- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 54.0 °C
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 54.0 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C | 129 °F | 120°C/h; ISO 75/1 |
| Polykemi AB POLYfill PP CQX8025 R2 Polypropylene, Mineral Reinforced, Scratch Resistant Information provided by Polykemi AB |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C | 129 °F | (from DAM) |
| Ineos ABS Triax® 1180 ABS + Polyamide Blend (Conditioned)
(discontinued **) Key Features:UnfilledHigh impact or high impact modifiedSuitable processing methods:Injection moldingInformation provided by Bayer Polymers.LANXESS was spun-off from Bayer in early 2005. Business r.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 - 136 °C | 129 - 277 °F | Average value: 89.3 °C Grade Count:8 |
| Overview of materials for Thermoset Polyurethane, Liquid This property data is a summary of similar materials in the MatWeb database for the category "Thermoset Polyurethane, Liquid". Each property range of values reported is minimum and maximum values of.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C | 129 °F | ASTM D648 |
| Custom Resins Vexel™ 3250 PBT
(discontinued **) General Purpose Unreinforced; High Flow. Property data for dry as molded samples.Data provided by the manufacturer |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C | 129 °F | |
| Plastcom SLOVAMID 6 MI PA6, improved strength FeaturesPA 6 with the content of thermoplastic kaoutchouc. Impacted, for mouldings with high toughness either at minus temperatures, suitable for external use, eg. ski shoes, sports and safety helme.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C | 129 °F | ISO 75 |
| Phillips Sumika Marlex® CHP-370 Thermoplastic Polyolefin
(discontinued **) Thermoplastic Polyolefin, Good Stiffness and Impact PerformanceApplications: Automotive Pillar TrimConditioning after Molding: 48 hr at 23°CNominal Shrinkage: 0.8-1.0%Drying conditionsTemperature: .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C | 129 °F | ISO 75 |
| Solvay Engineered Polymers SEQUEL® 2322 Engineered Polyolefin
(discontinued **) SEQUEL® 2322 engineered polyolefin is designed for mold-in-color automotive interior applications that require medium stiffness and good dimensional stability. This material exhibits excellent low.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 - 75.6 °C | 129 - 168 °F | Average value: 67.1 °C Grade Count:12 |
| Overview of materials for PVC, Sheet Grade This property data is a summary of similar materials in the MatWeb database for the category "PVC, Sheet Grade". Each property range of values reported is minimum and maximum values of appropriate M.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C @Thickness 6.40 mm |
129 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| LG Chemical Lupox® GP1000H PBT Description: Injection Molding, PBT, High Flow, High ImpactApplication: Automotive (Connector)CAS No. 155123-66-3 and 24968-12-5Information provided by LG Chemical |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C | 129 °F | |
| Isoflon PA 12 Polyamide 12 General use for mechanical partsGood heat resistanceEasy to useInformation provided by Isoflon. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C @Thickness 3.20 mm |
129 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP PL002 PA 6 LNP* LUBRICOMP* PL002 is a compound based on Nylon 6 base resin containing 10% PTFE. Added feature of this grade is: Wear Resistant. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C @Thickness 6.40 mm |
129 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Valox® 311 PBT Unreinforced, improved resistance to UV. Medium viscosity. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C @Thickness 3.20 mm |
129 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Valox® HX215HP PBT High Flow, Unreinforced, Polybutylene Terephthalate (PBT). For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI), food conta.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C @Thickness 3.20 mm |
129 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Valox® IQ3001 PBT (Europe-Africa-Middle East) Valox IQ3001 is an unfilled environmentally responsible iQ-PBT resin modified with elastomer. Targeted for flexible hinge applications. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C @Thickness 3.20 mm |
