Kingfa JH960 6100 Non-halogenated Flame Retardant PC/ABS
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | Kingfa Sci. & Tech. Co. |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Kingfa JH960 6100 Non-halogenated Flame Retardant PC/ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features:Halogen free flame retardant, V-0/1.5mm5VB/1.6mm, 5VA/3.2mmExcellent mechanical propertiesChemical resistanceHydrolysis resistanceDrop down resistantSuper high flow ability, suit for thin wall and complex partsApplications:Computer monitor cabinetOA cabinetLCD cabinetPDP TV setMobile CD and DVDInformation Provided by Kingfa Sci. & Tech. Co., Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.18 g/cc @Temperature 23.0 °C |
1.18 g/cc @Temperature 73.4 °F |
ASTM D792 |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm @Temperature 23.0 °C |
0.0050 - 0.0070 in/in @Temperature 73.4 °F |
ASTM D955 |
| Melt Flow | 32 g/10 min @Load 10.0 kg, Temperature 260 °C |
32 g/10 min @Load 22.0 lb, Temperature 500 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 115 | 115 | ASTM D785 |
| Tensile Strength at Break | 55.0 MPa | 7980 psi | 50mm/min; ASTM D638 |
| Elongation at Break | >= 50 % | >= 50 % | 50mm/min; ASTM D638 |
| Flexural Strength | 85.0 MPa | 12300 psi | 2mm/min; ASTM D790 |
| Flexural Modulus | 2.60 GPa | 377 ksi | 2mm/min; ASTM D790 |
| Izod Impact, Notched | 3.80 J/cm @Thickness 3.20 mm, Temperature -10.0 °C |
7.12 ft-lb/in @Thickness 0.126 in, Temperature 14.0 °F |
ASTM D256 |
| 4.50 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
8.43 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 97.0 °C @Thickness 6.40 mm |
207 °F @Thickness 0.252 in |
ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C @Thickness 6.40 mm |
185 °F @Thickness 0.252 in |
ASTM D648 |
| Flammability, UL94 | 5VB @Thickness 1.60 mm |
5VB @Thickness 0.0630 in |
|
| 5VA @Thickness 3.20 mm |
5VA @Thickness 0.126 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.00e+16 ohm | 1.00e+16 ohm | ASTM D257 |
| Dielectric Strength | 19.0 kV/mm | 483 kV/in | 1.6mm; ASTM D149 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | <= 265 °C | <= 509 °F | |
| Rear Barrel Temperature | 210 - 230 °C | 410 - 446 °F | Start Point: 215°C |
| Middle Barrel Temperature | 220 - 240 °C | 428 - 464 °F | Start Point: 225°C |
| Front Barrel Temperature | 225 - 250 °C | 437 - 482 °F | Start Point: 235°C |
| Melt Temperature | 220 - 240 °C | 428 - 464 °F | Start Point: 230°C |
| Mold Temperature | 40.0 - 60.0 °C | 104 - 140 °F | Start Point: 60°C |
| Drying Temperature | 78.0 - 80.0 °C @Time 7200 - 14400 sec |
172 - 176 °F @Time 2.00 - 4.00 hour |
Pre-dry |
| Back Pressure | 0.300 - 0.700 MPa | 43.5 - 102 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Injection Speed | 50-80% |