Lanxess Durethan® BKV 115 H2.0 DUS008 000000 Nylon 6, 15% Glass Fiber

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 20% Glass Fiber Filled , Nylon 6, Glass Filled, Impact Grade , Nylon 6, Heat Stabilized
Manufacturer Lanxess
Trade Name Durethan®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lanxess Durethan® BKV 115 H2.0 DUS008 000000 Nylon 6, 15% Glass Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PA 6, 15% glass fibers, injection molding, impact modified, heat-ageing stabilizedInformation provided by LANXESS.
Physical Properties Metric English Comments
Density 1.23 g/cc
0.0444 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.0050 cm/cm
0.0050 in/in
60x60x2; 280°C / MT 80°C; 600 bar; ISO 294-4
Linear Mold Shrinkage, Transverse 0.0060 cm/cm
0.0060 in/in
60x60x2; 280°C / MT 80°C; 600 bar; ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength at Break 114 MPa
16500 psi
5 mm/min; ISO 527-1,-2
Elongation at Break 4.1 %
4.1 %
5 mm/min; ISO 527-1,-2
Tensile Modulus 5.90 GPa
856 ksi
1 mm/min; ISO 527-1,-2
Flexural Strength 175 MPa
25400 psi
2 mm/min; ISO 178-A
Flexural Modulus 5.10 GPa
740 ksi
2 mm/min; ISO 178-A
Izod Impact, Notched (ISO) <= 10.0 kJ/m²

@Temperature 23.0 °C
 <= 4.76 ft-lb/in²

@Temperature 73.4 °F
 ISO 180-1A
<= 10.0 kJ/m²

@Temperature -30.0 °C
 <= 4.76 ft-lb/in²

@Temperature -22.0 °F
 ISO 180-1A
Izod Impact, Unnotched (ISO) 35.0 kJ/m²

@Temperature -30.0 °C
 16.7 ft-lb/in²

@Temperature -22.0 °F
 ISO 180-1U
55.0 kJ/m²

@Temperature 23.0 °C
 26.2 ft-lb/in²

@Temperature 73.4 °F
 ISO 180-1U
Charpy Impact Unnotched 4.50 J/cm²

@Temperature -30.0 °C
 21.4 ft-lb/in²

@Temperature -22.0 °F
 ISO 179-1eU
6.50 J/cm²

@Temperature 23.0 °C
 30.9 ft-lb/in²

@Temperature 73.4 °F
 ISO 179-1eU
Charpy Impact, Notched <= 1.00 J/cm²

@Temperature 23.0 °C
 <= 4.76 ft-lb/in²

@Temperature 73.4 °F
 ISO 179-1eA
<= 1.00 J/cm²

@Temperature -30.0 °C
 <= 4.76 ft-lb/in²

@Temperature -22.0 °F
 ISO 179-1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 30.0 µm/m-°C

@Temperature 23.0 - 55.0 °C
 16.7 µin/in-°F

@Temperature 73.4 - 131 °F
 ISO 11359-1,-2
CTE, linear, Transverse to Flow 100 µm/m-°C

@Temperature 23.0 - 55.0 °C
 55.6 µin/in-°F

@Temperature 73.4 - 131 °F
 ISO 11359-1,-2
Deflection Temperature at 0.46 MPa (66 psi) 214 °C
417 °F
ISO 75-1,-2
Deflection Temperature at 1.8 MPa (264 psi) 188 °C
370 °F
ISO 75-1,-2
Shrinkage 0.100 %

@Temperature 120 °C,
Time 14400 sec
 0.100 %

@Temperature 248 °F,
Time 4.00 hour
 post-shrinkage, transverse, 60x60x2; ISO 294-4
0.200 %

@Temperature 120 °C,
Time 14400 sec
 0.200 %

@Temperature 248 °F,
Time 4.00 hour
 post-shrinkage, 60x60x2; ISO 294-4
Processing Properties Metric English Comments
Melt Temperature 280 °C
536 °F
Injection molding; ISO 294
Mold Temperature 80.0 °C
176 °F
Injection molding; ISO 294
Dry Time 2.00 - 6.00 hour

@Temperature 80.0 °C
 2.00 - 6.00 hour

@Temperature 176 °F
Moisture Content 0.030 - 0.12 %
0.030 - 0.12 %
residual; Karl Fischer test
Users viewing this material also viewed the following: