- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 88.0 °C
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 88.0 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 88.0 °C @Thickness 3.20 mm |
190 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Cycolac® FR30U ABS (Asia Pacific) Flame retardant ABS. Good indoor UV properties. Excellent moldability with no bloom. V-1/V-0/5VB rated. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 88.0 °C | 190 °F | 120°C/h; ISO 75/1 |
| Polykemi AB POLYabs S20 ABS Information provided by Polykemi AB |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 88.0 °C @Thickness 4.00 mm |
190 °F @Thickness 0.157 in |
ISO 75/Method Bf |
| Premix Thermoplastics PRE-ELEC® ABS 1410 PRE-ELEC ABS 1410 is a conductive thermoplastic compound based on ABS. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-ELEC ABS 141.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 88.0 °C | 190 °F | 4 mm thick;10.0 mm wide molded rod; ISO 75/Method Bf |
| Premix Thermoplastics PRE-ELEC® ESD 7100 PRE-ELEC ESD 7100 is a static dissipative thermoplastic compound based on ABS. The dissipative property is permanent and built into the polymer chain. PRE-ELEC ESD 7100 has been developed for inject.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 88.0 °C | 190 °F | 120°C/h; ISO 75/1 |
| Polykemi AB POLYelast TPE R44 TV10 Thermoplastic Elastomer, Mineral Reinforced Information provided by Polykemi AB |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 88.0 °C @Thickness 3.20 mm |
190 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Cycoloy® CU6800 PC+ABS (Asia Pacific) Non-chlorinated and non-brominated flame retardant PC/ABS featuring excellent flow properties. UL-94 V1 listed at 2.0mm intended for a wide range of different applications. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 88.0 °C | 190 °F | unannealed; ASTM D648 |
| Phillips 66 COPYLENE® CR350LN Polypropylene, Random Copolymer COPYLENE™ CR350LN is a high flow random copolymer nucleated and with antistat for good mold release in injection molding applications. Applications: Containers, Closures, HousewaresInformation prov.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 88.0 °C | 190 °F | 120°C/h; ISO 75/1 |
| Polykemi AB POLYabs F00L ABS Information provided by Polykemi AB |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 88.0 °C | 190 °F | 120°C/h; ISO 75/1 |
| Polykemi AB POLYabs N00 ABS Information provided by Polykemi AB |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 88.0 °C | 190 °F | |
| Arkema Group Oroglas® HFI-7 Acrylic
(discontinued **) OROGLAS HFI-7 is a medium impact grade that in addition to the improvement in impact resistance provides superior flow which contribute to reduce the cycle time and improve demolding.Key features :.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 88.0 °C | 190 °F | unannealed; ASTM D648 |
| Phillips 66 COPYLENE® CH020-02 Polypropylene, Thermoforming, Sheet, Film COPYLENE™ CH020-02 is a polypropylene homopolymer resin suitable for thermoforming, sheet and film fiber applications. Applications: Opaque Containers. Equivalent to Pro-fax® HL783HInformation pro.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 88.0 °C | 190 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP Lubricomp CI001 PS LNP* Lubricomp* CI001 is a compound based on Polystyrene resin containing Silicone. Added features of this material include: Internally Lubricated.This data was supplied by SABIC-IP for the America.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 88.0 °C @Thickness 6.40 mm |
190 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| LG Chemical LUPOY GN5008HF PC/ABS, Halogen Free Flame Retardant, High Impact Description: Injection Molding, PC/ABS, Halogen Free Flame Retardant, Heat Resistance, High FlowApplication: E&E (OA, Navigation Housing)CAS: 103598-77-2, 9003-56-9 and 181028-79-5Information provid.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 88.0 °C | 190 °F | ISO 75-1,-2 |
| Inno-Comp INNOPOL® CS 4-8000 Polypropylene Random Copolymer INNOPOL® CS 4-8000 is a polypropylene random copolymer. This grade is available in nature and custom colored form.INNOPOL® CS 4-8000 is highly suitable for pressure pipe manufacturing, includi.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 88.0 °C | 190 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP STAT-KON DD0001 PC (Asia Pacific) LNP STAT-KON* DD0001 is a compound based on Polycarbonate resin containing Carbon Powder, Flame Retardant. Added features of this material include: Electrically Conductive. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 88.0 °C | 190 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP STAT-KON DD0001 PC (Europe-Africa-Middle East) LNP STAT-KON* DD0001 is a compound based on Polycarbonate resin containing Carbon Powder, Flame Retardant. Added features of this material include: Electrically Conductive. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 88.0 °C | 190 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP STAT-KON MD000AP PP LNP* STAT-KON* MD000AP is a compound based on Polypropylene containing Carbon Powder. Added features of this grade include: Electrically Conductive, Exceptional Processing. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 88.0 °C | 190 °F | ISO 75 |
