LG Chemical LUPOS GP2205 SAN+GF20%, General Purpose
| Category | Polymer , Thermoplastic , SAN Polymer , Styrene Acrylonitrile (SAN), Molded, Glass Reinforced |
| Manufacturer | LG Chemical |
| Trade Name | LUPOS |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUPOS GP2205 SAN+GF20%, General Purpose.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Feature: Injection Molding, SAN+GF20%, General PurposeApplication: Electric & Electronic (Housing, Components)CAS No. 9003-54-7 and 65997-17-3Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.21 g/cc | 1.21 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.020 | 0.020 | Injection Molding |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0030 cm/cm @Thickness 3.20 mm |
0.0020 - 0.0030 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 9.0 g/10 min @Load 3.80 kg, Temperature 200 °C |
9.0 g/10 min @Load 8.38 lb, Temperature 392 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 115 | 115 | ASTM D785 |
| Tensile Strength, Yield | 98.1 MPa @Thickness 3.20 mm |
14200 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Elongation at Break | 3.0 % @Thickness 3.20 mm |
3.0 % @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Flexural Yield Strength | 152 MPa @Thickness 3.20 mm |
22000 psi @Thickness 0.126 in |
10mm/min; ASTM D790 |
| Flexural Modulus | 6.86 GPa @Thickness 3.20 mm |
996 ksi @Thickness 0.126 in |
10mm/min; ASTM D790 |
| Izod Impact, Notched | 0.392 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
0.735 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C @Thickness 6.40 mm |
212 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| UL RTI, Electrical | 50.0 °C @Thickness >=1.50 mm |
122 °F @Thickness >=0.0591 in |
|
| UL RTI, Mechanical with Impact | 50.0 °C @Thickness >=1.50 mm |
122 °F @Thickness >=0.0591 in |
|
| UL RTI, Mechanical without Impact | 50.0 °C @Thickness >=1.50 mm |
122 °F @Thickness >=0.0591 in |
|
| Flammability, UL94 | HB @Thickness >=1.50 mm |
HB @Thickness >=0.0591 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 220 - 235 °C | 428 - 455 °F | Injection Molding |
| Middle Barrel Temperature | 220 - 240 °C | 428 - 464 °F | Injection Molding |
| Front Barrel Temperature | 220 - 240 °C | 428 - 464 °F | Injection Molding |
| Nozzle Temperature | 230 - 245 °C | 446 - 473 °F | Injection Molding |
| Melt Temperature | 235 - 245 °C | 455 - 473 °F | Injection Molding |
| Mold Temperature | 50.0 - 80.0 °C | 122 - 176 °F | Injection Molding |
| Drying Temperature | 80.0 - 100 °C | 176 - 212 °F | Injection Molding |
| Dry Time | 4.00 - 5.00 hour | 4.00 - 5.00 hour | Injection Molding |
| Back Pressure | 0.981 - 3.92 MPa | 142 - 569 psi | Injection Molding |
| Screw Speed | 40 - 60 rpm | 40 - 60 rpm | Injection Molding |
Users viewing this material also viewed the following:
- Polykemi AB POLYfill PPH GF1020 Polypropylene Homopolymer, Glass Fibre-Reinforced
- Dielectric Polymers NT-8512-2 Powder Coating Tape (discontinued **)
- Kennametal Stellite Stellite® STAR cast
- H.C. Starck Amperit® 704.054 Chromium Oxide (Cr2O3) 99.5%
- Solvay Specialty Polymers Veradel® 3600RP Polyethersulfone (PESU)
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane, 285ºF Cure Temperature
- Covestro Bayblend® FR3050 PC/ABS Blend
- Axiall HHW-191 Rigid PVC, Extrusion
- DuPont Fusabond® MC190D Ethylene Vinyl Acetate (28% VA) (discontinued **)
Copyright © lookpolymers.com All Rights Reserved