Strength at Break | 97.0 MPa | 14100 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics LNP STAT-KON DE002 PC LNP* STAT-KON* DE002 is a Polycarbonate base resin containing 10% Carbon Fiber. Added feature of this grade is: Electrically Conductive. |
|||
| Tensile Strength at Break | 97.0 MPa | 14100 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics LNP STAT-KON DE002 PC (Asia Pacific) LNP* Stat-Kon* DE002 is a Polycarbonate containing Carbon Fiber. |
|||
| Tensile Strength at Break | 97.0 MPa | 14100 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP STAT-KON DE002 PC (Asia Pacific) LNP* Stat-Kon* DE002 is a Polycarbonate containing Carbon Fiber. |
|||
| Tensile Strength at Break | 97.0 MPa | 14100 psi | ASTM D638 |
| SABIC Innovative Plastics LNP STAT-KON DEL33EC PC LNP STAT-KON* DEL33EC is a compound based on Polycarbonate resin containing 15% Carbon Fiber, 15% PTFE. Added features include: Clean Compounding System, Electrically Conductive, Wear Resistant, Ea.. |
|||
| Tensile Strength at Break | 97.0 MPa | 14100 psi | ASTM D638 |
| SABIC Innovative Plastics LNP STAT-KON DEL33EC PC (Asia Pacific) LNP STAT-KON* DEL33EC is a compound based on Polycarbonate resin containing Carbon Fiber, PTFE. Added features of this material include: Clean Compounding System. |
|||
| Tensile Strength at Break | 97.0 MPa | 14100 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics Valox® IQ4860HR PBT Valox iQ* Resin iQ4860HR: Environmentally responsible iQ* PBT resin with 30% Glass reinforcement + UL94 V-0. Hydrolytically stable and impact modified. |
|||
| Tensile Strength at Break | 97.0 MPa | 14100 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics Valox® IQ4860HR PBT (Asia Pacific) Valox iQ* Resin iQ4860HR: Environmentally responsible iQ* PBT resin with 30% Glass reinforcement + UL94 V-0. Hydrolytically stable and impact modified. |
|||
| Tensile Strength at Break | 97.0 MPa | 14100 psi | ISO 527 |
| SABIC Innovative Plastics LNP THERMOCOMP BF004 SAN (Asia Pacific) LNP* Thermocomp* BF004 is a compound based on Styrene Acrylonitrile resin containing Glass Fiber. |
|||
| Tensile Strength at Break | 97.0 MPa | 14100 psi | ISO 527 |
| SABIC Innovative Plastics LNP THERMOCOMP DF0046P PC LNP* Thermocomp* DF0046P is a compound based on Polycarbonate resin containing 20% Glass Fiber. Added features include: Exceptional Processing, Non-Brominated & Non-Chlorinated Flame Retardant. |
|||
| Tensile Strength at Break | 97.0 MPa | 14100 psi | ISO 527 |
| SABIC Innovative Plastics LNP THERMOCOMP DF0046P PC (Asia Pacific) LNP* Thermocomp* DF0046P is a compound based on Polycarbonate resin containing Glass Fiber, Flame Retardant. Added features of this material include: Exceptional Processing, Flame Retardant, Non-Br.. |
|||
| Tensile Strength at Break | 97.0 MPa | 14100 psi | ISO 527 |
| SABIC Innovative Plastics LNP Thermocomp EB004 PEI (Asia Pacific) LNP* Thermocomp* EB004 is a compound based on Polyetherimide resin containing Glass Bead.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
| Tensile Strength at Break | 97.0 MPa | 14100 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP THERMOCOMP RF003H PA 66 LNP* THERMOCOMP* RF003H is a compound based on Nylon 66 containing 15% Glass Fiber. Added feature of this grade is: Healthcare. |
|||
| Tensile Strength at Break | 97.0 MPa | 14100 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP THERMOCOMP RF003XXH PA 66 LNP* THERMOCOMP* RF003XXH is a compound based on Nylon 66 containing 15% Glass Fiber. Added feature of this grade is: Healthcare. |
