Arlon 66211A007 0.007" (0.178 mm) Uncured Silicone Rubber Monofilament Polyester Fabric Substrate

Category Polymer , Thermoset , Silicone , Silicone Rubber
Manufacturer Arlon
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Arlon 66211A007 0.007" (0.178 mm) Uncured Silicone Rubber Monofilament Polyester Fabric Substrate.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Design/Construction: Interleave 1: Polyethylene Side 1: Uncured Silicone Rubber Substrate: Monofilament Polyester Fabric Side 2: Uncured Silicone RubberInterleave 2: Polyethylene This data represents typical values for the production material. The data should not be used to write, or in place of, material specifications.Information provided by Arlon, Silicone Technologies Division
Physical Properties Metric English Comments
Density 1.44 g/cc
0.0520 lb/in³
Silicone Property; Arlon SQA-TMS-024
Thickness 50.8 microns
2.00 mil
Substrate; Arlon SQA-TMS-003
63.5 microns
2.50 mil
Side 1; Arlon SQA-TMS-003
63.5 microns
2.50 mil
Side 2; Arlon SQA-TMS-003
63.5 microns
2.50 mil
Interleave 1
63.5 microns
2.50 mil
Interleave 2
178 microns
7.00 mil
Overall; Arlon SQA-TMS-003
Mechanical Properties Metric English Comments
Hardness, Shore A 73
73
Silicone Property; ASTM D2240
Tensile Strength 7.58 MPa
1100 psi
Silicone Property; ASTM D412
Elongation at Break 87 %
87 %
Silicone Property; ASTM D412
Tear Strength 7.89 kN/m
45.0 pli
Die B, Silicone Property; ASTM D624
Peel Strength 0.193 kN/m
1.10 pli
Bond Strength; Arlon SQA -TMS-011
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 232 °C
450 °F
Minimum Service Temperature, Air -56.7 °C
-70.0 °F
Processing Properties Metric English Comments
Cure Time 120 min

@Temperature 204 °C
2.00 hour

@Temperature 400 °F
Recommended Postcure Cycle
15.0 min

@Pressure 0.345 MPa,
Temperature 121 °C
0.250 hour

@Pressure 50.0 psi,
Temperature 250 °F
Recommended Cure Cycle
Shelf Life 6.00 Month

@Temperature 21.1 °C
6.00 Month

@Temperature 70.0 °F
From date of manufacture
Descriptive Properties Value Comments
Color Slate Gray
White
Substrate
Fuel Resistance 0.118
Fuel CM85 resistance, ASTM D471
0.139
Fuel A resistance, ASTM D471
0.269
Fuel C resistance, ASTM D471
Total Product Weight (oz/yd2) 8.6
Arlon SQA-TMS-025