Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 199 °F Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 93.0 °C

@Thickness 3.20 mm
199 °F

@Thickness 0.126 in
Unannealed; ASTM D648
Ovation Polymers OpteSTAT™ NC PPS 7010 Polyphenylenesulfide based Carbon Nanotube Compound
Material resistivity can be tailored to the application, while retaining the physical and thermal properties of the base polymer. Applications include components of disk drives, business machines or..
Deflection Temperature at 1.8 MPa (264 psi) 93.0 °C

@Thickness 6.40 mm
199 °F

@Thickness 0.252 in
unannealed; ASTM D648
SABIC Innovative Plastics Cycoloy® CX7259 PC (Asia Pacific)
Cycoloy resin grade CX7259 is a flame retardant impact modified polycarbonate blend aiming at ultra thin wall designs. It is listed as UL-94 V1 at 0.5mm & V0 at 0.6mm with excellent flow and balance..
Deflection Temperature at 1.8 MPa (264 psi) 93.0 °C
199 °F
Polycasa Acryl® KR 2008/1 Acrylic, Impact Grade
Impact grade for extruded tubes and profiles; e.g. strip light diffusers; good scratch and abrasion resistance.Data was collected by ISO methods.Quinn Manufacturing Group rebranded its Plastics Divi..
Deflection Temperature at 1.8 MPa (264 psi) 93.0 °C
199 °F
ISO 75-1/-2
DuPont Performance Polymers Delrin® 100P BK602 Acetal Homopolymer  (Unverified Data**)
Delrin® 100P is a high viscosity acetal homopolymer for use in easy to fill molds. Delrin® 100P provides maximum toughness in the product line without modification. Delrin® 100P has improved pro..
Deflection Temperature at 1.8 MPa (264 psi) 93.0 °C

@Thickness 3.20 mm
199 °F

@Thickness 0.126 in
unannealed; ASTM D648
SABIC Innovative Plastics Lexan® FST3403 PC Copolymer (Europe-Africa-Middle East)
Lexan* FST3403 resin is a high flow PC Copolymer Resin, suitable for injection molding. This halogen-free flame retardant resin is EN45545 R6 HL3 compliant and an ideal candidate for train interior ..
Deflection Temperature at 1.8 MPa (264 psi) 93.0 °C
199 °F
Ineos ABS Lustran® SAN 51
Key Features:UnfilledSuitable processing methods:Injection molding
Deflection Temperature at 1.8 MPa (264 psi) 93.0 °C

@Thickness 6.35 mm
199 °F

@Thickness 0.250 in
ASTM D648
IRPC Polimaxx Polene GP150 Polystyrene
APPLICATIONS: INJECTION MOULDING ELECTRICAL APPLIANCES, HOUSEHOLD PRODUCT, TOYS, SANITARY WARE, etc.
Deflection Temperature at 1.8 MPa (264 psi) 93.0 °C
199 °F
ISO 75A
Lucite International Diakon® CRG812 Acrylic Polymer, Toughened Compound
The Diakon® impact PMMA series offer the best combination of impact, chemical and heat resistance and provide rigidity and surface hardness. The grades in the Diakon® series can be processed b..
Deflection Temperature at 1.8 MPa (264 psi) >= 93.0 °C

@Thickness 6.40 mm
>= 199 °F

@Thickness 0.252 in
Unannealed; ASTM D648
LG Chemical 95HCTC SAN, High Transparency, Heat Resistance, Chemical Resistance
Feature: Injection Molding, SAN, High Transparency, Heat Resistance, Chemical ResistanceApplication: Lighter, Cosmetic Container, ToothbrushCAS No. 9003-54-7Information provided by LG Chemical
Deflection Temperature at 1.8 MPa (264 psi) 93.0 °C
199 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics NORYL WCV065 PPE+Polyolefin (Europe-Africa-Middle East)
Flexible, non-halogenated FR, PPE+Polyolefin resin designed for evaluation in Automotive ISO6722 Class A-C applications.
Deflection Temperature at 1.8 MPa (264 psi) 93.0 °C

@Thickness 3.20 mm
199 °F

@Thickness 0.126 in
unannealed; ASTM D648
SABIC Innovative Plastics LNP STAT-KON DE0021E PC
LNP STAT-KON* DE0021E is a compound based on Polycarbonate resin containing 10% Carbon Fiber. Added features of this material include: Easy Molding, Flame Retardant, Electrically Conductive.
Deflection Temperature at 1.8 MPa (264 psi) 93.0 °C

@Thickness 6.40 mm
199 °F

@Thickness 0.252 in
ASTM D648
Samsung Cheil Industries Starex® VG-4920F ABS, Glass Filled FR
Information provided by Samsung Cheil Industries.
Deflection Temperature at 1.8 MPa (264 psi) 93.0 °C

