Plaskolite Optix® CA-927 Impact Modified Acrylic Resin
| Category | Polymer , Thermoplastic , Acrylic (PMMA) , Acrylic, Impact Modified, Molded |
| Manufacturer | Plaskolite |
| Trade Name | Optix® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Plaskolite Optix® CA-927 Impact Modified Acrylic Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Injection Molding Grade Pellets. Better impact strength than CA-924. Excellent surface gloss, optical clarity, and practical toughness.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in³ | ASTM D792 |
| Melt Flow | 4.5 g/10 min | 4.5 g/10 min | Condition 230/3.8; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 50.0 MPa | 7250 psi | ASTM D638 |
| Elongation at Break | 5.3 % | 5.3 % | ASTM D638 |
| Modulus of Elasticity | 2.00 GPa | 290 ksi | ASTM D638 |
| Flexural Strength | 76.0 MPa | 11000 psi | ASTM D790 |
| Izod Impact, Notched | 0.530 J/cm | 0.993 ft-lb/in | ASTM D256 |
| Gardner Impact | 3.30 J | 2.43 ft-lb | ASTM D3029 GB |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 79.0 °C | 174 °F | ASTM D648 |
| Vicat Softening Point | 112 °C | 234 °F | ASTM D1525 |
| Flammability, UL94 | HB | HB |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Transmission, Visible | 91.3 % | 91.3 % | Luminous Transmittance, ASTM D1003 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 221 - 254 °C | 430 - 489 °F |
Users viewing this material also viewed the following:
- Okulen® 2000 PE-UHMW, T
- DuPont Bexloy® AXW602NC010 3% Glass Reinforced, Heat Stabilized Modified Ionomer Resin (discontinued **)
- Lehmann & Voss LUVOCOM® 1-8181 Polyamide 66, with carbon fiber, toughness-modified
- LTL Color Compounds ColorFast® PBA2000 PBT/ABS Alloy, Flame Retarded
- Samyang Trirex® 3500G30 Polycarbonate, 30% Glass Reinforced
- Hexcel® HexPly® 954-2A Curing Cyanate Resin, K1100 Fiber
- Chosun Refractories AMC-70 Alumina Magnesia Carbon Bricks for Ladle Wall And Bottom
- Resinoid 1360 Phenolic Molding, Glass Reinforced
- BASF Elastollan S 70 A SPF TPUR
- Polyplastic Armlen® PP GF 30-1EX Polypropylene Copolymer, 30% Glass Fiber
Copyright © lookpolymers.com All Rights Reserved