SABIC Innovative Plastics LNP Stat-kon RE003 PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Stat-kon RE003 PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP STAT-KON* RE003 is a compound based on Nylon 66 resin containing Carbon Fiber. Added features of this material include: Electrically Conductive.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | ISO 1183 |
| 1.203 g/cc | 0.04346 lb/in³ | ASTM D 792 | |
| Moisture Absorption at Equilibrium | 1.47 % | 1.47 % | 23°C / 50% RH; ISO 62 |
| 0.93 % @Time 86400 sec |
0.93 % @Time 24.0 hour |
50% RH; ASTM D 570 | |
| Linear Mold Shrinkage, Flow | 0.0017 - 0.0026 cm/cm @Time 86400 sec |
0.0017 - 0.0026 in/in @Time 24.0 hour |
ISO 294 |
| 0.0020 - 0.0030 cm/cm @Time 86400 sec |
0.0020 - 0.0030 in/in @Time 24.0 hour |
ASTM D 955 | |
| Linear Mold Shrinkage, Transverse | 0.0068 - 0.0078 cm/cm @Time 86400 sec |
0.0068 - 0.0078 in/in @Time 24.0 hour |
ISO 294 |
| 0.0070 - 0.0080 cm/cm @Time 86400 sec |
0.0070 - 0.0080 in/in @Time 24.0 hour |
ASTM D 955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 180 MPa | 26100 psi | ISO 527 |
| 201 MPa | 29200 psi | ASTM D 638 | |
| Elongation at Break | 2.4 % | 2.4 % | ISO 527 |
| 2.6 % | 2.6 % | ASTM D 638 | |
| Tensile Modulus | 11.55 GPa | 1675 ksi | 1 mm/min; ISO 527 |
| 11.72 GPa | 1700 ksi | 50 mm/min; ASTM D 638 | |
| Flexural Strength | 287 MPa | 41600 psi | ISO 178 |
| 302 MPa | 43800 psi | ASTM D 790 | |
| Flexural Modulus | 10.65 GPa | 1545 ksi | ISO 178 |
| 11.26 GPa | 1633 ksi | ASTM D 790 | |
| Izod Impact, Notched | 0.640 J/cm @Temperature 23.0 °C |
1.20 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 4.32 J/cm @Temperature 23.0 °C |
8.09 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² @Temperature 23.0 °C |
2.38 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 42.0 kJ/m² @Temperature 23.0 °C |
20.0 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| 8.00 J @Temperature 23.0 °C |
5.90 ft-lb @Temperature 73.4 °F |
Instrumented Impact Energy @ peak; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 24.3 µm/m-°C @Temperature -40.0 - 40.0 °C |
13.5 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 24.3 µm/m-°C @Temperature -40.0 - 40.0 °C |
13.5 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 68.5 µm/m-°C @Temperature -40.0 - 40.0 °C |
38.1 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 68.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
38.1 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 260 °C @Thickness 3.20 mm |
500 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 261 °C | 502 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 250 °C @Thickness 3.20 mm |
482 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 100 - 1.00e+6 ohm | 100 - 1.00e+6 ohm | ASTM D 257 |
Users viewing this material also viewed the following:
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 0.5 PHR Zinc Stearate
- Sibur 140-13 Compound 230/1 Polyvinyl Chloride (PVC)
- Silberline Sparkle Silver® 3334-AR
- DuPont™ Kapton® 200A Polyimide Film, 50 Micron Thickness
- EMS-Grivory Grivory® LVX-65H SST nat PA12-GF65
- 3M Adhesive Remover
- Chang Chun Plastic PBT3015 15% Glass Fiber Enforced PBT
- 3M 9472FL Adhesive Transfer Tape with 300LSE Adhesive
- Solvay Specialty Polymers Veradel® 3300 PREM Polyethersulfone (PESU) (Unverified Data**)
- A. Schulman POLYBATCH™ Bright While LL80250 Concentrate Based In LLDPE
Copyright © lookpolymers.com All Rights Reserved