@Thickness 6.40 mm
199 °F

@Thickness 0.252 in
ASTM D648
Samsung Cheil Industries Starex® VG-4920F ABS, Glass Filled FR
Information provided by Samsung Cheil Industries.
Deflection Temperature at 1.8 MPa (264 psi) 93.0 °C
199 °F
Unannealed; ISO 75-2/A
Styron PULSEâ„¢ GX50 PC/ABS Engineering Resin
Overview: PULSE GX50 engineering resins give exceptional impact strength even at low temperature and have sufficient heat resistance for the majority of automotive interior components. This resin pr..
Deflection Temperature at 1.8 MPa (264 psi) 93.0 °C
199 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics NORYL EXNL0353 PPE+HIPS
EXNL0353 resin is a modified PPE + PS blend with an excellent balance of non-halogenated flame retardance, hydrolytic stability, impact and heat resistance, good flow, and low specific gravity for l..
Deflection Temperature at 1.8 MPa (264 psi) 93.0 °C
199 °F
0.5 inch unannealed; ASTM D648
PlastxWorld CEVIAN®-V 520 ABS
Super High Rigid ABSThese are typical values and are not intended for specification purposes. UL approved file No. is E47773. Information provided by PlastxWorld Inc.
Deflection Temperature at 1.8 MPa (264 psi) 92.8 °C
199 °F
unannealed, unspecified pressure; ASTM D648
Chi Mei Kibilac® PW-978B ASA, High Heat
Acrylonitrile/Styrene/AcrylateInformation provided by Calsak Corporation
Deflection Temperature at 1.8 MPa (264 psi) 93.0 °C
199 °F
ISO 75-1/-2
DuPont Performance Polymers Delrin® 500PE NC010A Acetal Homopolymer
Delrin® 500PE NC010A is a medium viscosity acetal homopolymer, an enhanced version of Delrin® 500P with extremely low VOC emissions. It has improved processing thermal stability, and good mechanic..
Deflection Temperature at 1.8 MPa (264 psi) 92.8 °C
199 °F
0.125 in bar Annealed 4 hours at 80°C; ASTM D648
Diamond Polymers ABS 9501
Description: Injection Molding Grade, Ultra High ImpactInformation provided by Diamond Polymers, Inc.
Deflection Temperature at 1.8 MPa (264 psi) 93.0 °C
199 °F
Annealed; ASTM Data
Dow AIM® 4810 High Impact Styrenic Resin
AIM® 4810 advanced styrenic resin is designed to offer the processability of high impact polystyrene and the gloss and practical toughness of high gloss ABS. It can be processed at lower temperatur..
Deflection Temperature at 1.8 MPa (264 psi) 92.8 °C
199 °F
Annealing cycle: 4hrs at 80°C; ASTM D648
Arkema Group Plexiglas® V044 Acrylic
Plexiglas® V044 is a thermoplastic acrylic resin formulated for extrusion applications. It is characterized by its chemical and heat resistance as well high melt flow. Plexiglas® V044 has excelle..
Deflection Temperature at 1.8 MPa (264 psi) 93.0 °C
199 °F
ASTM D648
Ashley Polymers Ashlene® 520MS/520SMS Nylon 66, MoS2 Filled
A general purpose Molybdenum-disulfide filled nylon resin.Data provided by the manufacturer
Deflection Temperature at 1.8 MPa (264 psi) 93.0 °C

@Thickness 6.40 mm
199 °F

@Thickness 0.252 in
Method A; ASTM D648
Bhansali Engineering Abstron SE32H Extrusion ABS
Very High Impact, Better Flow and Sheet/Pipe/Profile applicationInformation provided by Bhansali
Deflection Temperature at 1.8 MPa (264 psi) 93.0 °C
199 °F
ISO 75-1, -2
Celanese Celcon® M25UV POM, UV Resistant
Celcon« M25UV is an acetal copolymer developed as a natural UV light stabilized low flow, high molecular weight grade. It has been formulated as a natural acetal that does not discolor, yet maintai..
Deflection Temperature at 1.8 MPa (264 psi) 93.0 °C
199 °F
ISO 75-1, -2
Celanese Hostaform® MT® SlideX™ 1203 POM, Medical Technology
POM copolymerInformation provided by Celanese
Deflection Temperature at 1.8 MPa (264 psi) 93.0 °C
199 °F
Method A - Annealed; ASTM D-648
Bhansali Engineering Abstron SHF-50+M ABS Injection Molding Grade
High Flow High Gloss, Fancy ApplicationsInformation provided by Bhansali
Deflection Temperature at 1.8 MPa (264 psi) 93.0 °C
199 °F
Asahi Kasei Thermylene® P-9900-0712 Chemically Coupled Polypropylene Compound
Applications: Automotive: Blower Wheels, HVAC Electrical and Specialty: Flush Valves, Pump BasesInformation provided by Asahi Kasei
Deflection Temperature at 1.8 MPa (264 psi) 92.8 °C

@Thickness 6.40 mm
199 °F

@Thickness 0.252 in
ASTM D648
Samsung Cheil Industries Infino® NH-3208GL PC, Glass Filled FR
Information provided by Samsung Cheil Industries.
Deflection Temperature at 1.8 MPa (264 psi) 93.0 °C
199 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics GELOY FXW751SK ASA+PC
Sparkle Metallic VisualFx ASA+PC Resin - Weatherable, High Heat & Impact Resin
Deflection Temperature at 1.8 MPa (264 psi) 93.0 °C
199 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics GELOY XP4025 ASA+PC
Available in a wide range of colors and is recommended for unpainted exterior applications.