LG Chemical Lupoy NF1007F 10R Polycarbonate Resin

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer LG Chemical
Trade Name LUPOY
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LG Chemical Lupoy NF1007F 10R Polycarbonate Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: LUPOY NF 1007F10R, eco-friendly UL94 V0/3.0 mm, is designed for extrusion and injection molding products. It combines an excellent physical property balance of heat resistance, transparency and impact strength and exhibits excellent processing characteristics.Main Characteristics: Good mold release, Medium viscosity, Non chlorine, bromine, nor phosphate additives and Complying with global environmental standardsApplications: Lighting, TV Housing, Electrons/Electrical and Information Technology EquipmentCAS: 103598-77-2Information provided by LG Chemical
Physical Properties Metric English Comments
Specific Gravity 1.20 g/cc
1.20 g/cc
ASTM D792
Water Absorption 0.32 %

@Temperature 23.0 °C
0.32 %

@Temperature 73.4 °F
equilibrium, 50% RH; ASTM D570
0.15 %

@Temperature 23.0 °C,
Time 86400 sec
0.15 %

@Temperature 73.4 °F,
Time 24.0 hour
ASTM D570
Linear Mold Shrinkage, Flow 0.00050 - 0.00070 cm/cm
0.00050 - 0.00070 in/in
ASTM D955
Melt Flow 10 g/10 min

@Load 1.20 kg,
Temperature 300 °C
10 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell M 73
73
ASTM D785
Tensile Strength, Ultimate 71.0 MPa
10300 psi
ASTM D638
Tensile Strength, Yield 60.0 MPa
8700 psi
50mm/min; ASTM D638
Elongation at Break 150 %
150 %
ASTM D638
Elongation at Yield 6.0 %
6.0 %
ASTM D638
Tensile Modulus 2.41 GPa
350 ksi
ASTM D638
Flexural Yield Strength 96.0 MPa
13900 psi
ASTM D790
Flexural Modulus 2.41 GPa
350 ksi
ASTM D790
Izod Impact, Notched 9.074 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
17.00 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
0.25 mm notch; ASTM D256
Izod Impact, Unnotched NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
ASTM D256
Dart Drop, Total Energy 87.0 J

@Thickness 3.20 mm
64.2 ft-lb

@Thickness 0.126 in
203m/min; ASTM D3763
Abrasion 45

@Load 1.00 kg
45

@Load 2.20 lb
[%], CS-10 F wheel, 500 cycles; ASTM D1044
Thermal Properties Metric English Comments
CTE, linear 68.0 µm/m-°C

@Temperature -40.0 - 82.0 °C
37.8 µin/in-°F

@Temperature -40.0 - 180 °F
ASTM D696
Hot Ball Pressure Test >= 125 °C
>= 257 °F
IEC 598-1
Deflection Temperature at 0.46 MPa (66 psi) 138 °C

@Thickness 4.00 mm
280 °F

@Thickness 0.157 in
Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 126 °C

@Thickness 4.00 mm
259 °F

@Thickness 0.157 in
Unannealed; ASTM D648
Vicat Softening Point 146 °C

@Load 5.10 kg
295 °F

@Load 11.2 lb
50°C/hr; ASTM D1525
Softening Point 150 - 200 °C
302 - 392 °F
melting point per MSDS
UL RTI, Electrical 130 °C

@Thickness >=0.750 mm
266 °F

@Thickness >=0.0295 in
130 °C

@Thickness >=1.50 mm
266 °F

@Thickness >=0.0591 in
130 °C

@Thickness >=3.00 mm
266 °F

@Thickness >=0.118 in
UL RTI, Mechanical with Impact 110 °C

@Thickness >=0.750 mm
230 °F

@Thickness >=0.0295 in
110 °C

@Thickness >=1.50 mm
230 °F

@Thickness >=0.0591 in
110 °C

@Thickness >=3.00 mm
230 °F

@Thickness >=0.118 in
UL RTI, Mechanical without Impact 130 °C

@Thickness >=0.750 mm
266 °F

@Thickness >=0.0295 in
130 °C

@Thickness >=1.50 mm
266 °F

@Thickness >=0.0591 in
130 °C

@Thickness >=3.00 mm
266 °F

@Thickness >=0.118 in
Flammability, UL94 V-2

@Thickness 1.50 mm
V-2

@Thickness 0.0591 in
ASTM D635
V-0

@Thickness 3.00 mm
V-0

@Thickness 0.118 in
ASTM D635
Flash Point >= 450 °C
>= 842 °F
Oxygen Index 35 %
35 %
ASTM D2863
Glow Wire Test 850 °C

@Thickness 2.00 mm,
Time 5.00 sec
1560 °F

@Thickness 0.0787 in,
Time 0.00139 hour
IEC 695-2-1
Optical Properties Metric English Comments
Refractive Index 1.586
1.586
ASTM D542
Haze 0.70 - 1.5 %
0.70 - 1.5 %
ASTM D1003
Transmission, Visible 89 %
89 %
ASTM D1003
Electrical Properties Metric English Comments
Volume Resistivity 2.00e+17 ohm-cm
2.00e+17 ohm-cm
ASTM D257
Dielectric Constant 3.0

@Frequency 60.0 Hz
3.0

@Frequency 60.0 Hz
ASTM D150
Dielectric Strength 17.0 kV/mm
432 kV/in
ASTM D149
Dissipation Factor 0.0010

@Frequency 60.0 Hz
0.0010

@Frequency 60.0 Hz
ASTM D150
Arc Resistance 0.00 - 60 sec
0.00 - 60 sec
ASTM D495
Comparative Tracking Index 250 V

@Thickness 2.00 mm
250 V

@Thickness 0.0787 in
IEC 112
Hot Wire Ignition, HWI 15 - 30 sec

@Thickness >=1.50 mm
15 - 30 sec

@Thickness >=0.0591 in
30 - 60 sec

@Thickness >=3.00 mm
30 - 60 sec

@Thickness >=0.118 in
High Amp Arc Ignition, HAI >= 120 arcs

@Thickness 1.50 mm
>= 120 arcs

@Thickness 0.0591 in
>= 120 arcs

@Thickness 3.00 mm
>= 120 arcs

@Thickness 0.118 in
High Voltage Arc-Tracking Rate, HVTR 80.0 - 150 mm/min
3.15 - 5.91 in/min
Descriptive Properties Value Comments
Autoignition Temperature >450°C