SABIC Innovative Plastics LNP LUBRICOMP YL003C Polyester Elastomer (Asia Pacific)

Category Polymer , Thermoplastic , Polyester, TP
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRICOMP YL003C Polyester Elastomer (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LUBRICOMP* YL-4030 CCS is a PTFE Lubricated Compound based on Polyester Elastomer resin which has low ionic and low outgassing performance for the Semicon and Internal Hard Disk Drive applications.
Physical Properties Metric English Comments
Density 1.27 g/cc
0.0459 lb/in³
ASTM D792
1.27 g/cc
0.0459 lb/in³
ISO 1183
Water Absorption 0.20 %

@Time 173000 sec
0.20 %

@Time 48.0 hour
ASTM D570
Water Absorption at Saturation 0.50 %
0.50 %
ISO 62
Linear Mold Shrinkage, Flow 0.015 - 0.017 cm/cm

@Time 86400 sec
0.015 - 0.017 in/in

@Time 24.0 hour
ASTM D955
0.016 cm/cm

@Time 86400 sec
0.016 in/in

@Time 24.0 hour
ISO 294
Linear Mold Shrinkage, Transverse 0.017 - 0.019 cm/cm

@Time 86400 sec
0.017 - 0.019 in/in

@Time 24.0 hour
ASTM D955
0.018 cm/cm

@Time 86400 sec
0.018 in/in

@Time 24.0 hour
ISO 294
Mechanical Properties Metric English Comments
Hardness, Shore D 56
56
ASTM D2240
Tensile Strength at Break 22.0 MPa
3190 psi
ASTM D638
Elongation at Break 90 %
90 %
ASTM D638
>= 450 %
>= 450 %
50 mm/min; ISO 527
Tensile Modulus 0.260 GPa
37.7 ksi
1 mm/min; ISO 527
0.280 GPa
40.6 ksi
50 mm/min; ASTM D638
Flexural Strength 12.0 MPa
1740 psi
ISO 178
19.0 MPa
2760 psi
ASTM D790
Flexural Modulus 0.280 GPa
40.6 ksi
ISO 178
0.290 GPa
42.1 ksi
ASTM D790
Izod Impact, Notched 1.50 J/cm
2.81 ft-lb/in
ASTM D256
Izod Impact, Unnotched 5.80 J/cm
10.9 ft-lb/in
ASTM D4812
Izod Impact, Unnotched (ISO) 23.0 kJ/m²
10.9 ft-lb/in²
80*10*4; ISO 180/1U
48.0 kJ/m²
22.8 ft-lb/in²
80*10*3; ISO 180/1U
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 110 µm/m-°C

@Temperature -40.0 - 40.0 °C
61.1 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
110 µm/m-°C

@Temperature -40.0 - 40.0 °C
61.1 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 180 µm/m-°C

@Temperature -40.0 - 40.0 °C
100 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
180 µm/m-°C

@Temperature -40.0 - 40.0 °C
100 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 88.0 °C
190 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
85.0 °C

@Thickness 6.40 mm
185 °F

@Thickness 0.252 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 57.0 °C
135 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
54.0 °C

@Thickness 6.40 mm
129 °F

@Thickness 0.252 in
unannealed; ASTM D648
Flammability, UL94 HB

@Thickness 1.00 mm
HB

@Thickness 0.0394 in
UL 94