| Styrolution PS-145D Polystyrene Description: Polystyrene 145D is a high flow, general purpose polystyrene. PS 145D offers exceptional processing characteristics for thing walled parts, multi-cavity tools, and complex designs. It i.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 88.0 °C | 190 °F | Unannealed; ASTM D648 |
| Lubrizol Isoplast® 2531 Engineering Thermoplastic Polyurethane Resin for Medical Applications Features: USP Class VIAvailable in Americas, Europe, Middle East, Africa, India and AsiaData provided by LubrizolLubrizol acquired the Isoplast product line from Dow in 2009. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 88.0 °C | 190 °F | ISO 75-2 |
| Borealis Daplen™ EF040AE TPO Compound Daplen EF040AE is a elastomer modified polypropylene compound intended for injection molding. Daplen EF040AE is a material with excellent impact/stiffness ratio. Thanks to its low thermal expansio.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 88.0 °C | 190 °F | ASTM D648 |
| Formosa Plastics Formolene® 6535A Thin Walled Injection Molding Polypropylene Impact CopolymerApplications: Housewares, dairy packaging and stadium cups.Formolene 6535A is a medium impact, controlled rheology copolymer of polypropylene designed for such applications as housew.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 88.0 °C | 190 °F | ASTM D648 |
| Total PPR 7238 Polypropylene, Random Copolymer - Blow Molding Impact Strength. TOTAL Polypropylene 7238 offers excellent impact strength, clarity and gloss.Lubricated 7238 offers superior core rod release for ease in processing.High Purity. 7238 features min.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 88.0 °C | 190 °F | Annealed; ISO 75-2A |
| Total PSC 1340 Crystal Polystyrene 1340 is a high molecular weight crystal polystyrene which allows maximum dilution rates with high impact polystyrene grades such as LACQRENE® 7240. In dilution, LACQRENE® 1340 gives excellent pro.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 88.0 °C | 190 °F | ASTM D648 |
| Total PPC 4720 WZ Polypropylene, Impact Copolymer ATOFINA 4720 is an impact copolymer. 4720 is characterized by a high fluidity offering a combination of east of processing and good mechanical properties.ApplicationATOFINA 4720 has been formulated.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 88.0 °C | 190 °F | ASTM D648 |
| Eastman Tenite 307E0V16310 Propionate Clear, Trsp Tenite cellulosic plastics are noted for their excellent balance of properties - toughness, hardness, strength, surface gloss, clarity, and a warm feel. The mechanical properties if Tenite cellulosi.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 88.0 °C | 190 °F | ASTM D648 |
| Entec Hypro™ PP-CP0.5/10 Impact Copolymer, Fractional Melt Flow This is a high impact copolymer intended for use in blow molding, pipe, tubing, sheet and other extrusion applications.Information provided by Entec |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 88.0 °C | 190 °F | ASTM D-648 |
| Bapolan® 6450 Polystyrene Injection Molding Resin Bapolan 6450 is a high impact polystyrene resin designed for injection molding applications requiring fast cycle times, superior impact and gloss. It complies with US FDA21 CFR177.1640 and 94HB UL .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 88.0 - 90.0 °C | 190 - 194 °F | |
| C.O.I.M. EXTER S® S 501 Neopentylic Resin Description: The Exter S product line contains a large number of unsaturated polyester resin products with an array of properties and applications.Specific Notes for ESTER S® S 501: Resin for high-.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 88.0 °C | 190 °F | ASTM D648 |
| Bapolene® PP5083 Polypropylene, Injection Grade Bapolene PP 5083 is a clarified PP Random Copolymer for injection molding. This resin exhibits good processing and impact properties. This product meets FDA regulation 21CFR 177.1520 and is suitab.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 88.0 °C | 190 °F | ASTM D648 |
| Carmel Olefins CAPILENE® SR 50 Polypropylene Impact Copolymer Description: CAPILENE® SR 50 is a medium melt flow rate impact copolymer for injection molding applications. This grade offers good balance of stiffness, impact strength and processability.Applic.. |
|||