129 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Valox® V2000DM PBT (Europe-Africa-Middle East) Unreinforced, directly metallizable PBT injection molding resin with high flow better release characteristics. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C | 129 °F | 80*10*4 s=60mm; ISO 75-1 a |
| Sax Polymers SAXAMID 136Q32 Nylon 6, Injection Molding Grade SAXAMID 136Q32 is a high impact-modified polyamide 6 injection-molding-grade.Information provided by SAX Polymers |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C @Thickness 3.20 mm |
129 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Valox® IQ3001 PBT Valox IQ3001 is an unfilled environmentally responsible iQ-PBT resin modified with elastomer. Targeted for flexible hinge applications. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C @Thickness 3.20 mm |
129 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Valox® V2000DM PBT Unreinforced, directly metallizable PBT injection molding resin with high flow better release characteristics. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C | 129 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP STAT-LOY W3000XXJ PBT LNP* STAT-LOY* W3000XXJ is a compound based on PBT. Added features of this grade include: Anti-Stat, Colorable, Healthcare |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C | 129 °F | Plain Cast Resin; ASTM D648 |
| TSE Industries EcoWIND® M110 General Purpose Filament Winding Polyurethane Resin TSE-EcoWIND® resins are “Environmentally-Preferred Products” or EPP’s. They are a pair of polyurethane resins free of Styrene, and are “ultra-low” emitting during application. TSE-EcoWIND® re.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C | 129 °F | ISO 75 |
| Unipetrol PP MONSTEN® GB 503 Polypropylene Impact Copolymer Made for injection molding applications. Basic stabilization. Impact copolymer.Information provided by Unipetrol RPA |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C | 129 °F | ISO 75-1, 2 |
| Polyplastics Duranex® CE7300 Polybutylene Terephthalate (PBT), Higher impact resistant DURANEX® is a crystalline thermoplastic based on polybutylene terephthalate (PBT) that can be readily strengthened, modified, or otherwise performance enhanced through the addition of glass fibers .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C | 129 °F | ISO 75-1/-2 |
| DuPont Performance Polymers Crastin® S610SF BK851 Polybutylene Terephthalate (PBT) Unreinforced Low Viscosity Polybutylene Terephthalate Developed for Super Fast Production Crastin S610SF is an unreinforced low viscosity polybutylene terephthalate for injection molding. It has hig.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C | 129 °F | ASTM Test |
| BASF Ultramid® B27 E 01 PA6 (Dry) Ultramid B27 E 01 is a low viscosity general-purpose, extrusion PA6 grade well suited for compounding. It conforms to FDA requirements including, 21 CFR 177.1500,EU Directive 2002/72/EC, the German.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C | 129 °F | ASTM D648 |
| Albis Plastics Cellulose Acetate Butyrate B902 (UV Inhibitor Added), 16% Plasticizer
(discontinued **) Amorphous Cellulose Acetate Butyrate (CAB)Characteristics: Dimensional Stability, Weatherability and Low Temp Impact StrengthApplications: Pens, Ski Goggles, Auto Trim, Skylights, Tool Handles and T.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C | 129 °F | ASTM D648 |
| Albis Plastics Cellulose Acetate Butyrate B9004 (Odor Mask Added), 16% Plasticizer
(discontinued **) Amorphous Cellulose Acetate Butyrate (CAB)Characteristics: Dimensional Stability, Weatherability and Low Temp Impact StrengthApplications: Pens, Ski Goggles, Auto Trim, Skylights, Tool Handles and T.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C | 129 °F | ISO 75 |
| Unipetrol PP MONSTEN® EH 501 Polypropylene Impact Copolymer Made for extrusion applications. LHTA stabilization. Impact copolymer.Information provided by Unipetrol RPA |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C | 129 °F | ASTM D648 |
| Adell RZ-16 Copolymer Polypropylene, 30% Calcium Carbonate Filled Data provided by Adell Plastics, Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C | 129 °F | ASTM D648 |
| Braskem CP 286 Injection Molding Polypropylene Heterophasic Copolymer Description: CP 286 is a high melt flow rate, heterophasic copolymer, suitable for injection moulding applications and also as base resin for compound. The resin combines excellent stiffness with g.. |
|||