|||
| Tensile Strength at Break | 97.0 MPa | 14100 psi | Type I, 10 mm/min; SABIC - Japan Method |
| SABIC Innovative Plastics NORYL PCN2615H PPE+PS (Asia Pacific) PPE+PS, Noryl, Glass Fiber, Mica, Flame Retardant, UL Grade, Non-Halogen Flame Retaardant, High Flow, |
|||
| Tensile Strength at Break | 97.0 MPa | 14100 psi | ASTM D638 |
| SABIC Innovative Plastics LNP THERMOCOMP NF004 PC+ABS (Asia Pacific) LNP* Thermocomp* NF004 is a compound based on PC+ABS Blend resin containing Glass Fiber. |
|||
| Tensile Strength at Break | 97.0 MPa | 14100 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP THERMOCOMP ZF004 PPE+PS (Europe-Africa-Middle East) LNP* THERMOCOMP* ZF004 is a compound based on PPE+PS Blend resin containing Glass Fiber. |
|||
| Tensile Strength at Break | 97.0 MPa | 14100 psi | ISO 527-93 |
| Wellman Wellamid® MRGFX1716-BK1 40% Mineral/Glass Reinforced, Silicone Lubricated Nylon 6 Description: Mineral/Glass Reinforced, Silicone Lubricated Nylon 6Information provided by Wellman. |
|||
| Tensile Strength at Break | 97.0 MPa @Temperature 23.0 °C |
14100 psi @Temperature 73.4 °F |
ISO 527 |
| DuPont Performance Polymers Rynite® 515CS BK575M PET Rynite® 515CS BK575M is a 15% glass fiber reinforced, black polyethylene terephthalate resin modified for improved color stability after heat aging.Information provided by DuPont Performance Polyme.. |
|||
| Tensile Strength at Break | 97.0 MPa | 14100 psi | ISO 527 |
| BASF Petra® 7010 BK 5830 15% Glass Filled PET Description: Petra 7010 BK5830 is a 15% glass fiber reinforced, pigmented black injection molding compound based on post-consumer recycle polyethylene terephthalate. Formulated for superior surface .. |
|||
| Tensile Strength at Break | 97.5 MPa @Temperature 160 - 175 °C, Time 1.80e+7 sec |
14100 psi @Temperature 320 - 347 °F, Time 5000 hour |
5 [mm/min], 50% Loss of Tensile Strength; ICE 216 |
| Akro-Plastic Akromid® B3 GF 35 (2473) PA 6 Dry, 35% Glass Filled AKROMID® B (Polyamide 6) is an engineering compound, characterized by high mechanical strength, stiffness and thermal resistance. Furthermore, this polyamide offers high toughness at low temperatur.. |
|||
| Tensile Strength at Break | 97.5 MPa @Temperature 130 - 150 °C, Time 7.20e+7 sec |
14100 psi @Temperature 266 - 302 °F, Time 20000 hour |
5 [mm/min], 50% Loss of Tensile Strength; ICE 216 |
| Akro-Plastic Akromid® B3 GF 35 (2473) PA 6 Dry, 35% Glass Filled AKROMID® B (Polyamide 6) is an engineering compound, characterized by high mechanical strength, stiffness and thermal resistance. Furthermore, this polyamide offers high toughness at low temperatur.. |
|||
| Tensile Strength at Break | 97.0 MPa @Temperature 80.0 °C |
14100 psi @Temperature 176 °F |
ASTM Test |
| BASF Ultramid® TG7S 35% Glass Filled PA6 (Dry) Ultramid TG7S is a 34% glass reinforced, heat stabilized, impact modified PA6 injection molding grade. It was developed to meet the demanding requirements of the first North American seat
cushion .. |
|||
| Tensile Strength at Break | 97.0 MPa @Temperature 80.0 °C |
14100 psi @Temperature 176 °F |
ISO Data |
| BASF Ultramid® TG7S 35% Glass Filled PA6 (Dry) Ultramid TG7S is a 34% glass reinforced, heat stabilized, impact modified PA6 injection molding grade. It was developed to meet the demanding requirements of the first North American seat
cushion .. |
|||
| Tensile Strength at Break | 97.2 MPa | 14100 psi | ASTM D638 |
| Chase Plastics CP Pryme® N233GL (COND, 50% RH) Nylon 6, 33% Glass Fiber Reinforced, Internally Lubricated Information provided by Chase Plastics. |
|||