- Ineos ABS TRIAX® 1120 ABS/Nylon Blend, Injection Grade, As Conditioned
Ineos ABS TRIAX® 1120 ABS/Nylon Blend, Injection Grade, As Conditioned
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS)/Nylon Blend , Nylon |
| Manufacturer | Ineos ABS |
| Trade Name | Triax® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ineos ABS TRIAX® 1120 ABS/Nylon Blend, Injection Grade, As Conditioned.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Injection molding grade with good flow and stress corrosion cracking resistance, good chemical resistance (fuel, cleaning agents), high impact and notched impact strength, good acoustical damping behavior.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.06 g/cc | 0.0383 lb/in³ | Dry As Molded |
| Linear Mold Shrinkage | 0.010 cm/cm | 0.010 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 90 | 90 | ASTM D785 |
| Tensile Strength, Yield | 30.0 MPa | 4350 psi | |
| Elongation at Break | 190 % | 190 % | ASTM D638 |
| Elongation at Yield | 13 % | 13 % | |
| Tensile Modulus | 1.03 GPa | 149 ksi | |
| Flexural Yield Strength | 57.0 MPa | 8270 psi | at 5% strain; ASTM D790 |
| Flexural Modulus | 1.20 GPa | 174 ksi | ASTM D790 |
| Izod Impact, Notched | 8.00 J/cm @Thickness 3.20 mm |
15.0 ft-lb/in @Thickness 0.126 in |
ASTM D256 |
| 0.800 J/cm @Thickness 3.20 mm, Temperature -40.0 °C |
1.50 ft-lb/in @Thickness 0.126 in, Temperature -40.0 °F |
ASTM D256 | |
| Charpy Impact Unnotched | NB | NB | |
| 1.60 J/cm² @Temperature -30.0 °C |
7.61 ft-lb/in² @Temperature -22.0 °F |
||
| Charpy Impact, Notched | 7.40 J/cm² | 35.2 ft-lb/in² | |
| Impact Test | 42.0 J @Thickness 2.50 mm |
31.0 ft-lb @Thickness 0.0984 in |
Instrumented Total Impact; 2.5 mm thick, 12.5 mm dart, 40 mm clamp, 3.3 m/s; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 99.0 °C | 210 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 93.0 °C | 199 °F | |
| Vicat Softening Point | 98.0 °C | 208 °F | |
| UL RTI, Electrical | 110 °C | 230 °F | |
| UL RTI, Mechanical with Impact | 65.0 °C | 149 °F | |
| UL RTI, Mechanical without Impact | 105 °C | 221 °F | |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 9.00e+12 ohm-cm | 9.00e+12 ohm-cm | ASTM D257 |
| Surface Resistance | 3.20e+13 ohm | 3.20e+13 ohm | ASTM D257 |
| Dielectric Constant | 3.5 @Frequency 1e+6 Hz |
3.5 @Frequency 1e+6 Hz |
ASTM D150 |
| Dielectric Strength | 15.0 kV/mm @Thickness 1.60 mm |
381 kV/in @Thickness 0.0630 in |
Short time under oil; ASTM D149 |
| Dissipation Factor | 0.039 @Frequency 1e+6 Hz |
0.039 @Frequency 1e+6 Hz |
ASTM D150 |
| Arc Resistance | 60 - 120 sec @Thickness 3.18 mm |
60 - 120 sec @Thickness 0.125 in |
UL Rating PLC 6 (60-120 sec) |
| Comparative Tracking Index | >= 600 V @Thickness 3.18 mm |
>= 600 V @Thickness 0.125 in |
UL Rating PLC 0 (>600 V) |
| Hot Wire Ignition, HWI | 30 - 60 sec @Thickness 3.18 mm |
30 - 60 sec @Thickness 0.125 in |
UL Rating PLC 2 (30-60 sec) |
| High Amp Arc Ignition, HAI | >= 120 arcs @Thickness 1.57 mm |
>= 120 arcs @Thickness 0.0618 in |
UL Rating PLC 0 (>120 arcs) |
| High Voltage Arc-Tracking Rate, HVTR | <= 10.0 mm/min @Thickness 3.18 mm |
<= 0.394 in/min @Thickness 0.125 in |
UL Rating PLC 0 (<10 mm/min.) |