PolyOne Versaflex™ OM 3060-1 Thermoplastic Elastomer (TPE)

Category Polymer , Thermoplastic , Elastomer, TPE
Manufacturer PolyOne Corporation
Trade Name Versaflex™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PolyOne Versaflex™ OM 3060-1 Thermoplastic Elastomer (TPE).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Versaflex™ OM 3060-1 is a clear, medical compliant overmold designed to adhere to multiple substrates. - Excellent bond to PC, ABS, PC/ABS, PC/PETG, and PC/PBT - Rubber Feel - Soft TouchVersaflex™ OM 3060-1 can use a variety of color concentrates. The type of color concentrates most suitable for the application are dependent upon the grade and the specific substrate materials, including color concentrate and filler levels. It should be noted that some color concentrates may affect adhesion to the substrate, resulting in decreased peel strength. Concentrates based on PVC should not be used. The final determination of color concentrate suitable should be determined by customer trials. Purge thoroughly before and after use of this product with a low flow (0.5-2.5 MFR) polyethylene or polypropylene. Versaflex™ OM 3060-1 can use regrind up to 20% with minimal property losses, provided that the regrind is free of contamination. To minimize losses during molding, the melt temperature should remain as low as possible. The final determination of regrind effectiveness should be determined by the customer. Versaflex™ OM 3060-1 has good melt stability. Maximum residence times may vary, depending on the size of the barrel. Generally, the barrel should be emptied if it is idle for periods of 8 - 10 minutes or longer. Drying is not Required Injection Speed: 1 to 5 in/sec 1st Stage - Boost Pressure: 180 to 580 psi 2nd Stage - Hold Pressure: 50% of Boost Hold Time (Thick Part): 4 to 10 sec Hold Time (Thin Part): 1 to 3 secInformation provided by PolyOne
Physical Properties Metric English Comments
Specific Gravity 0.898 g/cc
0.898 g/cc
ASTM D792
Viscosity 13000 cP

@Shear Rate 11200 1/s,
Temperature 200 °C
13000 cP

@Shear Rate 11200 1/s,
Temperature 392 °F
ASTM D3835
Linear Mold Shrinkage, Flow 0.0080 - 0.012 cm/cm
0.0080 - 0.012 in/in
ASTM D955
Mechanical Properties Metric English Comments
Hardness, Shore A 59

@Temperature 23.0 °C
59

@Temperature 73.4 °F
10 sec; ASTM D2240
Tensile Strength at Break 3.45 MPa

@Temperature 23.0 °C
500 psi

@Temperature 73.4 °F
Die C2 hr; ASTM D412
Tensile Stress 2.48 MPa

@Strain 300 %,
Temperature 23.0 °C
360 psi

@Strain 300 %,
Temperature 73.4 °F
Die C2 hr; ASTM D412
Elongation at Break 480 %

@Temperature 23.0 °C
480 %

@Temperature 73.4 °F
Die C2 hr; ASTM D412
Tear Strength 31.5 kN/m
180 pli
ASTM D624
Compression Set 33 %

@Temperature 23.0 °C,
Time 79200 sec
33 %

@Temperature 73.4 °F,
Time 22.0 hour
ASTM D395B
Thermal Properties Metric English Comments
Flammability, UL94 HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
UL 94
Processing Properties Metric English Comments
Rear Barrel Temperature 177 - 216 °C
351 - 421 °F
Middle Barrel Temperature 182 - 221 °C
360 - 430 °F
Front Barrel Temperature 193 - 232 °C
379 - 450 °F
Nozzle Temperature 204 - 243 °C
399 - 469 °F
Mold Temperature 21.1 - 32.2 °C
70.0 - 90.0 °F
Back Pressure 0.517 - 1.21 MPa
75.0 - 175 psi
Screw Speed 75 - 125 rpm
75 - 125 rpm
Descriptive Properties Value Comments
Agency Ratings FDA Unspecified Rating
ISO 10993 Part 4
ISO 10993 Part 5
UL 94 .QMFZ2.E76261
USP Class VI
Appearance Clear/Transparent
Features Good Colorability
Good Moldability
Good Processability
Good Processing Stability
High Clarity
Forms Pellets
Generic Material TPE
Generic Name Thermoplastic Elastomer (TPE)
Manufacturer / Supplier GLS Thermoplastic Elastomers
Processing Method Injection Molding
Regional Availability Africa & Middle East
Asia Pacific
Europe
North America
South America
RoHS Compliance RoHS Compliant
Suggested Max Regrind 20%
Uses Consumer Applications
Electrical/Electronic Applications
Medical/Healthcare Applications
Overmolding
Personal Care
Transparent or Translucent Parts
Transparent Parts
Copyright © lookpolymers.com All Rights Reserved