LNP Lubricomp® PDX-J-91198 Polyethersulfone, Proprietary Filler  (discontinued **)

Category Polymer , Thermoplastic , Polyethersulfone (PES)
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LNP Lubricomp® PDX-J-91198 Polyethersulfone, Proprietary Filler  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Features: LubricatedForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still active under new names instituted after the SABIC purchase.
Physical Properties Metric English Comments
Specific Gravity 1.50 g/cc
1.50 g/cc
Method A; ASTM D792
Density 1.50 g/cc
0.0542 lb/in³
ISO 1183
Water Absorption 0.40 %
0.40 %
at 24 hrs; ASTM D570
Linear Mold Shrinkage 0.0020 cm/cm
0.0020 in/in
ASTM D955
Linear Mold Shrinkage, Transverse 0.0040 cm/cm
0.0040 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 117 MPa
17000 psi
ASTM D638
Elongation at Break 1.9 %
1.9 %
ASTM D638
Tensile Modulus 10.1 GPa
1460 ksi
ASTM D638
Flexural Strength 165 MPa
23900 psi
ASTM D790
Flexural Modulus 8.83 GPa
1280 ksi
ASTM D790
Izod Impact, Notched 0.427 J/cm

@Thickness 3.18 mm
0.800 ft-lb/in

@Thickness 0.125 in
ASTM D256
Izod Impact, Unnotched 3.31 J/cm

@Thickness 3.18 mm
6.20 ft-lb/in

@Thickness 0.125 in
ASTM D256
Izod Impact, Notched (ISO) 7.40 kJ/m²
3.52 ft-lb/in²
ISO 180
Izod Impact, Unnotched (ISO) 26.9 kJ/m²
12.8 ft-lb/in²
ISO 180
Falling Dart Impact 4.20 J
3.10 ft-lb
ASTM D3763
Impact Test 2.36 J
1.74 ft-lb
Multi-Axial Instrumented Impact Energy; ISO 6603-2
Coefficient of Friction, Dynamic 0.43
0.43
vs. Steel - @ 40 psi, 50 ft/min, tested in accordance with LNP WI-0687; ASTM D1894
Coefficient of Friction, Static 0.34
0.34
vs. Steel @ 40 psi, tested in accordance with LNP WI-0687; ASTM D1894
K (wear) Factor 8.06 x 10-8 mm³/N-M
4.00 x 10-10 in³-min/ft-lb-hr
40psi, 50ft/min; tested in accordance with LNP WI-0687
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 211 °C
412 °F
Unannealed; ASTM D648
Processing Properties Metric English Comments
Melt Temperature 354 - 371 °C
669 - 700 °F
Mold Temperature 135 - 149 °C
275 - 300 °F
Drying Temperature 121 - 149 °C
250 - 300 °F
Dry Time 4 hour
4 hour
Moisture Content 0.050 %
0.050 %
Suggested
Back Pressure 0.345 - 0.689 MPa
50.0 - 99.9 psi