LG Chemical LUMAX HR5157 PBT+ABS+GF15%, Heat Resistance

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), 20% Glass Fiber Filled , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 20% Glass Fiber Filled , Polybutylene Terephthalate (PBT), Heat Resistant
Manufacturer LG Chemical
Trade Name LUMAX
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LG Chemical LUMAX HR5157 PBT+ABS+GF15%, Heat Resistance.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Injection Molding Grade, PBT+ABS+GF15%, Heat ResistanceApplication: E&E (CD ROM Tray)CAS: 9003-56-9, 65997-17-3, 24968-12-5 and 25038-59-9Information provided by LG Chemical
Physical Properties Metric English Comments
Specific Gravity 1.33 g/cc
1.33 g/cc
ASTM D792
Maximum Moisture Content 0.020
0.020
Injection Molding
Linear Mold Shrinkage, Flow 0.0040 - 0.0090 cm/cm

@Thickness 3.20 mm
0.0040 - 0.0090 in/in

@Thickness 0.126 in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength, Yield 77.5 MPa

@Thickness 3.20 mm
11200 psi

@Thickness 0.126 in
5mm/min; ASTM D638
Elongation at Break 3.0 %

@Thickness 3.20 mm
3.0 %

@Thickness 0.126 in
5mm/min; ASTM D638
Flexural Yield Strength 127 MPa

@Thickness 3.20 mm
18500 psi

@Thickness 0.126 in
1.3mm/min; ASTM D790
Flexural Modulus 4.41 GPa

@Thickness 3.20 mm
640 ksi

@Thickness 0.126 in
1.3mm/min; ASTM D790
Izod Impact, Notched 0.785 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
1.47 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
ASTM D256
Thermal Properties Metric English Comments
Melting Point 225 °C
437 °F
Peak at Break
Deflection Temperature at 1.8 MPa (264 psi) 175 °C

@Thickness 6.40 mm
347 °F

@Thickness 0.252 in
Unannealed; ASTM D648
UL RTI, Electrical 50.0 °C

@Thickness >=1.50 mm
122 °F

@Thickness >=0.0591 in
50.0 °C

@Thickness >=3.00 mm
122 °F

@Thickness >=0.118 in
UL RTI, Mechanical with Impact 50.0 °C

@Thickness >=1.50 mm
122 °F

@Thickness >=0.0591 in
50.0 °C

@Thickness >=3.00 mm
122 °F

@Thickness >=0.118 in
UL RTI, Mechanical without Impact 50.0 °C

@Thickness >=1.50 mm
122 °F

@Thickness >=0.0591 in
50.0 °C

@Thickness >=3.00 mm
122 °F

@Thickness >=0.118 in
Flammability, UL94 HB

@Thickness >=1.50 mm
HB

@Thickness >=0.0591 in
HB

@Thickness >=3.00 mm
HB

@Thickness >=0.118 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
ASTM D257
Dielectric Strength 21.0 kV/mm

@Thickness 1.00 mm
533 kV/in

@Thickness 0.0394 in
ASTM D149
Arc Resistance 120 - 180 sec
120 - 180 sec
ASTM D495
Comparative Tracking Index 250 V
250 V
Solution A; IEC 60112
Hot Wire Ignition, HWI 7.0 - 15 sec

@Thickness >=1.50 mm
7.0 - 15 sec

@Thickness >=0.0591 in
15 - 30 sec

@Thickness >=3.00 mm
15 - 30 sec

@Thickness >=0.118 in
High Amp Arc Ignition, HAI 30 - 60 arcs

@Thickness 1.50 mm
30 - 60 arcs

@Thickness 0.0591 in
30 - 60 arcs

@Thickness 3.00 mm
30 - 60 arcs

@Thickness 0.118 in
High Voltage Arc-Tracking Rate, HVTR 25.4 - 50.0 mm/min
1.00 - 1.97 in/min
Processing Properties Metric English Comments
Rear Barrel Temperature 225 - 235 °C
437 - 455 °F
Injection Molding
Middle Barrel Temperature 230 - 245 °C
446 - 473 °F
Injection Molding
Front Barrel Temperature 245 - 255 °C
473 - 491 °F
Injection Molding
Nozzle Temperature 245 - 255 °C
473 - 491 °F
Injection Molding
Melt Temperature 245 - 255 °C
473 - 491 °F
Injection Molding
Mold Temperature 60.0 - 90.0 °C
140 - 194 °F
Injection Molding
Drying Temperature 100 °C
212 °F
Injection Molding
Dry Time 4.00 - 5.00 hour
4.00 - 5.00 hour
Injection Molding