LG Chemical LUPOY HP5004 PC/ABS, High Impact at Low Temperature
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) , Polycarbonate, Impact Modified |
| Manufacturer | LG Chemical |
| Trade Name | LUPOY |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUPOY HP5004 PC/ABS, High Impact at Low Temperature.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Injection Molding, PC/ABS, General Purpose, High Impact at Low Temperature, High Flow, Heat ResistanceApplication: Mobile Phone HousingCAS: 103598-77-2 and 9003-56-9Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.14 g/cc | 1.14 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.020 | 0.020 | Injection Molding |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0060 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 5.0 g/10 min @Load 2.16 kg, Temperature 250 °C |
5.0 g/10 min @Load 4.76 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 111 | 111 | ASTM D785 |
| Tensile Strength, Yield | 54.9 MPa @Thickness 3.20 mm |
7970 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Elongation at Break | 100 % @Thickness 3.20 mm |
100 % @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Flexural Yield Strength | 88.3 MPa @Thickness 3.20 mm |
12800 psi @Thickness 0.126 in |
10mm/min; ASTM D790 |
| Flexural Modulus | 2.26 GPa @Thickness 3.20 mm |
327 ksi @Thickness 0.126 in |
10mm/min; ASTM D790 |
| Izod Impact, Notched | >= 4.90 J/cm @Thickness 3.20 mm, Temperature -30.0 °C |
>= 9.18 ft-lb/in @Thickness 0.126 in, Temperature -22.0 °F |
ASTM D256 |
| >= 5.88 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
>= 11.0 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 112 °C @Thickness 6.40 mm |
234 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| UL RTI, Electrical | 60.0 °C @Thickness >=0.750 mm |
140 °F @Thickness >=0.0295 in |
|
| UL RTI, Mechanical with Impact | 60.0 °C @Thickness >=0.750 mm |
140 °F @Thickness >=0.0295 in |
|
| UL RTI, Mechanical without Impact | 60.0 °C @Thickness >=0.750 mm |
140 °F @Thickness >=0.0295 in |
|
| Flammability, UL94 | HB @Thickness >=0.750 mm |
HB @Thickness >=0.0295 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 240 - 250 °C | 464 - 482 °F | Injection Molding |
| Middle Barrel Temperature | 250 - 280 °C | 482 - 536 °F | Injection Molding |
| Front Barrel Temperature | 250 - 280 °C | 482 - 536 °F | Injection Molding |
| Nozzle Temperature | 250 - 280 °C | 482 - 536 °F | Injection Molding |
| Melt Temperature | 255 - 285 °C | 491 - 545 °F | Injection Molding |
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | Injection Molding |
| Drying Temperature | 80.0 - 100 °C | 176 - 212 °F | Injection Molding |
| Dry Time | 3.00 - 5.00 hour | 3.00 - 5.00 hour | Injection Molding |
| Back Pressure | 0.981 - 3.92 MPa | 142 - 569 psi | Injection Molding |
| Screw Speed | 40 - 70 rpm | 40 - 70 rpm | Injection Molding |