Polymer Resources TP-IGFR-G30 Polybutylene Terephthalate, 30% Glass Reinforced, Flame Retardant, Reduced Warpage

Category	Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled , Polybutylene Terephthalate (PBT), Glass Fiber Filled, Flame Retardant
Manufacturer	Polymer Resources, LTD
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Polymer Resources TP-IGFR-G30 Polybutylene Terephthalate, 30% Glass Reinforced, Flame Retardant, Reduced Warpage.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Polybutylene Terephthalate, 30% Glass Reinforced, Flame Retardant, Reduced WarpageProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation.

Physical Properties	Metric	English	Comments
Specific Gravity	1.57 g/cc	1.57 g/cc	ASTM D792
Linear Mold Shrinkage	0.0040 - 0.0080 cm/cm	0.0040 - 0.0080 in/in	ASTM D955
Melt Flow	5.0 - 15 g/10 min @Load 2.16 kg, Temperature 250 °C	5.0 - 15 g/10 min @Load 4.76 lb, Temperature 482 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	107 MPa	15500 psi	ASTM D638
Tensile Strength, Yield	107 MPa	15500 psi	ASTM D638
Flexural Strength	172 MPa	25000 psi	ASTM D790
Flexural Modulus	6.21 GPa	900 ksi	ASTM D790
Izod Impact, Notched	0.801 J/cm @Temperature 22.8 °C	1.50 ft-lb/in @Temperature 73.0 °F	ASTM D256

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	199 °C	390 °F	ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	157 °C	315 °F	ASTM D648
UL RTI, Electrical	75.0 °C @Thickness 1.50 mm	167 °F @Thickness 0.0591 in	UL 746
	75.0 °C @Thickness 3.00 mm	167 °F @Thickness 0.118 in	UL 746
UL RTI, Mechanical with Impact	75.0 °C @Thickness 1.50 mm	167 °F @Thickness 0.0591 in	UL 746
	75.0 °C @Thickness 3.00 mm	167 °F @Thickness 0.118 in	UL 746
UL RTI, Mechanical without Impact	75.0 °C @Thickness 1.50 mm	167 °F @Thickness 0.0591 in	UL 746
	75.0 °C @Thickness 3.00 mm	167 °F @Thickness 0.118 in	UL 746
Flammability, UL94	V-0 @Thickness 1.50 mm	V-0 @Thickness 0.0591 in
	V-0 @Thickness 3.00 mm	V-0 @Thickness 0.118 in

Electrical Properties	Metric	English	Comments
Comparative Tracking Index	175 - 250 V	175 - 250 V	UL 746
Hot Wire Ignition, HWI	>= 120 sec @Thickness 1.50 mm	>= 120 sec @Thickness 0.0591 in	UL 746
	>= 120 sec @Thickness 3.00 mm	>= 120 sec @Thickness 0.118 in	UL 746
High Amp Arc Ignition, HAI	30 - 60 arcs @Thickness 1.50 mm	30 - 60 arcs @Thickness 0.0591 in	UL 746
	>= 120 arcs @Thickness 3.00 mm	>= 120 arcs @Thickness 0.118 in	UL 746

Processing Properties	Metric	English
Rear Barrel Temperature	238 - 254 °C	460 - 490 °F
Middle Barrel Temperature	243 - 260 °C	470 - 500 °F
Front Barrel Temperature	249 - 266 °C	480 - 510 °F
Melt Temperature	232 - 260 °C	450 - 500 °F
Mold Temperature	71.1 - 87.8 °C	160 - 190 °F
Drying Temperature	116 - 121 °C	240 - 250 °F
Dry Time	3.00 - 4.00 hour	3.00 - 4.00 hour

Descriptive Properties	Value	Comments
Vent	0.0005