SABIC Innovative Plastics LNP VERTON MV006BS PP
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP VERTON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP VERTON MV006BS PP.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* VERTON* MV006BS is a compound based on Polypropylene resin containing 30% Long Glass Fiber. Added features of this grade include: Heat Stabilized, Burst Pressure, Structural, Chemically Coupled.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.09 g/cc | 1.09 g/cc | ASTM D792 |
| Density | 1.09 g/cc | 0.0394 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.0200 % | 0.0200 % | 23°C / 50% RH; ISO 62 |
| 0.0300 % | 0.0300 % | 50% RH, 24 hrs; ASTM D570 | |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0060 cm/cm @Time 86400 sec |
0.0030 - 0.0060 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0080 cm/cm @Time 86400 sec |
0.0050 - 0.0080 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 87.0 MPa | 12600 psi | 5 mm/min; ISO 527 |
| 104 MPa | 15100 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 96.0 MPa | 13900 psi | 5 mm/min; ISO 527 |
| 104 MPa | 15100 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 2.2 % | 2.2 % | 5 mm/min; ISO 527 |
| 2.3 % | 2.3 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 2.2 % | 2.2 % | 5 mm/min; ISO 527 |
| 2.3 % | 2.3 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 6.33 GPa | 918 ksi | 1 mm/min; ISO 527 |
| 6.93 GPa | 1010 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 145 MPa | 21000 psi | ISO 178 |
| Flexural Yield Strength | 162 MPa | 23500 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 5.84 GPa | 847 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 2.14 J/cm | 4.01 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 7.70 J/cm | 14.4 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 20.0 kJ/m² | 9.52 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 53.0 kJ/m² | 25.2 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 12.0 J @Temperature 23.0 °C |
8.85 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 6.00 J | 4.43 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 76.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
42.2 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 76.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
42.2 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 162 °C | 324 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 163 °C @Thickness 3.20 mm |
325 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 155 °C | 311 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 155 °C @Thickness 3.20 mm |
311 °F @Thickness 0.126 in |
unannealed; ASTM D648 |